摘要: 通过改变MoS2（质量分数1.0%~2.0%）和石墨（质量分数0~1.0%）的成分比例，在一定滑动线速度下，测量青铜基含油轴承承受压强的极限值，研究MoS2和石墨含量对青铜基含油轴承的力学性能和摩擦性能的影响。结果表明：在不加入石墨的情况下，随着MoS2含量的增加，含油轴承的负荷×线速度（pv）极限值降低，其中青铜-1MoS2（MoS2质量分数1.0%）含油轴承极限pv值最高，达到2.940 MPa·m·s-1；在同时加入石墨和MoS2的情况下，随着石墨含量的增加，含油轴承的摩擦因数降低，其中青铜-1MoS2/-1石墨（MoS2质量分数1.0%，石墨质量分数1.0%）含油轴承摩擦因数最低，为0.038；石墨能够改善含油轴承的摩擦性能，但是会大幅度降低其力学性能。Abstract: By changing the contents of MoS2 (mass fraction 1.0%~2.0%) and graphite (mass fraction 0~1.0%), the bearing pressure limit value of bronze oil bearing at the certain sliding linear velocity was measured, the effects of MoS2 and graphite contents on the mechanical and frictional properties of bronze oil bearing were studied. The results show that, the limit value of load×linear velocity (pv) for the oil bearings decreases with the increase of MoS2 content without graphite addition, and the bronze-1MoS2 (1.0%MoS2, mass fraction) oil bearing has the highest pv value of 2.940 MPa·m·s-1. In the case of adding graphite and MoS2 at the same time, the friction coefficient of the oil bearing decreases with the increase of the graphite content, and the bronze-1MoS2-1graphite (1.0%MoS2 and 1.0%graphite, mass fraction) oil bearing has the lowest friction coefficient of 0.038. Graphite can improve the friction properties of oil bearings, but it may greatly reduce the mechanical properties of oil bearings.
-
Keywords:
- bronze /
- oil bearing /
- friction /
- molybdenum disulfide /
- graphite
-
电容器级钽丝是用于制作钽电解电容器的阳极引线，其优点是钽丝的表面氧化膜介电常数大，可靠性高。电容器级钽丝是以钽粉为原料，利用粉末冶金方法烧结成钽条后，再经轧制、拉拔等金属塑性加工手段制成的，其重要性能指标包括抗拉强度、直线度、化学成分组成和漏电流等。近几年，随着钽电解电容器向小型化和耐高压方向发展，钽丝的生产工艺也在不断完善和更新；在稳定力学性能、化学成分和电性能的前提下，要提高钽丝的直线度，保证电容器成形过程中钽丝不弯曲，从而提高电容器的可靠性[1]。
众所周知，在拉拔过程中，随着加工量的增加，不论是钽丝还是其他材料的线材都会因为抵抗变形而产生大量的残余应力，导致线材的直线度变差。钽电解电容器对其阳极引线—钽丝的直线度要求很高，所以需要通过一种矫直的方法来均匀或消除这种残余应力。目前，在硬态钽丝的生产中采用拉弯矫直的原理[2]，依靠矫直机两辊(中间内凹，双曲线辊)的角度变化对钽丝进行反复弯曲，使钽丝的残余应力均匀的分布在钽丝内部组织中，从而达到矫直的目的。常用的矫直方法还有热应力矫直方法，即通过连续走线的方式，将钽丝置于高温环境中，利用再结晶消除钽丝内部的残余应力[3]。钽丝之所以弯曲，是因为在拉拔过程中受到拉应力和压应力，两种力的作用大小不一而形成的；热应力矫直法是在放线张力和高温的作用下，消除钽丝中原有的拉应力和压应力，使弯曲的钽丝完全变直的过程。矫直后的钽丝在放线张力下绕在一定曲率半径的绕线盘上，绕线盘的曲率半径对钽丝的直线度影响很大，尤其对退火态钽丝的直线度影响更大。采用高温连续走线退火方法生产钽丝，钽丝微观组织细小、均匀，是生产高性能和直线度良好电容器级钽丝的有效工艺。本文通过优化连续退火工艺和矫直收线工艺来改善钽丝的直线度，从而提高钽丝的适用性。
1. 原料钽粉对钽丝直线度的影响
根据用户对钽丝耐高温性能要求的不同，以掺杂或非掺杂钽粉为原料，采用粉末冶金法生产具有耐高温性能的钽丝。在钽粉中掺杂可提高钽丝再结晶退火温度，细化钽丝晶粒度，提高钽丝强度，增加钽丝的抗变形能力[4]。
1.1 钽丝再结晶程度对直线度的影响
不同直线度的非掺杂钽丝(直径为0.8 mm)再结晶组织如图 1和图 2所示。从再结晶钽丝的晶粒度分析，直线度好的钽丝晶粒细小，没有出现晶粒长大的情况，说明退火不完全，没有将金属内部的残余应力完全消除。由于晶粒之间存在一定的变形抗力，在1800 ℃高温条件下退火，钽丝内部晶粒出现再结晶，晶粒明显细化且很均匀，说明晶粒之间存在的变形应力被完全消除，钽丝的直线度较好，退火后钽丝产品的抗拉强度较小。
![]()
图 1 直线度为4/100钽丝晶粒度Figure 1. Grain size of the tantalum wire with the straightness of 4/100![]()
图 2 直线度为0.4/100钽丝晶粒度Figure 2. Grain size of the tantalum wire with the straightness of 0.4/1001.2 原料钽粉掺杂和非掺杂对钽丝直线度的影响
采用掺杂(钇、硅)[5]钽粉制备钽丝，可在钽丝高温退火过程中细化钽丝组织晶粒度，起到细晶韧化、固溶强化和弥散强化的作用[6]，使钽丝具有更好的室温力学性能、漏电流、烧结折丝及抗氧脆性性能，因此在生产耐高温有机电容器中被普遍使用。在原料钽粉中掺杂钇制备钽丝，研究钽丝在高温退火后的直线度。
图 3和图 4所示为掺杂钇元素和非掺杂钽丝的显微组织晶粒度。由图可知，在相同退火条件下，掺杂钽丝的晶粒细小、均匀，非掺杂钽丝的晶粒粗大、不均匀。这表明掺杂钽丝的结晶程度不如非掺杂钽丝，这是因为钽丝中掺杂的钇元素均匀镶嵌在钽晶界上，抑制了钽晶粒的长大和回复，无法将残留在晶界上的残余应力消除干净[7]。为了完全消除掺杂钽丝中的残余应力，建议将高温连续退火温度控制在1650~1900 ℃，走线速度控制在10~40 m·min-1。晶界上的钇元素含量随着温度的升高逐渐降低，金属的抗拉强度也会逐渐降低，从而达到回复的目的。掺杂后的钽丝经过高温退火能有效提高其再结晶度，使退火后钽丝的直线度得到显著改善。
![]()
图 3 0.8 mm掺杂钇元素钽丝的晶粒度Figure 3. Grain size of the tantalum wire doping by yttrium element in the diameter of 0.8 mm![]()
图 4 0.8 mm非掺杂钽丝的晶粒度Figure 4. Grain size of the tantalum wire without doping in the diameter of 0.8 mm在相同退火条件下，掺杂和非掺杂钽丝的直线度如表 1所示。由表可知，在高温连续退火后，掺杂和非掺杂钽丝直线度的标准偏差分别为0.24和0.23，没有明显差异；经精绕密排后，掺杂钽丝直线度的标准偏差为0.16，非掺杂钽丝直线度的标准偏差为0.36，掺杂钽丝直线度的变化比非掺杂钽丝要小的多，其稳定性好。在相同退火条件下，虽然掺杂钽丝的再结晶过程已经形成，但晶粒大小远不及非掺杂钽丝晶粒的粗大，因此晶粒与晶界之间的应力相应也较大，相对抵制塑性变形的能力也较大。因此，在精绕密排过程中，掺杂钽丝即便发生一定的塑性变形，也没有非掺杂钽丝那么明显，掺杂钽丝的直线度明显好于非掺杂钽丝[8]。为满足轧制片式钽电解电容器阳极引线的要求，阳极引线优先选用掺杂的钽丝。
表 1 掺杂和非掺杂钽丝(0.8 mm)直线度Table 1. Straightness of the tantalum wires (0.8 mm) with and without doping次数 掺杂钽丝直线度，x/100 非掺杂钽丝直线度，x/100 连续退火后 产品精绕密排 连续退火后 产品精绕密排 第一次 0.80/100 1.70/100 0.80/100 2.80/100 第二次 1.00/100 1.70/100 1.00/100 2.40/100 第三次 1.40/100 1.50/100 1.20/100 3.10/100 第四次 0.80/100 1.30/100 0.80/100 2.20/100 第五次 0.80/100 1.50/100 0.60/100 2.40/100 第六次 0.80/100 1.40/100 0.60/100 2.20/100 均值 0.93/100 1.52/100 0.83/100 2.52/100 标准差 0.24/100 0.16/100 0.23/100 0.36/100 2. 高温退火工艺对钽丝直线度的影响
2.1 钽丝高温退火前的直线度对退火后钽丝直线度的影响
选用同批次ϕ0.6 mm掺杂钽丝。在高温连续退火前，对部分钽丝进行矫直，对另外一部分钽丝未进行矫直，两种钽丝经高温退火后直线度的对比试验结果如表 2所示[9]。从表 2可以看出，退火前钽丝的直线度对退火后钽丝的直线度有显著影响，这是因为走线式连续退火不可能将钽丝的残余内应力完全消除，退火后钽丝发生的塑性变形是不完全的，丝材弯曲一侧的压应力和另一侧的拉应力没有被完全消除[10]。在高温退火前对钽丝进行一次热应力矫直过程，均衡了弯曲两侧的拉应力和压应力，使得丝材的直线度变得均匀可控。
表 2 退火前钽丝直线度对退火后钽丝直线度的影响Table 2. Effect of the tantalum wire straightening before annealing on the tantalum wire straightening after annealing工艺 钽丝直线度，x/100 退火前矫直 退火前未矫直 退火前 3.00/100 6.00/100 退火后 2.00/100 3.50/100 均值 2.50/100 4.75/100 标准差 0.71/100 1.77/100 2.2 走线式连续退火的放线张力对钽丝直线度的影响
选用同批次ϕ0.8 mm掺杂钽丝，在高温连续退火过程中(温度1650~1900 ℃，走线速度10~40 m·min-1)，采用不同放线张力(0.5 kg和0.9kg)进行试验，退火后钽丝的直线度如图 5所示。由图可知，随着张力的增大，退火后钽丝的直线度在逐渐变好，由原来最大5.0/100变为最小0.8/100。这是因为钽丝在连续走线式退火过程中，张力的增大给直线度差的钽丝一个拉应力和一个压应力，这种拉应力、压应力越大，在高温再结晶回复越明显[11]。但是这种拉应力、压应力不可能无限制增加，在钽丝不发生塑性变形的前提下，可以提高拉应力、压应力，否则钽丝在高温下极易发生塑性变形[12]，从而在宏观上表现为钽丝变细。通过试验发现，当钽丝直径大于ϕ0.6 mm时，张力增加到0.9 kg对钽丝直径影响不大。
![]()
图 5 退火放线张力对钽丝直线度的影响Figure 5. Effect of the payoff tension on the straightness of tantalum wire during annealing2.3 连续退火出炉口定位轮直径对退火后钽丝直线度的影响
走线式连续退火炉因为是连续走线，钽丝在出炉口时温度很高，在出炉后经过出炉口定位轮时，由于走线方向发生一定角度的转向，此时定位轮会给钽丝施加一定的外力(F外，如式(1)所示)，这种外力极易让钽丝发生塑性变形，从而影响钽丝直线度。为了减少这种外力，唯一可以改变的是增大定位轮的直径。由向心力公式(式(2))可知，增加定位轮直径，可以减小定位轮转动产生的向心力(F向)[13]。
$$ F_{\text {外 }}=F_{\text {向 }} $$ (1) $$ F_{\text {向 }}=M v^{2} / R $$ (2) 式中：F外为定位轮给钽丝施加的外力；F向为定位轮转动产生的向心力；R为定位轮直径；M为定位轮质量；v为定位轮转速。
选用同批次ϕ0.8 mm掺杂钽丝，通过将连续退火出炉口定位轮直径由原来的220 mm增加到300 mm，在速度v不变的情况下，减少外力F外的方法进行试验，改进钽丝的直线度，结果如表 3所示。从表可知，经过增加连续退火出炉口定位轮直径后，钽丝的直线度得到明显改善。
表 3 续退火出炉口定位轮直径对退火后钽丝直线度的影响Table 3. Effect of the wheel diameter of tap hole on the straightness of tantalum wire after annealing导轮直径/ mm 钽丝直线度，x/100 220 2.4/100 300 0.8/100 3. 钽丝精绕密排中收线盘直径的大小对钽丝直线度的影响
通常钽丝经过高温退火后，收线排列比较松散，需要对钽丝进行精绕密排，防止钽丝发生松丝、乱丝的现象，在存储、搬运和使用过程中影响钽丝的直线度。选用同批次ϕ0.8 mm掺杂钽丝，采用直径不同的收线盘进行精绕密排试验，在相同的精绕密排工艺条件下，钽丝的直线度如表 4所示。从表 4可以看出，对于密排前直线度相同的钽丝，在相同的精绕密排工艺条件下，密排到直径不同的收线盘上，测试出的钽丝直线度有明显的差距，随着收线盘直径的增大，其直线度变好。通常钽丝的精绕密排过程是需要一定的张力，这种张力情况与前面提到的退火收线一样，对钽丝也会造成一定的塑性变形，塑性变形在弹性变形范围之内发生，一定程度上会有回复，但塑性变形发生在弹性变形范围之外，就会产生永久性变形，从而影响钽丝的直线度。
表 4 矫直收线盘直径的大小对钽丝直线度的影响Table 4. Effect of the straightening coil diameter on the straightness of tantalum wire精绕收线盘直径/ mm 钽丝直线度，x/100 密排前 密排后 230 1.2/100 2.4/100 300 1.2/100 1.3/100 4. 结论
(1) 通过高温连续退火，掺杂钽丝的晶粒比非掺杂钽丝晶粒小且更加均匀，晶粒与晶界之间的应力也相应较大，抵制塑性变形的能力也较大，掺杂钽丝的直线度明显好于非掺杂钽丝。为满足轧制片式钽电解电容器阳极引线的要求，阳极引线优先选用掺杂的钽丝。
(2) 钽丝退火前的直线度极大影响着退火后产品的直线度，因此在退火前必须进行去应力矫直过程。
(3) 走线式连续退火的放线张力对钽丝直线度有一定的影响，张力越大，直线度越好，但不能无限增加，否则钽丝直径会发生变化。
(4) 连续退火出炉口定位轮直径越大，钽丝的直线度越好；矫直收线盘的直径越大，钽丝的直线度越好。
-
![]()
图 1 未添加石墨、添加不同质量分数MoS2的轴承试样腐蚀前后的显微组织形貌：(a)青铜-1MoS2(MoS2质量分数1.0%)；(b)青铜-1.5MoS2(MoS2质量分数1.5%)；(c)青铜-2MoS2(MoS2质量分数2.0%)；(d)腐蚀后青铜-1MoS2；(e)腐蚀后青铜-1.5MoS2；(f)腐蚀后青铜-2MoS2
Figure 1. Microstructures of the bearing samples without graphite and with MoS2 in different mass fractions before and after corrosion: (a) bronze-1MoS2 (MoS2 mass fraction of 1.0%); (b) bronze-1.5MoS2 (MoS2 mass fraction of 1.5%); (c) bronze-2MoS2 (MoS2 mass fraction of 2.0%); (d) bronze-1MoS2 after corrosion; (e) bronze-1.5MoS2 after corrosion; (f) bronze-2MoS2 after corrosion
![]()
图 2 含质量分数1.0%MoS2且添加不同质量分数石墨的轴承试样腐蚀前后显微组织形貌：(a)青铜-1MoS2(不含石墨)；(b)青铜-1MoS2-0.5石墨(石墨质量分数0.5%)；(c)青铜-1MoS2-1石墨(石墨质量分数1.0%)；(d)腐蚀后青铜-1MoS2；(e)腐蚀后青铜-1MoS2-0.5石墨；(f)腐蚀后青铜–1MoS2-1石墨
Figure 2. Microstructures of the bearing samples with 1.0% MoS2 and graphite in different mass fractions before and after corrosion: (a) bronze-1MoS2 (without graphite); (b) bronze-1MoS2-0.5graphite (graphite mass fraction of 0.5%); (c) bronze-1MoS2-1graphite (graphite mass fraction of 1.0%); (d) bronze-1MoS2 after corrosion; (e) bronze-1MoS2-0.5graphite after corrosion; (f) bronze-1MoS2- 1graphite after corrosion
![]()
图 3 试样成分对轴承含油率的影响
Figure 3. Effect of the sample composition on the bearing oil content
![]()
图 4 试样成分对轴承硬度(a)和压溃强度(b)的影响
Figure 4. Effect of the sample composition on the hardness (a) and crushing strength (b) of bearings
![]()
图 5 试样成分对轴承极限pv值(a)和摩擦因数(b)的影响
Figure 5. Effect of the sample composition on the limit pv value (a) and friction coefficient (b) of bearings
![]()
图 6 7#试样的压坯、烧结样品和摩擦样品表面的X射线衍射图谱
Figure 6. XRD patterns of the compacted, sintered, and friction surfaces of 7# samples
![]()
图 7 在线速度为0.5 m·s-1条件下摩擦失效试样表面的扫描电子显微形貌和元素面分布能谱分析：(a)1#试样；(b)7#试样
Figure 7. SEM images and EDS analysis of the failure specimen surface by friction at the linear velocity of 0.5 m·s-1: (a) sample 1#; (b) sample 7#
表 1 铜基含油轴承主要成分含量(质量分数)
Table 1 Main composition of the bronze oil bearing
% 序号 Cu–10Sn MoS2 石墨 硬脂酸锌 1# 余量 1.0 0 0.6 2# 余量 1.5 0 0.6 3# 余量 2.0 0 0.6 4# 余量 1.0 0.5 0.6 5# 余量 1.5 0.5 0.6 6# 余量 2.0 0.5 0.6 7# 余量 1.0 1.0 0.6 8# 余量 1.5 1.0 0.6 9# 余量 2.0 1.0 0.6 
下载: 导出CSV
-
[1] 韩凤麟. 粉末冶金机械零件. 粉末冶金技术, 2016, 34(2): 155 https://www.cnki.com.cn/Article/CJFDTOTAL-FMYJ802.008.htm Han F L. Powder metallurgy machinery parts. Powder Metall Technol, 2016, 34(2): 155 https://www.cnki.com.cn/Article/CJFDTOTAL-FMYJ802.008.htm
[2] 申小平. 粉末冶金制造工程. 北京: 国防工业出版社, 2015 Shen X P. Powder Metallurgy Manufacturing Engineering. Beijing: National Defense Industry Press, 2015
[3] 渡边侊尚, 韩凤麟. 烧结含油轴承. 粉末冶金技术, 2002, 20(3): 121 DOI: 10.3321/j.issn:1001-3784.2002.03.001 Teruhisa W, Han F L. Porous sintered bearings. Powder Metall Technol, 2002, 20(3): 121 DOI: 10.3321/j.issn:1001-3784.2002.03.001
[4] 段家欢. 浅析粉末冶金材料及冶金技术发展. 世界有色金属, 2018(15): 16 DOI: 10.3969/j.issn.1002-5065.2018.15.010 Duan J H. Development of powder metallurgy materials and metallurgical technology. World Nonferrous Met, 2018(15): 16 DOI: 10.3969/j.issn.1002-5065.2018.15.010
[5] 鲁乃光. 烧结金属摩擦材料现状与发展动态. 粉末冶金技术, 2002, 20(5): 294 DOI: 10.3321/j.issn:1001-3784.2002.05.008 Lu N G. The present state and tendency of sintered friction materials in the world. Powder Metall Technol, 2002, 20(5): 294 DOI: 10.3321/j.issn:1001-3784.2002.05.008
[6] 杜明. 石墨及镀铜石墨–铜基复合材料摩擦学性能研究[学位论文]. 长春: 长春工业大学, 2018 Du M. Study on Tribological Properties of Graphite and Copper Coated Graphite-Copper Composites Materials [Dissertation]. Changchun: Changchun University of Technology, 2018
[7] 孙永安, 张玲, 李县辉, 等. 高速自润滑含油轴承的研究. 粉末冶金技术, 2002, 20(2): 90 DOI: 10.3321/j.issn:1001-3784.2002.02.007 Sun Y A, Zhang L, Li X H, et al. Study about high-speed self-lubricating oil-containing bearing. Powder Metall Technol, 2002, 20(2): 90 DOI: 10.3321/j.issn:1001-3784.2002.02.007
[8] 周青伟. 二硫化钼及其复合材料的制备与性能研究[学位论文]. 南京: 南京大学, 2019 Zhou Q W. The Preparation and Property Study of Nanomaterials Based on Molybdenum Disulfide [Dissertation]. Nanjing: Nanjing University, 2019
[9] 石淼森. 固体润滑材料. 北京: 化学工业出版社, 2000 Shi M S. Solid Lubricating Materials. Beijing: Chemical Industry Press, 2000
[10] 晏浩洋. 固体润滑技术的原理与应用. 技术与市场, 2016, 23(11): 133 DOI: 10.3969/j.issn.1006-8554.2016.11.099 Yan H Y. Principle and application of solid lubrication technology. Technol Market, 2016, 23(11): 133 DOI: 10.3969/j.issn.1006-8554.2016.11.099
[11] 杨茜婷. 银–石墨–二硫化钼复合材料的摩擦磨损性能研究[学位论文]. 合肥: 合肥工业大学, 2010 Yang Q T. Study on Friction and Wear Properties of Ag–G–MoS2 [Dissertation]. Hefei: Hefei University of Technology, 2010
[12] 崔中涛. 石墨–二硫化钼涂层摩擦学性能及其在深沟球轴承上的应用研究[学位论文]. 重庆: 重庆大学, 2018 Cui Z T. Tribological Properties of Graphite–MoS2 Coating and Its Application in Deep Groove Ball Bearings[Dissertation]. Chongqing: Chongqing University, 2018
[13] 杨承璋. 二硫化钼涂层摩擦学性能及其在TBA轴承上的应用[学位论文]. 重庆: 重庆大学, 2018 Yang C Z. Tribological Properties of MoS2 Coating and Its Application in TBA Bearing[Dissertation]. Chongqing: Chongqing University, 2018
[14] 陈淑娴. 铜–二硫化钼复合材料的制备及其组织与性能研究[学位论文]. 合肥: 合肥工业大学, 2009 Chen S X. The Study of Preparation, Microstructure and Properties of Cu–MoS2 Composites [Dissertation]. Hefei: Hefei University of Technology, 2009
[15] 张银娣. 自润滑Cu/Cu–MoS2复合材料的制备及性能研究[学位论文]. 洛阳: 河南科技大学, 2014 Zhang Y D. Preparation and Properties of Cu/Cu–MoS2 Self-lubricating Composite [Dissertation]. Luoyang: Henan University of Science and Technology, 2014
[16] 牛淑琴, 阮虎生, 朱家佩, 等. 青铜–石墨系含油自润滑复合材料的研究与应用. 摩擦学学报, 1992, 12(4): 335 https://www.cnki.com.cn/Article/CJFDTOTAL-MCXX199204005.htm Niu S Q, Ruan H S, Zhu J P, et al. The study and application of bronze-graphite oil-containing self-lubricating composites. Tribology, 1992, 12(4): 335 https://www.cnki.com.cn/Article/CJFDTOTAL-MCXX199204005.htm
[17] 陈锐. 石墨材料与石墨轴承. 炭素, 2001(4): 32 DOI: 10.3969/j.issn.1001-8948.2001.04.005 Chen R. Graphite-material and graphite-bearing. Carbon, 2001(4): 32 DOI: 10.3969/j.issn.1001-8948.2001.04.005
[18] 张铭君, 朱世伟, 于俊凤, 等. 石墨/铜基复合材料研究进展. 铸造技术, 2017, 38(11): 2565 https://www.cnki.com.cn/Article/CJFDTOTAL-ZZJS201711002.htm Zhang M J, Zhu S W, Yu J F, et al. Development of graphite/copper matrix composites. Foundry Technol, 2017, 38(11): 2565 https://www.cnki.com.cn/Article/CJFDTOTAL-ZZJS201711002.htm
[19] 张蒙蒙, 谢凤, 李斌, 等. 金属硫化物固体润滑剂简介. 合成润滑材料, 2015, 42(3): 27 DOI: 10.3969/j.issn.1672-4364.2015.03.010 Zhang M M, Xie F, Li B, et al. Introduction of metallic sulfide solid lubricants in brief. Synth Lubric, 2015, 42(3): 27 DOI: 10.3969/j.issn.1672-4364.2015.03.010