Microstructure and mechanical properties of Fe–Co–Ni based superalloy prepared by hot isostatic pressing
-
摘要: 以气雾化（gas atomization，GA）粉末为原料，采用热等静压（hot isostatic pressing，HIP）致密化烧结工艺制备Fe18Ni23Co25Cr21Mo8WNbC2铁钴镍基高温合金，研究热等静压温度对致密化Fe18Ni23Co25Cr21Mo8WNbC2粉末高温合金金相组织、力学性能和断口形貌的影响。结果表明：热等静压技术制备的高温合金致密化程度很高，烧结体由（Fe，Ni）固溶体相和弥散分布的M6C碳化物强化相组成；热等静压温度为950~1050 ℃时，烧结体的密度、力学性能随着热等静压烧结温度的提高而提高；当热等静压温度达到1100 ℃时，致密化烧结体晶粒组织明显长大，其力学拉伸性能降低；致密化烧结体的室温拉伸断口以穿晶断裂为主，局部区域晶粒被拉伸开裂，650 ℃高温断口为穿晶断裂和沿晶断裂的混合形貌，基体相存在沿应力方向被拉长的韧窝。Abstract: The Fe-Co-Ni based superalloys (Fe18Ni23Co25Cr21Mo8WNbC2) were prepared by the hot isostatic pressing (HIP), using the gas atomization powders as the raw material, and the effects of HIP temperatures on the microstructure, mechanical properties, and fracture morphology of the densified Fe18Ni23Co25Cr21Mo8WNbC2 superalloys were studied. The results show that, the HIPed superalloys have the high densification degree, and the sintered superalloys are composed of the (Fe, Ni) solidsolution phase and the dispersed M6C carbide strengthening phase. With the increase of sintering temperature from 950 ℃ to 1050 ℃, the density and mechanical properties of the HIPed sintered superalloys increase. When the HIP temperature reaches 1100 ℃, the grains of the densified sintered superalloys grow significantly and the mechanical tensile properties decrease. The tensile fracture of the densified sintered superalloys at room-temperature is mainly transgranular, and the grains in the local area are stretched and cracked. The tensile fracture of the densified sintered superalloys at 650 ℃ is a mixture of the transgranular and intergranular fracture, and the dimples in matrix are elongated along the direction of stress.
-
电容器级钽丝是用于制作钽电解电容器的阳极引线，其优点是钽丝的表面氧化膜介电常数大，可靠性高。电容器级钽丝是以钽粉为原料，利用粉末冶金方法烧结成钽条后，再经轧制、拉拔等金属塑性加工手段制成的，其重要性能指标包括抗拉强度、直线度、化学成分组成和漏电流等。近几年，随着钽电解电容器向小型化和耐高压方向发展，钽丝的生产工艺也在不断完善和更新；在稳定力学性能、化学成分和电性能的前提下，要提高钽丝的直线度，保证电容器成形过程中钽丝不弯曲，从而提高电容器的可靠性[1]。
众所周知，在拉拔过程中，随着加工量的增加，不论是钽丝还是其他材料的线材都会因为抵抗变形而产生大量的残余应力，导致线材的直线度变差。钽电解电容器对其阳极引线—钽丝的直线度要求很高，所以需要通过一种矫直的方法来均匀或消除这种残余应力。目前，在硬态钽丝的生产中采用拉弯矫直的原理[2]，依靠矫直机两辊(中间内凹，双曲线辊)的角度变化对钽丝进行反复弯曲，使钽丝的残余应力均匀的分布在钽丝内部组织中，从而达到矫直的目的。常用的矫直方法还有热应力矫直方法，即通过连续走线的方式，将钽丝置于高温环境中，利用再结晶消除钽丝内部的残余应力[3]。钽丝之所以弯曲，是因为在拉拔过程中受到拉应力和压应力，两种力的作用大小不一而形成的；热应力矫直法是在放线张力和高温的作用下，消除钽丝中原有的拉应力和压应力，使弯曲的钽丝完全变直的过程。矫直后的钽丝在放线张力下绕在一定曲率半径的绕线盘上，绕线盘的曲率半径对钽丝的直线度影响很大，尤其对退火态钽丝的直线度影响更大。采用高温连续走线退火方法生产钽丝，钽丝微观组织细小、均匀，是生产高性能和直线度良好电容器级钽丝的有效工艺。本文通过优化连续退火工艺和矫直收线工艺来改善钽丝的直线度，从而提高钽丝的适用性。
1. 原料钽粉对钽丝直线度的影响
根据用户对钽丝耐高温性能要求的不同，以掺杂或非掺杂钽粉为原料，采用粉末冶金法生产具有耐高温性能的钽丝。在钽粉中掺杂可提高钽丝再结晶退火温度，细化钽丝晶粒度，提高钽丝强度，增加钽丝的抗变形能力[4]。
1.1 钽丝再结晶程度对直线度的影响
不同直线度的非掺杂钽丝(直径为0.8 mm)再结晶组织如图 1和图 2所示。从再结晶钽丝的晶粒度分析，直线度好的钽丝晶粒细小，没有出现晶粒长大的情况，说明退火不完全，没有将金属内部的残余应力完全消除。由于晶粒之间存在一定的变形抗力，在1800 ℃高温条件下退火，钽丝内部晶粒出现再结晶，晶粒明显细化且很均匀，说明晶粒之间存在的变形应力被完全消除，钽丝的直线度较好，退火后钽丝产品的抗拉强度较小。
![]()
图 1 直线度为4/100钽丝晶粒度Figure 1. Grain size of the tantalum wire with the straightness of 4/100![]()
图 2 直线度为0.4/100钽丝晶粒度Figure 2. Grain size of the tantalum wire with the straightness of 0.4/1001.2 原料钽粉掺杂和非掺杂对钽丝直线度的影响
采用掺杂(钇、硅)[5]钽粉制备钽丝，可在钽丝高温退火过程中细化钽丝组织晶粒度，起到细晶韧化、固溶强化和弥散强化的作用[6]，使钽丝具有更好的室温力学性能、漏电流、烧结折丝及抗氧脆性性能，因此在生产耐高温有机电容器中被普遍使用。在原料钽粉中掺杂钇制备钽丝，研究钽丝在高温退火后的直线度。
图 3和图 4所示为掺杂钇元素和非掺杂钽丝的显微组织晶粒度。由图可知，在相同退火条件下，掺杂钽丝的晶粒细小、均匀，非掺杂钽丝的晶粒粗大、不均匀。这表明掺杂钽丝的结晶程度不如非掺杂钽丝，这是因为钽丝中掺杂的钇元素均匀镶嵌在钽晶界上，抑制了钽晶粒的长大和回复，无法将残留在晶界上的残余应力消除干净[7]。为了完全消除掺杂钽丝中的残余应力，建议将高温连续退火温度控制在1650~1900 ℃，走线速度控制在10~40 m·min-1。晶界上的钇元素含量随着温度的升高逐渐降低，金属的抗拉强度也会逐渐降低，从而达到回复的目的。掺杂后的钽丝经过高温退火能有效提高其再结晶度，使退火后钽丝的直线度得到显著改善。
![]()
图 3 0.8 mm掺杂钇元素钽丝的晶粒度Figure 3. Grain size of the tantalum wire doping by yttrium element in the diameter of 0.8 mm![]()
图 4 0.8 mm非掺杂钽丝的晶粒度Figure 4. Grain size of the tantalum wire without doping in the diameter of 0.8 mm在相同退火条件下，掺杂和非掺杂钽丝的直线度如表 1所示。由表可知，在高温连续退火后，掺杂和非掺杂钽丝直线度的标准偏差分别为0.24和0.23，没有明显差异；经精绕密排后，掺杂钽丝直线度的标准偏差为0.16，非掺杂钽丝直线度的标准偏差为0.36，掺杂钽丝直线度的变化比非掺杂钽丝要小的多，其稳定性好。在相同退火条件下，虽然掺杂钽丝的再结晶过程已经形成，但晶粒大小远不及非掺杂钽丝晶粒的粗大，因此晶粒与晶界之间的应力相应也较大，相对抵制塑性变形的能力也较大。因此，在精绕密排过程中，掺杂钽丝即便发生一定的塑性变形，也没有非掺杂钽丝那么明显，掺杂钽丝的直线度明显好于非掺杂钽丝[8]。为满足轧制片式钽电解电容器阳极引线的要求，阳极引线优先选用掺杂的钽丝。
表 1 掺杂和非掺杂钽丝(0.8 mm)直线度Table 1. Straightness of the tantalum wires (0.8 mm) with and without doping次数 掺杂钽丝直线度，x/100 非掺杂钽丝直线度，x/100 连续退火后 产品精绕密排 连续退火后 产品精绕密排 第一次 0.80/100 1.70/100 0.80/100 2.80/100 第二次 1.00/100 1.70/100 1.00/100 2.40/100 第三次 1.40/100 1.50/100 1.20/100 3.10/100 第四次 0.80/100 1.30/100 0.80/100 2.20/100 第五次 0.80/100 1.50/100 0.60/100 2.40/100 第六次 0.80/100 1.40/100 0.60/100 2.20/100 均值 0.93/100 1.52/100 0.83/100 2.52/100 标准差 0.24/100 0.16/100 0.23/100 0.36/100 2. 高温退火工艺对钽丝直线度的影响
2.1 钽丝高温退火前的直线度对退火后钽丝直线度的影响
选用同批次ϕ0.6 mm掺杂钽丝。在高温连续退火前，对部分钽丝进行矫直，对另外一部分钽丝未进行矫直，两种钽丝经高温退火后直线度的对比试验结果如表 2所示[9]。从表 2可以看出，退火前钽丝的直线度对退火后钽丝的直线度有显著影响，这是因为走线式连续退火不可能将钽丝的残余内应力完全消除，退火后钽丝发生的塑性变形是不完全的，丝材弯曲一侧的压应力和另一侧的拉应力没有被完全消除[10]。在高温退火前对钽丝进行一次热应力矫直过程，均衡了弯曲两侧的拉应力和压应力，使得丝材的直线度变得均匀可控。
表 2 退火前钽丝直线度对退火后钽丝直线度的影响Table 2. Effect of the tantalum wire straightening before annealing on the tantalum wire straightening after annealing工艺 钽丝直线度，x/100 退火前矫直 退火前未矫直 退火前 3.00/100 6.00/100 退火后 2.00/100 3.50/100 均值 2.50/100 4.75/100 标准差 0.71/100 1.77/100 2.2 走线式连续退火的放线张力对钽丝直线度的影响
选用同批次ϕ0.8 mm掺杂钽丝，在高温连续退火过程中(温度1650~1900 ℃，走线速度10~40 m·min-1)，采用不同放线张力(0.5 kg和0.9kg)进行试验，退火后钽丝的直线度如图 5所示。由图可知，随着张力的增大，退火后钽丝的直线度在逐渐变好，由原来最大5.0/100变为最小0.8/100。这是因为钽丝在连续走线式退火过程中，张力的增大给直线度差的钽丝一个拉应力和一个压应力，这种拉应力、压应力越大，在高温再结晶回复越明显[11]。但是这种拉应力、压应力不可能无限制增加，在钽丝不发生塑性变形的前提下，可以提高拉应力、压应力，否则钽丝在高温下极易发生塑性变形[12]，从而在宏观上表现为钽丝变细。通过试验发现，当钽丝直径大于ϕ0.6 mm时，张力增加到0.9 kg对钽丝直径影响不大。
![]()
图 5 退火放线张力对钽丝直线度的影响Figure 5. Effect of the payoff tension on the straightness of tantalum wire during annealing2.3 连续退火出炉口定位轮直径对退火后钽丝直线度的影响
走线式连续退火炉因为是连续走线，钽丝在出炉口时温度很高，在出炉后经过出炉口定位轮时，由于走线方向发生一定角度的转向，此时定位轮会给钽丝施加一定的外力(F外，如式(1)所示)，这种外力极易让钽丝发生塑性变形，从而影响钽丝直线度。为了减少这种外力，唯一可以改变的是增大定位轮的直径。由向心力公式(式(2))可知，增加定位轮直径，可以减小定位轮转动产生的向心力(F向)[13]。
$$ F_{\text {外 }}=F_{\text {向 }} $$ (1) $$ F_{\text {向 }}=M v^{2} / R $$ (2) 式中：F外为定位轮给钽丝施加的外力；F向为定位轮转动产生的向心力；R为定位轮直径；M为定位轮质量；v为定位轮转速。
选用同批次ϕ0.8 mm掺杂钽丝，通过将连续退火出炉口定位轮直径由原来的220 mm增加到300 mm，在速度v不变的情况下，减少外力F外的方法进行试验，改进钽丝的直线度，结果如表 3所示。从表可知，经过增加连续退火出炉口定位轮直径后，钽丝的直线度得到明显改善。
表 3 续退火出炉口定位轮直径对退火后钽丝直线度的影响Table 3. Effect of the wheel diameter of tap hole on the straightness of tantalum wire after annealing导轮直径/ mm 钽丝直线度，x/100 220 2.4/100 300 0.8/100 3. 钽丝精绕密排中收线盘直径的大小对钽丝直线度的影响
通常钽丝经过高温退火后，收线排列比较松散，需要对钽丝进行精绕密排，防止钽丝发生松丝、乱丝的现象，在存储、搬运和使用过程中影响钽丝的直线度。选用同批次ϕ0.8 mm掺杂钽丝，采用直径不同的收线盘进行精绕密排试验，在相同的精绕密排工艺条件下，钽丝的直线度如表 4所示。从表 4可以看出，对于密排前直线度相同的钽丝，在相同的精绕密排工艺条件下，密排到直径不同的收线盘上，测试出的钽丝直线度有明显的差距，随着收线盘直径的增大，其直线度变好。通常钽丝的精绕密排过程是需要一定的张力，这种张力情况与前面提到的退火收线一样，对钽丝也会造成一定的塑性变形，塑性变形在弹性变形范围之内发生，一定程度上会有回复，但塑性变形发生在弹性变形范围之外，就会产生永久性变形，从而影响钽丝的直线度。
表 4 矫直收线盘直径的大小对钽丝直线度的影响Table 4. Effect of the straightening coil diameter on the straightness of tantalum wire精绕收线盘直径/ mm 钽丝直线度，x/100 密排前 密排后 230 1.2/100 2.4/100 300 1.2/100 1.3/100 4. 结论
(1) 通过高温连续退火，掺杂钽丝的晶粒比非掺杂钽丝晶粒小且更加均匀，晶粒与晶界之间的应力也相应较大，抵制塑性变形的能力也较大，掺杂钽丝的直线度明显好于非掺杂钽丝。为满足轧制片式钽电解电容器阳极引线的要求，阳极引线优先选用掺杂的钽丝。
(2) 钽丝退火前的直线度极大影响着退火后产品的直线度，因此在退火前必须进行去应力矫直过程。
(3) 走线式连续退火的放线张力对钽丝直线度有一定的影响，张力越大，直线度越好，但不能无限增加，否则钽丝直径会发生变化。
(4) 连续退火出炉口定位轮直径越大，钽丝的直线度越好；矫直收线盘的直径越大，钽丝的直线度越好。
-
![]()
图 1 气雾化预合金粉末显微形貌：(a)放大500倍；(b)放大1000倍
Figure 1. Microstructures of the prealloyed powders by gas atomization: (a) ×500; (b) ×1000
![]()
图 2 热等静压烧结体显微组织形貌：(a)放大1000倍；(b)放大5000倍
Figure 2. Microstructures of the HIPed sintering alloys: (a) ×1000; (b) ×5000
![]()
图 3 预合金粉末和热等静压烧结体的X射线衍射图谱
Figure 3. XRD spectra of the prealloyed powders and the HIPed sintering alloys
![]()
图 4 不同烧结温度下热等静压烧结体的金相组织：(a)900 ℃；(b)1000 ℃；(c)1050 ℃；(d)1100 ℃
Figure 4. Microstructures of the HIPed sintering alloys at different sintering temperatures: (a) 900 ℃; (b) 1000 ℃; (c) 1050 ℃; (d) 1100 ℃
![]()
图 5 不同烧结温度下热等静压烧结体的密度
Figure 5. Density of the HIPed sintering alloys at different sintering temperatures
![]()
图 6 经过不同热等静压烧结温度制备的试样在室温条件下的力学性能
Figure 6. Mechanical properties at room-temperature of the sample prepared by HIP at different sintering temperatures
![]()
图 7 经过不同热等静压烧结温度制备的试样在650 ℃高温条件下的力学性能
Figure 7. Mechanical properties at 650 ℃ of the sample prepared by HIP at different sintering temperatures
![]()
图 8 经过不同热等静压烧结温度制备的试样在室温和650 ℃高温拉伸断口形貌：(a)烧结温度1050 ℃，室温；(b)烧结温度1050 ℃，高温；(c)烧结温度1100 ℃，室温；(d)烧结温度1100 ℃，高温
Figure 8. Tension fracture morphology at room temperature and 650 ℃ of the samples prepared by HIP at different sintering temperatures: (a) 1050 ℃, room temperature; (b) 1050 ℃, high temperature; (c) 1100 ℃, room temperature; (d) 1100 ℃, high temperature
表 1 铁镍基合金粉末化学成分(质量分数)
Table 1 Chemical composition of the Fe–Co–Ni based alloy powders
% Fe Ni Co Cr Mo W Nb C 其余 14.18 20.36 23.41 17.80 11.82 4.32 3.25 0.45 4.41 
下载: 导出CSV
-
[1] 王琪, 李圣刚, 吕宏军, 等. 雾化法制备高品质钛合金粉末技术研究. 钛工业进展, 2010, 27(5): 16 DOI: 10.3969/j.issn.1009-9964.2010.05.004 Wang Q, Li S G, Lü H J, et al. Research on high quality titanium alloy powder production by atomization technology. Titanium Ind Prog, 2010, 27(5): 16 DOI: 10.3969/j.issn.1009-9964.2010.05.004
[2] Yuan W X, Mei J, Samarov V, et al. Computer modeling and tooling design for near net shaped components using hot isostatic pressing. J Mater Process Technol, 2006, 182(1-3): 39 http://www.sciencedirect.com/science/article/pii/S0924013606006571
[3] 胡文波, 贾成厂, 胡本芙, 等. 氩气雾化法制备FGH96高温合金粉末颗粒的凝固组织. 粉末冶金材料科学与工程, 2011, 16(5): 671 DOI: 10.3969/j.issn.1673-0224.2011.05.006 Hu W B, Jia C C, Hu B F, et al. Solidification microstructure of FGH96 superalloy powder prepared by argon gas atomization. Mater Sci Eng Powder Metall, 2011, 16(5): 671 DOI: 10.3969/j.issn.1673-0224.2011.05.006
[4] 徐裕来. 超超临界汽轮机叶片用高温合金Nimonic 80A成分优化、微结构及其高温强化机理研究[学位论文]. 上海: 上海大学, 2013 Xu Y L. Chemical Composition Optimization, Microstructure and High Temperature Strengthening Mechanism of Nimonic 80A for Ultra-Supercritical Steam Turbine Blade [Dissertation]. Shanghai: Shanghai University, 2013
[5] 何树先, 王俊, 孙宝德. 热等静压处理对K4169高温合金显微形貌及性能的影响. 铸造技术, 2013, 34(12): 1646 https://www.cnki.com.cn/Article/CJFDTOTAL-ZZJS201312018.htm He S X, Wang J, Sun B D. Effect of HIP treatment on the microstructures and properties of K4169 superalloy. Foundry Technol, 2013, 34(12): 1646 https://www.cnki.com.cn/Article/CJFDTOTAL-ZZJS201312018.htm
[6] Wu X Q, Jing H M, Zheng Y G, et al. The eutectic carbides and creep rupture strength of 25Cr20Ni heat-resistant steel tubes centrifugally cast with different solidification conditions. Mater Sci Eng A, 2000, 293(1-3): 252 http://www.sciencedirect.com/science/article/pii/S0921509300009849
[7] 肖璇, 周兰章, 郭建亭. 镍基高温合金U720Li的组织稳定性及蠕变行为. 金属学报, 2001, 37(11): 1159 DOI: 10.3321/j.issn:0412-1961.2001.11.006 Xiao X, Zhou L Z, Guo J T. Microstructural stability and creep behavior of nickel base superalloy U720Li. Acta Metall Sinica, 2001, 37(11): 1159 DOI: 10.3321/j.issn:0412-1961.2001.11.006
[8] 郭建亭, 周兰章, 袁超, 等. 我国独创和独具特色的几种高温合金的组织和性能. 中国有色金属学报, 2011, 21(2): 237 https://www.cnki.com.cn/Article/CJFDTOTAL-ZYXZ201102002.htm Guo J T, Zhou L Z, Yuan C, et al. Microstructure and properties of several originally invented and unique superalloys in China. Chin J Nonferrous Met, 2011, 21(2): 237 https://www.cnki.com.cn/Article/CJFDTOTAL-ZYXZ201102002.htm
[9] 孙崇锋, 党晓凤, 李生文, 等. 铁镍钴基高温合金雾化粉末烧结特性及显微组织. 稀有金属材料与工程, 2016, 45(12): 3115 https://www.cnki.com.cn/Article/CJFDTOTAL-COSE201612016.htm Sun C F, Dang X F, Li S W, et al. Sintering properties and microstructure of Fe–Ni–Co-based superalloy atomized powder. Rare Met Mater Eng, 2016, 45(12): 3115 https://www.cnki.com.cn/Article/CJFDTOTAL-COSE201612016.htm
[10] 谢辅洲, 杨世伟, 高丽, 等. 高温合金渗铝涂层抗高温氧化性能的研究. 热加工工艺, 2004(3): 11 DOI: 10.3969/j.issn.1001-3814.2004.03.005 Xie F Z, Yang S W, Gao L, et al. Study on high temperature oxidation properties of aluminized coating on superalloy. Hot Working Technol, 2004(3): 11 DOI: 10.3969/j.issn.1001-3814.2004.03.005
[11] Furrer D U, Shankar R, White C. Optimizing the heat treatment of Ni-based superalloy turbine discs. JOM, 2003, 55: 32 DOI: 10.1007/s11837-003-0157-0
[12] 崔令江, 林熙原, 朱强, 等. 高温合金热处理工艺研究进展. 材料导报, 2016, 30(13): 106 https://www.cnki.com.cn/Article/CJFDTOTAL-CLDB201613017.htm Cui L J, Lin X Y, Zhu Q, et al. Research progress on heat treatment process of superalloys. Mater Rev, 2016, 30(13): 106 https://www.cnki.com.cn/Article/CJFDTOTAL-CLDB201613017.htm
[13] 黄乾尧, 李汉康. 高温合金. 北京: 冶金工业出版社, 2000 Huang Q Y, Li H K. High Temperature Alloy. Beijing: Metallurgical Industry Press, 2000
[14] 邵卫东, 童潮山, 庄伟. 新型钴基高温合金成分设计及其组织与性能. 机械工程材料, 2005, 29(9): 41 DOI: 10.3969/j.issn.1000-3738.2005.09.013 Shao W D, Tong C S, Zhuang W. Composition design of a new cobalt base superalloy and its microstructure and properties. Mater Mechan Eng, 2005, 29(9): 41 DOI: 10.3969/j.issn.1000-3738.2005.09.013
[15] 雷应毅, 姚泽坤, 宁永权, 等. 热处理对粉末高温合金不均匀变形的改善作用. 稀有金属材料与工程, 2012, 41(9): 1689 DOI: 10.3969/j.issn.1002-185X.2012.09.039 Lei Y Y, Yao Z K, Ning Y Q, et al. Improvement of forging heat treatment on inhomogeneous deformation of P/M superalloy. Rare Met Mater Eng, 2012, 41(9): 1689 DOI: 10.3969/j.issn.1002-185X.2012.09.039
[16] 邹金文, 汪武祥. 粉末高温合金研究进展与应用. 航空材料学报, 2006, 26(3): 244 DOI: 10.3969/j.issn.1005-5053.2006.03.051 Zou J W, Wang W X. Development and application of P/M superalloy. J Aeron Mater, 2006, 26(3): 244 DOI: 10.3969/j.issn.1005-5053.2006.03.051