Effect of SiC on thermoelectric properties of P-type Bi0.5Sb1.5Te3 alloy prepared by pulverizing and sintering method
-
摘要: 向粉碎法制备的Bi0.5Sb1.5Te3+5%Te（质量分数）合金粉体中混入不同体积分数的SiC颗粒，利用放电等离子体烧结法制备SiC复合块体材料，探究块体材料组织和热电性能的变化规律。研究发现：随着SiC体积分数的增加，块体材料的取向性弱化，组织细化，载流子浓度增加，迁移率降低；由于取向性弱化及组织细化，加强了声子散射，降低了晶格热导率。由于SiC复合块体材料的电学性能恶化，块体材料的无量纲热电优值（ZT）并未获得显著的提升；当SiC体积分数为0.40%时，SiC复合块体材料在322 K时具有最优的无量纲热电优值（ZT=～0.81）。
-
关键词:
- Bi0.5Sb1.5Te3 /
- SiC复合 /
- 粉碎烧结 /
- 热电性能
Abstract: SiC particles in the different volume fraction were mixed into Bi0.5Sb1.5Te3+5%Te alloy powders (mass fraction) prepared by the pulverizing method. The mixed powders were sintered into the blocks by spark plasma sintering (SPS) method. The microstructure and thermoelectric properties of these block samples were investigated. The results show that, with the increase of SiC volume fraction, the orientation of the bulks is weakened, the microstructure is refined, the carrier concentration increases, and the mobility decreases. Due to the weakened orientation and the refined microstructure, the scattering of phonons is enhanced, leading to a reduced lattice thermal conductivity. However, due to the deterioration of the electrical properties for the blocks, the dimensionless thermoelectric value (ZT) of the bulks with SiC has no improvement. When the volume fraction of SiC is 0.40%, the block samples show the best thermoelectric performance with ZT = ~0.81 at 322 K.-
Keywords:
- Bi0.5Sb1.5Te3 /
- SiC composite /
- pulverizing and sintering /
- thermoelectric properties
-
粉末冶金摩擦材料是一种含有金属和非金属的多组元假合金。一般由基体组元、摩擦组元和润滑组元三部分组成[1-2]。与有机摩擦材料相比, 粉末冶金摩擦材料的力学强度高、抗冲击载荷强、摩擦系数稳定、热稳定性高、热传导性好、抗腐蚀能力强, 以及耐磨性能优良, 是现代刹车材料中应用较为广泛的材料之一[3-5]。目前已被应用于各种大型民用飞机、高性能军用飞机、火车、汽车、风电行业以及其它机械制动装置中[6-10]。
相对比于铁基粉末冶金摩擦材料高温下容易产生胶合、摩擦系数波动大、异常磨损明显、噪声大等情况, 铜基摩擦材料因其良好的导热性和自润湿性能, 在干、湿条件下均具备稳定的摩擦性能, 并在高速制动摩擦过程中, 基体与铜结构形成热扩散通道, 能够在相对短的时间内将大量摩擦热散发到环境中, 有效避免了热聚集引起胶粘对制动盘性能造成不利的影响[11]。长期以来, 对铜基粉末冶金摩擦材料的研究主要集中在配方研究和制备工艺对摩擦磨损性能的影响方面, 而刹车速度对铜基粉末冶金摩擦材料的摩擦磨损机理的研究相对较少。本文以铜基粉末冶金摩擦材料为研究对象, 探讨不同的刹车速度对铜基粉末冶金摩擦材料摩擦磨损性能的影响规律, 并对其微观组织进行研究表征, 为新型铜基粉末冶金摩擦材料的深入研究提供参考与理论支持。
1. 实验
1.1 试样制备
实验中所用的材料主要包括电解铜粉、还原铁粉、鳞片状天然石墨, SiO2粉和铬铁等。按表 1的配方分别称取各种粉料, 并在双锥形混合机中混合20~24 h, 将混合均匀的混合料制成压坯, 压坯尺寸为20 mm×15 mm, 厚度大于5 mm。将压坯置于钟罩式加压烧结炉内, 并在氢气保护气氛中进行加压烧结, 烧结温度为850~900℃, 烧结压力为0.3~0.5 MPa, 烧结时间为3.5~4 h。烧结完成后冷却至500℃后再随箱水冷至≤60℃, 出砂。
表 1 铜基粉末冶金摩擦材料化学成分(质量分数)Table 1. Chemical composition of the copper-based powder metallurgy brake materials% Cu Sn Fe SiO2 铬铁 其它 60~70 1~6 6~15 5~10 2~5 10~20 1.2 性能表征
采用JEOL公司的JSM-6390A型扫描电子显微镜(scanning electron microscope, SEM)对铜基粉末冶金摩擦材料实验前后的表面形貌进行观测; 采用HRF-150型洛氏硬度计和夏比冲击试验机分别对烧结后粉末层的硬度和冲击韧性进行表征; 在MM-3000型摩擦磨损性能试验台上进行摩擦磨损性能试验, 对偶盘材料为30CrMnSiA。试验前, 摩擦副表面先磨合至摩擦副贴合面积≥80%, 摩擦磨损试验条件及要求见表 2。
表 2 摩擦磨损试验条件Table 2. Condition of friction and wear test编号 惯量/ (kg·m2) 刹车压力/ MPa 刹车速度/ (m·s-1) 刹车转速/ (r·min-1) 次数 1# 0.225 0.66 27.78 2652 10 2# 33.33 3183 10 3# 38.89 3714 10 4# 44.44 4244 10 5# 50.00 4775 10 6# 55.56 5305 10 摩擦试验机记录摩擦吸收功率、刹车力矩与刹车时间关系。根据式(1)可计算出摩擦系数。
$$ \mu = \frac{{2M}}{{\left( {{\gamma _1} + {\gamma _2}} \right) \cdot F}} $$ (1) 式中:μ为摩擦系数, M为力矩(N·m), F为荷重(N), γ1为内圈半径(m), γ2为外圈半径(m)。用电子天平测量试样摩擦试验前后的质量变化; 用千分尺测量试样上6个不同位置处摩擦试验前后的厚度变化, 计算出摩擦试验前后试样厚度差, 求出平均值即试样的线性磨损量。
2. 结果与分析
2.1 微观结构
图 1为烧结后铜基粉末冶金摩擦材料表面显微组织形貌。图中黑色的为鳞片石墨, 白色的为铜, 灰色的可能为铁、铬铁或SiO2颗粒。从图可以看出, 大量的鳞片石墨稳定地分布在铜基体当中, 从而保证了刹车过程的平稳性和摩擦系数的稳定性。从图 1 (b)可以清楚地看到大量的灰色颗粒, 其中近似球状的较大颗粒为铬铁(200目, 如箭头所示), 其与基体接触良好, 两者之间观测不到明显的界面[12]; 较小的球状物可能为铁、二氧化硅等颗粒(100目); 这些颗粒均匀地分布在铜基体当中, 铜基体包裹着鳞片状石墨分布在摩擦片表面, 具有稳定的摩擦系数。
2.2 物理性能
铜基粉末冶金摩擦材料的力学性能如表 3所示。从表中可以看出, 摩擦材料的密度较高, 说明摩擦材料中的非金属组元所占体积较小; 材料的洛氏硬度较低, 说明摩擦试验中的对偶磨损相对较小; 材料的抗冲击韧性较大, 表明摩擦组元在材料烧结过程中以机械镶嵌的方式存在基体材料中, 提高了摩擦材料的耐磨性。在高速刹车过程中, 摩擦材料的力学性能确保了其在较大冲击力和较大磨损量条件下的使用。
表 3 摩擦材料的力学性能Table 3. Mechanical properties of friction material密度/ (g·cm-3) 洛氏硬度，HB 冲击韧性/ (J·cm-2) ≥5.72 ≥27 ≥33.5 2.3 摩擦磨损试验
图 2为试样在55.56 m/s刹车速度下的摩擦磨损曲线图。在此刹车速度下, 最大摩擦系数为0.5061, 平均摩擦系数为0.4521;经计算, 离均差率为11.94%, 较小的离均差率说明了铜基摩擦材料具有稳定的摩擦系数。从图中还可以看出, 摩擦系数曲线无明显的振颤现象, 力矩曲线也呈稳定增长趋势, 这也充分表明了该铜基粉末冶金摩擦材料的刹车制动效果平稳, 产生这种现象的原因可能是由于摩擦材料配方中摩擦组元铬铁和铜基体具有良好的润湿性能, 从而提高了摩擦系数的稳定性[12]。
![]()
图 2 铜基粉末冶金摩擦材料在55.56 m/s刹车速度下的摩擦数据曲线Figure 2. Friction curves of Cu-based powder metallurgy material at the braking velocity of 55.56 m/s图 3 (a)是在不同刹车速度条件下摩擦磨损性能试验后试样的摩擦吸收功率和摩擦系数曲线图。摩擦吸收功率是指试样在单位时间单位面积内所吸收的功, 它与摩擦面的温度升高有着直接对应关系, 因此影响试样的摩擦系数。从图 3 (a)可以看出, 随着刹车速度增大, 刹车能量升高, 摩擦面的温度进一步升高, 试样的摩擦吸收功率呈近似线性升高。刹车速度从27.78 m/s增加到44.44 m/s, 试样的摩擦吸收功率速率增长最快; 当刹车速度从44.44 m/s增加到55.56 m/s, 试样的摩擦吸收功率增加相对缓慢, 这表明铜基粉末冶金摩擦材料在低速条件下, 吸收的动能可能主要被铜基摩擦材料中的孔隙吸收并传导到空气当中; 当制动速率超过44.4 m/s时, 摩擦材料的吸收动能会被铜基摩擦材料自身所吸收, 并通过高的导热性将吸收能量传导至空气中。从图中还可以看出, 当刹车速度从27.78 m/s增加到44.44 m/s时, 摩擦系数也相对从0.4040增加到0.5071。但随着刹车速率的提高, 试样的摩擦系数出现了明显下降的趋势, 这可能与摩擦材料的摩擦机理和微观结构有关。
![]()
图 3 不同刹车速度下铜基粉末冶金摩擦材料的摩擦系数和摩擦吸收功率曲线(a)及线性磨损率和质量损失曲线(b)Figure 3. Relationships of friction absorption power–friction coefficient (a) and linear wear rate–mass loss (b) with braking velocity of Cu-based powder metallurgy friction material图 3 (b)是在不同刹车速度条件下摩擦磨损性能试验后试样的线性磨损率和质量磨损。从图 3 (b)可以看出, 试样的线磨损率随刹车速度的变化与质量损失随刹车速度的变化一致, 都呈上升的趋势。当刹车速度从27.78 m/s增加到33.33 m/s, 试样的线磨损率和质量磨损均较大, 这是由于在较低的速度下, 刹车未进入平稳阶段, 出现了较为明显的磨粒磨损; 当刹车速度从33.33 m/s增加到50.00 m/s时, 粘着磨损起主要作用, 因此线性磨损率和质量磨损都相对较小; 当刹车速率增长至55.56 m/s时, 试样的质量磨损呈明显增长趋势, 这可能是由于在高速条件下, 铜基摩擦材料自身软化造成摩擦组元脱落, 从而质量损耗明显。但由于线性磨损率数据的获得是通过千分尺测量一定面积上的厚度损耗而计算得到的, 因此线性磨损率并不能完全反应出摩擦组元的脱落引起厚度的微小变化, 因而线性损耗率增长不明显。
为进一步研究刹车速度对摩擦磨损性能的影响, 探讨摩擦磨损性能与摩擦面的关系, 采用扫描电子显微镜对在不同刹车速度下试样的摩擦面进行分析。图 4所示为不同刹车速度试验后铜基粉末冶金摩擦材料表面的扫描电子显微形貌。从图中可以看出, 当刹车速度为27.78 m/s和33.33 m/s时, 由于刹车速度较低, 摩擦剪切力较小, 因此摩擦表面温度较低, 且未能形成连续完整的氧化膜, 从而出现了较小面积的剥落且剥落的块状物较小, 其中剥落后较小的硬质颗粒在剪切力作用下从摩擦表面脱落, 在摩擦副之间形成磨粒, 在摩擦表面产生犁沟, 发生磨料磨损和剥层损耗, 其磨损主要是由机械啮合作用造成的; 当刹车速度为38.89 m/s和44.44 m/s时, 摩擦表面较为光滑, 无明显的脱落。这是由于随着刹车速度的增大, 摩擦吸收功率增大, 摩擦面的温度提高, 摩擦剪切力的作用也逐渐增强, 氧化膜趋于平滑连续, 摩擦表面与摩擦副的真实接触面积越大, 其机械啮合作用减弱, 粘着机理起主要作用。随着刹车速度的进一步增大, 摩擦表面在较大剪切力的作用下发生了较为严重的脱落。当刹车速度从50.00 m/s逐渐增大到55.56 m/s, 试样摩擦表面单位面积吸收的能量进一步增大, 温度进一步升高, 摩擦表面在较大剪切力的作用下发生了较为严重的脱落。这是由于摩擦产生的高温引起材料软化, 破坏了形成的氧化膜, 降低了分子键的抗剪切强度, 从而在摩擦面上出现了不同程度的犁沟[13-14]。
![]()
图 4 铜基粉末冶金摩擦材料在不同刹车速度下的扫描电子显微形貌Figure 4. SEM images of the Cu-based powder metallurgy friction material under the different velocity3. 结论
(1) 铜基粉末冶金摩擦材料的摩擦磨损性能与刹车速度密切相关。随着刹车速度的增大, 刹车能量急剧升高, 摩擦材料的摩擦吸收功率近似线性增长, 而摩擦系数呈先增大后减小的趋势, 并且铜基粉末冶金摩擦材料的线磨损率与质量磨损随刹车速度增长呈上升趋势。
(2) 在一定的刹车速度下, 铜基粉末冶金摩擦材料摩擦表面的氧化膜愈趋平滑连续。但随着刹车速度的提高, 铜基体自身发生软化, 破坏了已形成的氧化膜, 降低了分子键的抗剪切强度, 从而增大了磨损量。
-
![]()
图 1 烧结块体样品沿垂直烧结压力方向上的X射线衍射图谱
Figure 1. XRD patterns of the bulk samples along the vertical sintering pressure direction
![]()
图 2 添加不同体积分数SiC颗粒的烧结块体样品断口显微形貌：（a）0.00；（b）0.20；（c）0.40；（d）0.60
Figure 2. SEM images of the fracture surfaces of the sintered bulk samples added by SiC particles in the different volume fraction: (a) 0.00; (b) 0.20; (c) 0.40; (d) 0.60
![]()
图 3 样品0.40显微组织形貌及能谱分析：（a）SiC颗粒显微形貌；（b）SiC颗粒被基体均匀包覆；（c）位置1能谱分析谱
Figure 3. SEM images and EDS patterns of the sample 0.40: (a) microstructure of SiC particles; (b) microstructure of SiC particles covered by the matrix; (c) EDS patterns at position 1
![]()
图 4 样品0.40中各主要组元能谱面扫描分布
Figure 4. EDS mapping scanning of the sample 0.40 for the main elements
![]()
图 5 材料电学性能随温度变化规律：（a）电导率；（b）Seebeck系数；（c）功率因子
Figure 5. Temperature dependence of the electrical properties for the bulk samples: (a) electrical conductivity; (b) Seebeck coefficient; (c) powder factor
![]()
图 6 样品室温载流子浓度和迁移率随SiC体积分数变化规律
Figure 6. SiC volume fraction dependence of the carrier concentration and mobility for the bulk samples at room temperature
![]()
图 7 Seebeck系数与载流子浓度之间的Pisarenko关系
Figure 7. Pisarenko relationship between the Seebeck coefficient and carrier concentration
![]()
图 8 材料热学性能随温度变化规律：（a）热导率；（b）电子热导率；（c）晶格热导率和双极热导率
Figure 8. Temperature dependence of the thermal properties for the bulk samples. (a) thermal conductivity; (b) electron thermal conductivity; (c) lattice thermal conductivity and bipolar effect
表 1 块体样品在垂直烧结压力方向上沿着（00l）方向的取向因子
Table 1 Orientation factor of the bulk samples along the direction of (00l) at the vertical sintering pressure direction
样品 0.00 0.20 0.40 0.60 取向因子 0.1821 0.1564 0.1294 0.1050 
下载: 导出CSV
-
[1] Bell L E. Cooling, heating, generating power, and recovering waste heat with thermoelectric systems. Science, 2008, 321(5895): 1457 DOI: 10.1126/science.1158899
[2] DiSalvo F J. Thermoelectric cooling and power generation. Science, 1999, 285(5428): 703 DOI: 10.1126/science.285.5428.703
[3] Dresselhaus M S, Chen G, Tang M Y, et al. New directions for low-dimensional thermoelectric materials. Adv Mater, 2007, 19(8): 1043 DOI: 10.1002/adma.200600527
[4] Ginting D, Lin C C, Lydia R, et al. High thermoelectric performance in pseudo quaternary compounds of (PbTe)0.95−x(PbSe)x(PbS)0.05 by simultaneous band convergence and nano precipitation. Acta Mater, 2017, 131: 98
[5] Takagiwa Y, Pei Y, Pomrehn G, et al. Dopants effect on the band structure of PbTe thermoelectric material. Appl Phys Lett, 2012, 101(9): 092102 DOI: 10.1063/1.4748363
[6] Basu R, Bhattacharya S, Bhatt R, et al. Improved thermoelectric properties of Se-doped n-type PbTe1−xSex (0≤x≤1). J Electron Mater, 2013, 42(7): 2292 DOI: 10.1007/s11664-013-2645-5
[7] Ohno S, Imasato K, Anand S, et al. Phase boundary mapping to obtain n-type Mg3Sb2-based thermoelectrics. Joule, 2018, 2(1): 141 DOI: 10.1016/j.joule.2017.11.005
[8] Gelbstein Y, Davidow J, Girard S N, et al. Controlling metallurgical phase separation reactions of the Ge0.87Pb0.13Te alloy for high thermoelectric performance. Adv Energy Mater, 2013, 3(6): 815
[9] Kim Y M, Lydia R, Kim J H, et al. Enhancement of thermoelectric properties in liquid-phase sintered Te-excess bismuth antimony tellurides prepared by hot-press sintering. Acta Mater, 2017, 135: 297 DOI: 10.1016/j.actamat.2017.06.036
[10] Hor Y S, Richardella A, Roushan P, et al. p-type Bi2Se3 for topological insulator and low-temperature thermoelectric applications. Phys Rev B, 2009, 79(19): 195208 DOI: 10.1103/PhysRevB.79.195208
[11] Zhu T, Hu L, Zhao X, et al. New insights into intrinsic point defects in V2VI3 thermoelectric materials. Adv Sci, 2016, 3(7): 1600004 DOI: 10.1002/advs.201600004
[12] Zhu T, Liu Y, Fu C, et al. Compromise and synergy in high-efficiency thermoelectric materials. Adv Mater, 2017, 29(14): 1605884 DOI: 10.1002/adma.201605884
[13] Hu L, Wu H, Zhu T, et al. Tuning multiscale microstructures to enhance thermoelectric performance of n-type Bismuth-Telluride-based solid solutions. Adv Energy Mater, 2015, 5(17): 1500411 DOI: 10.1002/aenm.201500411
[14] Hu L P, Zhu T J, Wang Y G, et al. Shifting up the optimum figure of merit of p-type bismuth telluride-based thermoelectric materials for power generation by suppressing intrinsic conduction. NPG Asia Mater, 2014, 6(2): e88 DOI: 10.1038/am.2013.86
[15] Zhai R, Hu L, Wu H, et al. Enhancing thermoelectric performance of n-type hot deformed bismuth-telluride-based solid solutions by nonstoichiometry-mediated intrinsic point defects. ACS Appl Mater Interfaces, 2017, 9(34): 28577 DOI: 10.1021/acsami.7b08537
[16] Hu L, Zhu T, Liu X, et al. Point defect engineering of high-performance bismuth-telluride-based thermoelectric materials. Adv Funct Mater, 2014, 24(33): 5211 DOI: 10.1002/adfm.201400474
[17] Xu Z J, Hu L P, Ying P J, et al. Enhanced thermoelectric and mechanical properties of zone melted p-type (Bi, Sb)2Te3 thermoelectric materials by hot deformation. Acta Mater, 2015, 84: 385 DOI: 10.1016/j.actamat.2014.10.062
[18] Zhu B, Huang Z Y, Wang X Y, et al. Attaining ultrahigh thermoelectric performance of direction-solidified bulk n-type Bi2Te24Se0.6 via its liquid state treatment. Nano Energy, 2017, 42: 8
[19] Jiang J, Chen L, Bai S, et al. Fabrication and thermoelectric performance of textured n-type Bi2(Te, Se)3 by spark plasma sintering. Mater Sci Eng B, 2005, 117(3): 334 DOI: 10.1016/j.mseb.2005.01.002
[20] Mun H, Choi S M, Lee K H, et al. Boundary engineering for the thermoelectric performance of bulk alloys based on bismuth telluride. ChemSusChem, 2015, 8(14): 2312 DOI: 10.1002/cssc.201403485
[21] Pei Y, Lalonde A, Iwanaga S, et al. High thermoelectric figure of merit in heavy hole dominated PbTe. Energy Environ Sci, 2011, 4(6): 2085 DOI: 10.1039/c0ee00456a
[22] Chen Z, Zhang X, Pei Y. Manipulation of phonon transport in thermoelectrics. Adv Mater, 2018, 30(17): 1705617 DOI: 10.1002/adma.201705617
[23] Lostak P, Novotny R, Kroutil J, et al. Optical properties of Sb2‒xInxTe3 single crystals. Phys Status Solidi A, 1987, 104(2): 841 DOI: 10.1002/pssa.2211040238
[24] Chen Z, Jian Z, Li W, et al. Lattice dislocations enhancing thermoelectric PbTe in addition to band convergence. Adv Mater, 2017, 29(23): 1606768 DOI: 10.1002/adma.201606768
[25] Tan G, Stoumpos C C, Wang S, et al. Subtle roles of Sb and S in regulating the thermoelectric properties of N-type PbTe to high performance. Adv Energy Mater, 2017, 7(18): 1700099 DOI: 10.1002/aenm.201700099
[26] Biswas K, He J, Blum I D, et al. High-performance bulk thermoelectrics with all-scale hierarchical architectures. Nature, 2012, 489(7416): 414 DOI: 10.1038/nature11439
[27] Lotgering F K. Topotactical reactions with ferrimagnetic oxides having hexagonal crystal structures. J Inorg Nucl Chem, 1959, 9(2): 113 DOI: 10.1016/0022-1902(59)80070-1
[28] Ioffe A F. Semiconductor Thermoelements and Thermoelectric Cooling. London: Infosearch Limited, 1957
[29] Wang X Y, Wang H J, Xiang B, et al. Thermoelectric performance of Sb2Te3-based alloys is improved by introducing PN junctions. ACS Appl Mater Interfaces, 2018, 10(27): 23277 DOI: 10.1021/acsami.8b01719
[30] Wang S, Sun Y, Yang J, et al. High thermoelectric performance in Te-free (Bi, Sb)2Se3 via structural transition induced band convergence and chemical bond softening. Energy Environ Sci, 2016, 9(11): 3436 DOI: 10.1039/C6EE02674E
[31] Hong M, Chen Z G, Yang L, et al. Enhancing the thermoelectric performance of SnSe1−xTex nanoplates through band engineering. J Mater Chem A, 2017, 5(21): 10713 DOI: 10.1039/C7TA02677C
[32] Paul B, V A K, Banerji P. Embedded Ag-rich nanodots in PbTe: Enhancement of thermoelectric properties through energy filtering of the carriers. J Appl Phys, 2010, 108(6): 064322 DOI: 10.1063/1.3488621
[33] Zhang C, De La Mata M, Li Z, et al. Enhanced thermoelectric performance of solution-derived bismuth telluride based nanocomposites via liquid-phase Sintering. Nano Energy, 2016, 30: 630 DOI: 10.1016/j.nanoen.2016.10.056
[34] Zhang Q, Ai X, Wang L, et al. Improved thermoelectric performance of silver nanoparticles-dispersed Bi2Te3 composites deriving from hierarchical two-phased heterostructure. Adv Funct Mater, 2015, 25(6): 966 DOI: 10.1002/adfm.201402663
-
期刊类型引用(1)
1. 郭春芳. 纳米NiO/ZrO_2复合光催化剂的制备及性能. 印染助剂. 2022(03): 31-34 . 
百度学术
其他类型引用(1)
计量
- 文章访问数: 398
- HTML全文浏览量: 199
- PDF下载量: 186
- 被引次数: 2