摘要: 基于增材制造的技术特点, 设计完成了适用于3D打印的阴极热子组件模型, 并通过选择性激光熔融技术一体化3D打印完成了直径为3 mm和5 mm的样品, 并对样品展开了相应的后处理工艺研究, 包括去除支撑结构、热子绝缘防护和浸渍发射盐等。结果表明, 新型组件的热子能够将阴极加热至900~1100℃的工作温度范围; 在水冷阳极二极管中测试, 1100℃下阴极拐点发射电流密度达到7.94 A·cm-2。Abstract: The cathode-heater assembly model for 3D printing was designed based on the technical characteristics of additive manufacturing. The samples in the diameters of 3 mm and 5 mm were 3D-printed by selective laser melting; meanwhile, the corresponding post-treatments for the samples were carried out, including the removal of support structure, the insulation protection of heater, and the impregnation of active material. The results show that, the cathode can be heated to the work temperature in range of 900~1100 ℃ by the new heater assembly, and the emission current density at the cathode inflexion can achieved as 7.94 A·cm-2 at 1100 ℃ in water-cooled diode test.
-
硬质合金是以难熔金属碳化物（WC、TiC、TaC等）为硬质相，以过渡金属元素（Co、Ni、Fe等）为粘结相，采用粉末冶金方法制备的复合材料[1‒2]。硬质合金具有高强度、高硬度、高弹性模量、高耐磨损、高耐腐蚀、低热膨胀系数以及高化学稳定性等优点，被广泛地应用于拉丝模具、机械加工、耐磨耐腐蚀零件以及结构部件等领域，被誉为“工业的牙齿”[3‒6]。
自1923年发展至今，硬质合金的材料体系、WC晶粒尺寸、微观结构类型不断得到丰富与发展[7‒9]。均匀结构硬质合金是指内部微观结构均匀一致，具有相同成分、组织及性能的硬质合金[10]。根据WC晶粒大小，均匀结构硬质合金可分为纳米及超细晶硬质合金、超粗晶硬质合金和双晶硬质合金等[11‒18]。均匀结构硬质合金由陶瓷硬质相和金属粘结相组成，陶瓷硬质相的比例提高有助于硬度和耐磨性的改善，但会造成韧性的降低；反之，当金属粘结相的比例提高时，会出现相反的力学性能变化规律。均匀结构硬质合金存在无法同时提高耐磨性和断裂韧性的局限性。表面改性在硬质合金表层空间尺度上实现微观组织的变化，进而对表面力学性能进行优化调控，最终提高硬质合金工具的使用寿命，满足工业应用不断发展的现状。目前主要通过化学表面改性和物理表面改性获得具有实际工程应用价值的非均匀结构硬质合金。近年来，通过渗碳、脱碳、渗氮或脱氮处理等化学表面改性制备梯度硬质合金或通过物理气相沉积和化学气相沉积等物理表面改性制备涂层硬质合金已成为非均匀结构硬质合金的研究热点。基于物理气相沉积或化学气相沉积涂层方法的多层复合涂层硬质合金已实现大规模商业化应用。
本文针对目前传统均匀结构硬质合金耐磨性和断裂韧性难以同时提升的问题提出改进措施，介绍了不同表面改性处理得到非均匀结构硬质合金的制备机理与研究现状，并对今后的研究方向提出了展望。
1. 化学表面改性
随着硬质合金制备技术的发展，非均匀结构硬质合金的制备方法不断丰富，其中表面改性是制备非均匀结构硬质合金的主要方法。化学表面改性是通过原子扩散、液体流动、化学反应等方法实现硬质合金表面物相及微观组织的改变，进而完成合金表面力学性能的定向改善[19‒20]。目前通过化学表面改性制备的常见梯度硬质合金如表1所示。
表 1 基于化学表面改性的常见梯度硬质合金Table 1. Graded cemented carbides based on the chemical surface modification化学表面
改性方法材料体系特点 梯度结构特征 渗碳处理 缺碳 表层贫Co，芯部含η相 正常碳的质量分数 表层贫Co，芯部不含η相 脱碳处理 碳的质量分数偏高 表层富Co 渗氮处理 含Ti、Ta、Nb等元素 表层富含立方相 脱氮处理 含N元素 表层富Co，无立方相 渗碳或脱碳处理实现梯度结构是基于碳的扩散及碳的质量分数对硬质合金微观组织的影响。如WC–Co合金中只出现WC与Co两相，正常碳的质量分数应分布在富碳上限和缺碳下限之间[21]，其中富碳上限为（6.13+0.058×Co质量分数）%，缺碳下限为（6.13‒0.079×Co质量分数）%。当合金中的碳质量分数高于富碳上限时，就会出现游离C，也就是石墨相；当合金中的碳质量分数低于缺碳下限时，就会出现η相[21‒22]。渗氮或脱氮是基于氮的扩散和氮、钛及碳之间的化学反应。氮的扩散实现硬质合金表面物相和微观组织的变化，进而促进梯度结构的形成[19,23]。
1.1 渗碳处理——表层贫Co且芯部含η相梯度结构
表层贫Co且芯部含η相梯度结构的形成机理分析如下[24–27]：通过预烧结制备含η相硬质合金，然后进行渗碳液相烧结，渗入合金表面的C原子与表面η相发生反应，生成WC与Co。随着C原子由表及里的迁移，C原子由外向内与η相反应，这种反应导致η相降低甚至消失，Co相增加。C原子浓度在液相Co中呈现出外高内低的梯度，C原子浓度梯度驱动分解出来的W原子往外表层迁移，并且会与液相Co中的C原子反应生成WC。由W原子往外迁移而引起的体积缺陷也会驱动外表层中的液相Co由表及里迁移，因而导致过渡层的Co含量（质量分数）偏高，进而引起过渡层WC晶粒粗化。
表层贫Co且芯部含η相梯度结构示意图如图1所示[27]，可分为贫Co表层、富Co过渡层和含η相芯部。该梯度硬质合金的Co含量（质量分数）与维氏硬度分布如图2所示[27]。由图可知，表层Co质量分数低于名义Co质量分数，因而表层硬度高；过渡层的Co质量分数高于名义Co质量分数，因而硬度低，韧性高；芯部含有η相，其Co质量分数是合金的名义Co质量分数。
![]()
![]()
1.2 渗碳处理——表层贫Co且芯部不含η相梯度结构
图3所示为WC–10Co硬质合金的W–Co–C相图[28]。关于表层贫Co且芯部不含η相梯度结构形成机理分析如下[28‒29]：当温度在1275～1325 ℃区间时，WC、固相Co和液相Co三相共存，在此温度范围内，当C质量分数在5.34%～5.65%范围内增加时，固相Co含量（质量分数）明显减少，而液相Co含量显著增加。因此，当低C含量且不含η相硬质合金在此温度下进行渗碳处理时，C原子逐渐渗入合金的表层，较高的C含量使合金表层首先出现液相Co，进而液相Co从合金表层向合金内部渗入，当保温一定时间，再冷却降温后，所有Co都会以固相Co的形式存在，最终出现表层贫Co的梯度硬质合金。该梯度结构特征如图4所示[28]，由贫Co的表层和无η相的芯部组成。
![]()
1.3 脱碳处理——富Co表层梯度硬质合金
富Co表层梯度结构形成机理分析[30‒32]如下：从图3可以看出，液相Co含量（质量分数）会随着温度和C含量（质量分数）的变化而改变。脱碳处理即在低碳势的气氛下进行烧结，在1300 ℃以下进行脱碳，硬质合金表层的C含量将会率先降低，表层的Co优先从液相到固相发生转变，当液相Co开始凝固时，表层中溶解在液相Co中的C和W溶解度会下降，进而表层中的C和W向合金的内部迁移，最终形成表层富Co层，类似于一层Co覆盖在硬质合金的表层。脱碳处理得到的富Co表层梯度硬质合金如图5所示[28]。通过脱碳处理制备表层覆盖Co层的梯度硬质合金，对原始合金的C含量（质量分数）要求偏高，否则将会造成合金内部缺C。
![]()
1.4 渗氮处理——表层富含立方相梯度结构
表层富含立方相梯度结构形成机理如图6所示[19,33‒34]：渗氮促使烧结气氛中的N原子扩散到合金表面，N原子与合金表面的C、Ti原子反应生成Ti(C,N)。该反应促使合金内部区域的Ti原子从里往外迁移。合金次表层的Ti原子向外迁移留下空位，此空位需要其他原子予以填充。金属Co原子在硬质合金材料体系中的扩散系数高，尤其是液相烧结，部分Co相为液相，流动性最好，所以Co原子会定向迁移填充由Ti原子迁移所造成的原子空位。此时，合金的次表层Co含量增加，次表层Co的富集促进次表层WC晶粒通过溶解–析出机制长大粗化，所以次表层富Co且WC晶粒粗大。最终形成表层富立方相、次表层富Co且WC晶粒粗大的梯度结构硬质合金。
![]()
1.5 脱氮处理——表层富Co且无立方相梯度结构
表层富Co且无立方相梯度结构形成机理如图7所示[35‒36]：在无氮或贫氮的烧结气氛下，含氮硬质合金在液相烧结过程中合金表面的氮化物发生分解，即合金表面N原子向烧结气氛中扩散，进而造成合金表层的N原子含量降低。此时，合金内部N原子的浓度大于合金表面N原子的浓度，合金内部的N原子向合金表面扩散。由于N与Ti原子之间存在强烈的亲和力，当合金内部的N原子通过粘结相向合金表面扩散时，合金表面的Ti原子也会通过粘结相向内部扩散，同时液相Co会从合金内部流向表层去填补由TiN分解出现的空位，进而导致合金表层的Co含量增加。直至合金表层TiN几乎全部发生分解，进而形成表层富Co且无立方相梯度结构硬质合金。
![]()
目前，部分基于化学表面改性方法的结构功能一体化梯度硬质合金材料已实现商业化且制备机理已基本清晰。但在化学表面改性实现梯度结构过程中，关于化学扩散与热扩散原理还缺乏深入研究，需要深入分析原子的迁移驱动力、动力学方程，建立原子在化学势和温度梯度作用下的迁移模型。
2. 物理表面改性
物理表面改性是通过涂覆的方法在硬质合金表面制备单层或者多层复合涂层，从而赋予硬质合金特定的表面性能[37]。目前，涂层硬质合金主要通过物理气相沉积和化学气相沉积方法在材料表面涂覆高耐磨的难熔金属或非金属化合物[38]。
2.1 涂层方法分析
国内外研究人员对物理气相沉积和化学气相沉积涂层方法进行了广泛且深入的研究，结果表明两种方法分别具有不同优势[38‒41]。对于物理气相沉积，沉积温度低，涂层的沉积温度约200～500 ℃，一般对基体影响不大；对于化学气相沉积，由于沉积温度较高（850～1050 ℃），基体通常参与了薄膜成膜初期的化学反应。物理气相沉积涂层表面光滑，内部产生压应力，有助于抗裂纹扩展。对于化学气相沉积，涂层反应源的制备相对比较容易，涂层与基体结合强度高，涂层附着力强、均匀性好，适合用来给复杂形貌工件镀层。化学气相沉积涂层工业化成本低于物理气相沉积涂层。
2.2 涂层结构设计
由于单一涂层难以满足当前机加工对涂层硬质合金刀具的力学性能要求，涂层成分趋于多元化，涂层结构趋于复合化，涂层微观组织趋于纳米化[38,42]。从目前应用需求分析，机加工对涂层结构的功能性要求越来越高[42]，复合功能涂层结构已取得广泛应用。
瑞典、美国等国家的著名刀具公司都开发有多层结构的涂层硬质合金刀具。如瑞典Sandvik Coromant公司的GC2015牌号刀具具有TiCN–TiN/Al2O3–TiN的三层结构复合涂层，TiCN底层与基体的结合强度高，TiN/Al2O3中间层既耐磨又能抑制裂纹的扩展，TiN表层具有较好的化学稳定性且易于观察刀具的磨损[43]。美国Kennametal Hertel公司的KC9315型刀片上共有三层涂层，底层是Al2O3，中间层是TiCN，表面层是TiN。这种多层复合涂层的性能较单层的TiC、TiN涂层及TiC/TiN双层涂层具有明显性能优势。多层复合涂层的功能分析如图8所示[42]。
物理表面改性方法解决了硬质合金刀具硬度与强度之间的矛盾，已经在数控车床刀具领域取得广泛应用。涂层的性能取决于材料的微观组织结构与化学成分，除了研究涂层材料、涂层制备技术、涂层工艺之外，还需要重点研究涂层材料与硬质合金材料之间化学成分和热膨胀系数的匹配关系。
3. 总结与展望
硬质合金的主要研究方向已经从均匀结构向非均匀结构转变。对于化学表面改性梯度硬质合金，在研究当前梯度硬质合金微观结构及形成机理的基础上，需要完善其热力学、动力学数据，从微观机制上完整解释梯度结构的形成过程，实现准确调控梯度结构形成的重要参数，为功能梯度硬质合金的制备提供更充分的基础理论指导。对于物理表面改性涂层硬质合金，当前研究主要是在均匀结构硬质合金基体上进行涂层结构复合化设计，对硬质合金基体的梯度结构设计在改善涂层与基体结合强度方面具有潜在技术优势，因此，需要对硬质合金基体的非均匀结构设计开展深入研究。
-
![]()
图 2 热子引腿结构：（a）简单圆柱；（b）和（c）异形台阶
Figure 2. Potential pin structures of the heaters: (a)column; (b)and(c)specific steps
![]()
图 5 3D打印的阴极热子组件样品宏观形貌
Figure 5. Macromorphology of the 3D-printed cathode-heater assembly sample
![]()
图 6 3D打印的阴极热子组件样品光学形貌
Figure 6. Optical morphology of the 3D-printed cathode-heater assembly sample
![]()
图 7 去除支撑结构的阴极热子组件样品
Figure 7. Cathode-heater assembly samples after removing the supporting columns
![]()
图 9 阴极热子组件样品绝缘防护处理
Figure 9. Cathode-heater assembly samples after the insulation protection treatment
![]()
图 12 不同制备工艺得到的阴极表面微观组织：（a）选择性激光熔化工艺；（b）常规粉末冶金工艺
Figure 12. Microstructures of the cathode surfaces: (a)SLM; (b)the conventional powder metallurgy process
![]()
图 13 测试用水冷阳极二极管外观形貌
Figure 13. Appearance of the water-cooled diode used in the cathode emission performance testing
![]()
图 14 阴极热子组件的阴极发射伏安特性
Figure 14. Voltage current characteristics of the cathode emission for the cathode-heater assembly
表 1 加热功率及阴极热子温度
Table 1 Heating powers and the corresponding temperatures of cathode and heater
热子电/V 热子加热功率/W 热子温度/℃ 阴极发射表面温度/℃ 阴极热子温差/℃ 6 12.30 983 830 153 7 16.03 1050 883 167 8 19.28 1129 941 188 9 22.95 1176 987 189 10 26.90 1233 1035 198 11 30.25 1272 1071 201 
下载: 导出CSV
表 2 新型阴极热子组件的阴极表面能谱分析
Table 2 Energy spectrum analysis of the new type cathode-heater assembly surface
元素 质量分数/% 原子数分数/% O 13.90 59.73 Al 3.36 8.55 Ba 6.19 3.10 W 76.55 28.62
下载: 导出CSV
-
[1] 方荣, 陆玉新. 热阴极的发展现状. 真空电子技术, 2015(1): 12 https://www.cnki.com.cn/Article/CJFDTOTAL-ZKDJ201501004.htm Fang R, Lu Y X. The development of the thermionic cathodes. Vac Electron, 2015(1): 12 https://www.cnki.com.cn/Article/CJFDTOTAL-ZKDJ201501004.htm
[2] 李娜, 邵文生, 高玉娟, 等. 大电流密度钪酸盐阴极的发射性能研究. 真空电子技术, 2015(2): 38 https://www.cnki.com.cn/Article/CJFDTOTAL-ZKDJ201502009.htm Li N, Shao W S, Gao Y J, et al. Studies on emission performance of high current density scandate cathode. Vac Electron, 2015(2): 38 https://www.cnki.com.cn/Article/CJFDTOTAL-ZKDJ201502009.htm
[3] 樊昱, 李芬霞, 郭峰, 等. 3D打印技术发展现状. 世界有色金属, 2017(22): 221 https://www.cnki.com.cn/Article/CJFDTOTAL-COLO201722130.htm Fan Y, Li F X, Guo F, et al. Development status of 3D printing technology. World Nonferrous Met, 2017(22): 221 https://www.cnki.com.cn/Article/CJFDTOTAL-COLO201722130.htm
[4] 柳朝阳, 赵备备, 李兰杰, 等. 金属材料3D打印技术研究进展. 粉末冶金工业, 2020, 30(2): 83 https://www.cnki.com.cn/Article/CJFDTOTAL-FMYG202002025.htm Liu C Y, Zhao B B, Li L J, et al. Research progress of 3D printing technology for metallic materials. Powder Metall Ind, 2020, 30(2): 83 https://www.cnki.com.cn/Article/CJFDTOTAL-FMYG202002025.htm
[5] 杨佳, 郭洪钢, 谭建波. 选择性激光熔化技术研究现状和发展趋势. 河北工业科技, 2017, 34(4): 300 https://www.cnki.com.cn/Article/CJFDTOTAL-HBGY201704012.htm Yang J, Guo H G, Tan J B. Status and development trend of selective laser melting forming technology. Hebei J Ind Sci Technol, 2017, 34(4): 300 https://www.cnki.com.cn/Article/CJFDTOTAL-HBGY201704012.htm
[6] 王会杰, 崔照雯, 孙峰, 等. 激光选区熔化成形技术制备高温合金GH4169复杂构件. 粉末冶金技术, 2016, 34(5): 368 DOI: 10.3969/j.issn.1001-3784.2016.05.009 Wang H J, Cui Z W, Sun F, et al. Superalloy GH4169 complicated components prepared by selective laser melting forming technique. Powder Metall Technol, 2016, 34(5): 368 DOI: 10.3969/j.issn.1001-3784.2016.05.009
[7] Mullen L, Stamp R C, Fox P, et al. Selective laser melting: A unit cell approach for the manufacture of porous, titanium, bone in-growth constructs, suitable for orthopedic applications. J Biomedi Mater Res B, 2010, 92(1): 178
[8] Shen Y, McKown S, Tsopanos S, et al. The mechanical properties of sandwich structures based on metal lattice architectures. J Sandwich Struct Mater, 2010, 12(2): 159 DOI: 10.1177/1099636209104536
[9] 杨广宇, 汤慧萍, 刘楠, 等. 增材制造技术制备钨材料研究进展. 热加工工艺, 2016, 45(24): 16 https://www.cnki.com.cn/Article/CJFDTOTAL-SJGY201624004.htm Yang G Y, Tang H P, Liu N, et al. Research progress in tungsten material fabricated by additive manufacturing. Hot Working Technol, 2016, 45(24): 16 https://www.cnki.com.cn/Article/CJFDTOTAL-SJGY201624004.htm
[10] 谢琰军, 杨怀超, 王学兵, 等. 选择性激光熔化制备纯钨块体材料的研究. 粉末冶金技术, 2018, 36(2): 89 DOI: 10.19591/j.cnki.cn11-1974/tf.2018.02.002 Xie Y J, Yang H C, Wang X B, et al. Study on the tungsten bulk materials prepared by selective laser melting. Powder Metall Technol, 2018, 36(2): 89 DOI: 10.19591/j.cnki.cn11-1974/tf.2018.02.002
[11] 刘彩利, 赵永庆, 田广民, 等. 难熔金属材料先进制备技术. 中国材料进展, 2015, 34(2): 163 https://www.cnki.com.cn/Article/CJFDTOTAL-XJKB201502009.htm Liu C L, Zhao Y Q, Tian G M, et al. Advanced manufacturing technology for refractory metals. Mater China, 2015, 34(2): 163 https://www.cnki.com.cn/Article/CJFDTOTAL-XJKB201502009.htm
[12] 倪晓晴, 孔德成, 温莹, 等. 3D打印金属材料中孔隙率的影响因素和改善方法. 粉末冶金技术, 2019, 37(3): 163 DOI: 10.19591/j.cnki.cn11-1974/tf.2019.03.001 Ni X Q, Kong D C, Wen Y, et al. Influence factors and improvement methods on the porosity of 3D printing metal materials. Powder Metall Technol, 2019, 37(3): 163 DOI: 10.19591/j.cnki.cn11-1974/tf.2019.03.001
[13] 高航, 李世宠, 付有志, 等. 金属增材制造格栅零件磨粒流抛光. 航空学报, 2017, 38(10): 226 https://www.cnki.com.cn/Article/CJFDTOTAL-HKXB201710022.htm Gao H, Li S C, Fu Y Z, et al. Abrasive flow machining of additively manufactured metal grilling parts. Acta Aeronaut et Astronaut Sin, 2017, 38(10): 226 https://www.cnki.com.cn/Article/CJFDTOTAL-HKXB201710022.htm
[14] 周鑫, 刘伟. 纯钨单层铺粉激光选区熔化/凝固行为. 中国激光, 2016, 43(5): 71 https://www.cnki.com.cn/Article/CJFDTOTAL-JJZZ201605011.htm Zhou X, Liu W. Melting and solidifying behavior in single layer selective laser of pure tungsten powder. Chin J Lasers, 2016, 43(5): 71 https://www.cnki.com.cn/Article/CJFDTOTAL-JJZZ201605011.htm
[15] 朱学超, 魏青松, 孙春华. 激光选区熔化成形S136模具钢热处理组织和性能研究. 粉末冶金技术, 2019, 37(2): 83 DOI: 10.19591/j.cnki.cn11-1974/tf.2019.02.001 Zhu X C, Wei Q S, Sun C H. Study on microstructures and properties of S136 die steel formed by selective laser melting after heat treatment. Powder Metall Technol, 2019, 37(2): 83 DOI: 10.19591/j.cnki.cn11-1974/tf.2019.02.001
[16] Song B, Zhao X, Li S, et al. Differences in microstructure and properties between selective laser melting and traditional manufacturing for fabrication of metal parts: A review. Front Mech Eng, 2015, 10(2): 111
-
期刊类型引用(2)
1. 唐彦渊，羊求民，徐国钻，王红云，钟志强. 微量Y_2O_3对WC-6Co非均匀结构硬质合金微观结构及性能的影响. 粉末冶金技术. 2024(02): 184-191 . 
本站查看
2. 周晓刚，纪飞飞. 激光喷丸作用下TC4双相钛合金HCP结构位错组态及性能研究. 应用激光. 2022(10): 99-105 . 百度学术
其他类型引用(0)
计量
- 文章访问数: 174
- HTML全文浏览量: 55
- PDF下载量: 19
- 被引次数: 2