Preparation and research process of high thermal conductivity metal matrix composites
-
摘要: 随着电子器件芯片功率的不断提高，对散热材料的热物理性能提出了更高的要求。将高导热、低膨胀的增强相和高导热的金属进行复合得到的金属基复合材料，能够兼顾高的热导率和可调控的热膨胀系数，是理想的散热材料。本文对以Si、SiCp、金刚石、鳞片石墨为增强相的铜基及铝基复合材料的研究进展进行了总结，并就金属基复合材料目前存在的问题及未来的研究方向进行了展望。Abstract: With the increasing power of the electronic device chip, the higher requirements are put forward for the thermophysical properties of the heat dissipation materials. The metal matrix composites as the ideal heat dissipation material, which are composed of the high thermal conductivity and low thermal expansion reinforcement phase and the high thermal conductivity metal, show the high thermal conductivity and the adjustable coefficient of thermal expansion. The research progress of the copper matrix and aluminum matrix composites reinforced by Si, SiCp, diamond, and flake graphite in recent years was summarized in this paper, and the existing problems and future research direction of the metal matrix composites were prospected.
-
闭孔金属基复合泡沫材料(metal matrix syntactic foams，MMSFs)与泡沫金属相似，是一种具有与传统材料不同结构的新型材料。它是由金属基体和空心微球复合而成的一种含有大量闭孔孔隙的金属泡沫材料，具有比重小、吸音隔音效果好、能量吸收性好[1]等优点，并且具备良好的传热、电磁阻尼、摩擦磨损[2]及压缩[3]等特性。特别是在承受冲击载荷时，空心微球的破碎能够有效地吸收冲击能量，从而对基体起到保护效果。本文重点介绍了闭孔金属基复合泡沫材料的填充材料和制备工艺，并根据其结构与性能概述了其应用。
1. 填充材料—空心微球
在闭孔金属基复合泡沫材料的制备过程中，填充材料的选择非常重要，其性能与质量直接决定闭孔金属基复合泡沫材料的性能。如果所选择的空心微球表面有大量孔洞或破损，在制备过程中基体容易进入空心微球内腔，会使封闭内腔空间减小或消失，影响金属基复合泡沫材料的性能。而且，空心微球的种类不同，也会影响空心微球的比重、抗压强度等性能，从而影响最终复合泡沫材料的性能。目前，可应用于制备闭孔金属基复合泡沫材料的空心微球种类比较多，下面主要针对常用的几种空心微球进行介绍。
1.1 陶瓷空心微球
陶瓷空心微球根据成分划分主要包括飞灰、Al2O3空心微球及SiC空心微球(SiCHP)。
飞灰，又称为粉煤灰、漂珠，是工业生产的副产物，由工业中煤粉燃烧所形成的一种陶瓷空心微球。飞灰的主要组成相为非晶态SiO2和Al2O3，其显微形貌如图 1所示；其粒径一般为0.5~800 μm，密度为0.4~0.7 g·cm-3，杨氏模量约为13~17 GPa[4]。由于飞灰的结构、形状和力学性能波动较大，多年来主要用于制造耐火砖、铸造保温冒口以及保温隔热材料等普通产品，附加值较低。如果将飞灰添加到铝合金、镁合金或铝镁合金中用来制备金属基复合泡沫材料，不仅可以有效改善铝镁合金泡沫材料的综合性能，而且可以高效利用此工业副产品，实现高价值转换化[5–8]。
对于Al2O3空心微球，由于其制备成本较高，因此也常用质量分数约40%的Al2O3和质量分数约60%的SiO2混合空心微球代替纯Al2O3空心微球，其性能与纯Al2O3空心微球相当[9]。Santa等[10]利用Al2O3空心微球通过低压铸造技术合成复合泡沫材料。其准静态压缩结果表明，复合泡沫材料在压缩破坏时，初始阶段发生了明显的变形，随后发生空心球的破坏，并与基体一起被压缩致密化。复合泡沫材料的峰值强度、平台强度和韧性随着空心微球壁厚度(t)与直径(D)比值(t/D)的增加而增加。研究发现，t/D随空心微球直径的减小而增加，所以用小粒径微球生产的复合泡沫材料表现出较好的性能。
与飞灰、Al2O3空心微球相比，SiCHP具有更高的硬度、更高的热导率及更低的膨胀率等优点，现在已成为复合泡沫材料重要的填充材料[11–12]。SiCHP除了具有传统SiC的性能以外，还具有壳结构的经典物理性质，包括电气绝缘、光学效益、极端硬度、耐化学腐蚀等[13–14]。因此，SiCHP应用于闭孔金属基复合泡沫材料的制备，不仅可以保持其本身固有特性，拥有壳结构的物理特点，还将极大降低闭孔金属基复合泡沫材料的密度，提高复合材料的比强度与比刚度。SiCHP的密度(ρHS)可根据式(1)[13]进行计算。
$${\rho _{{\rm{HS}}}} = {\rho _{{\rm{SiC}}}}\left( {1 - {\eta ^3}} \right)$$ (1) 式中：η=Ri/R0，Ri为空心微球内径，R0为空心微球外径，ρSiC为实心SiC密度。由式(1)可得，SiCHP的密度取决于微球壳内外径比。由于实际的SiCHP微球壁不可避免地会存在不同程度的孔洞[14]，所以SiCHP的实际密度值一般都比理论值低；而且相比于实体颗粒，SiCHP的薄壁结构也导致其剪切强度明显降低。研究也表明，与飞灰相比，采用SiCHP制备的复合泡沫材料具有更高的强度，如Luong等[15]发现，SiCHP/Al复合泡沫材料的抗压强度远高于飞灰/Al复合泡沫材料。
1.2 玻璃微珠
玻璃微珠为浅白色粉末，具有薄壁空心结构，实际密度为0.125~0.60 g·cm-3，软化温度约600 ℃，导热率为0.05~0.20 W·m-1·℃-1。Lin等[16]研究了玻璃微珠与纯Al及Al–Mg合金制备的复合泡沫材料，结果表明玻璃微珠/纯Al在压缩过程中表现出不连续的剪切带和鼓形，而玻璃微珠/Al–Mg合金则显示出连续的剪切带，并被主剪切区分开。在拉伸状态下，纯Al基复合泡沫中的玻璃微珠容易从基体上剥离，而Al–Mg基复合泡沫中的玻璃微珠粘结良好，并出现层状撕裂。导致这种变形行为差异的原因是Al–Mg基体本身具有的延展性，以及玻璃微珠与Al–Mg基体发生界面反应生成的MgAl2O4层促进了其界面结合。
1.3 浮石(LECAP)
浮石是一种低成本的天然多孔火山石粉末，表面坚固且封闭，但内部存在许多大小不一的孔隙。单个颗粒内部孔的尺寸处于微米至毫米范围，其孔的大小对浮石颗粒的力学性能影响较大[17]。采用浮石填充的闭孔金属基复合泡沫材料可大量用于高吸能领域，例如建筑物的保护。
2. 闭孔金属基复合泡沫材料的制备方法
闭孔金属基复合泡沫材料的制备方法与一般金属基复合材料类似，根据制备中基体的状态大致可以分为液态法和固态法两大类。
2.1 液态法
液态法制备闭孔金属基复合泡沫材料的常用方法主要包括：低压铸造法、压力浸渗法、搅拌铸造法和重力铸造法等。
2.1.1 低压铸造法
低压铸造法是把混合有空心微球的液体金属在压力作用下由下而上充满型腔后形成铸件的一种方法。陈健美等[18]采用低压铸造法制备不同粒径的陶瓷空心微球/铝基泡沫材料，具体步骤如下：将陶瓷空心微球填充到模具中，预热到指定温度440~450 ℃，与此同时将铝加热(730~750 ℃)至熔融状态，低真空(0.03~0.05 MPa)吸入型模中，合金凝固后取样得到闭孔金属基复合泡沫材料。研究发现，陶瓷空心微球在铝基体中分布较为均匀，陶瓷微球与基体之间未出现裂纹和缝隙，且未出现明显的元素扩散现象；所制备的小粒径空心陶瓷微球铝基复合泡沫材料的压缩应力高于大粒径的复合泡沫材料。Malik等人[6]将空心微球紧密放置在圆筒模具中，预热至773 ℃，然后将液态金属倒入浇口，同时在底部施加负压，使液态金属充满陶瓷空心微球之间的间隙，制备出闭孔金属基复合泡沫材料。结果表明，低压铸造法可有效用于制备孔隙均匀分布的复合泡沫材料，但是由于液态金属温度较高，空心微珠与液态金属容易发生界面反应生成Mg2Si和MgO。Zhang等人[19]采用直径为0.25~4 mm的陶瓷空心微球通过低压铸造法制备出铝基复合泡沫材料，其密度为1.38~1.88 g·cm-3，孔隙率范围为0.31~0.51结果发现，在静态压缩和冲击试验中，复合泡沫材料中铝基体的体积分数起主导作用，决定了材料的抗压强度。
低压铸造法制备闭孔金属基复合泡沫材料工艺简单，但是由于空心微球密度较低，在液态金属中容易漂浮，导致在基体中分布不均，且制备过程温度较高，容易发生界面反应，玻璃微球容易发生软化。此外，空心微珠体积分数不好控制，使用设备具有较大局限性，不适合大范围普及。
2.1.2 压力浸渗法
压力浸渗法是采用高压使液态熔融金属以较高速度压入空心微球的间隙，从而制备闭孔金属基复合泡沫材料的一种方法。在制备过程中，压力和时间是主要工艺参数。在压力浸渗过程中，如果施加的压力超过空心微球的强度，薄壁空心微球易破碎并被基体合金填充。Lin等[16]用玻璃微珠填充纯Al和Al–Mg合金，以压力浸渗法制备Al基复合泡沫材料，并研究Al基复合泡沫材料的力学性能与失效机制。首先，将玻璃空心微球垂直放入压力为0.5 MPa的钢模中，然后在600 ℃下预热；再使用加压设备将熔融铝渗入预成型坯中，并在0.8 MPa下保持5 min，直到完全固化。Orbulov[20]用陶瓷空心微球以压力浸渗法制备金属基复合泡沫材料并研究浸渗温度、时间对浸渗长度的影响。结果表明，较高压力(750 kPa)和较短时间(1 s)下制备的给定渗透长度的金属基复合泡沫材料具有更好的力学性能。
压力浸渗方法虽然可以解决空心微球的漂浮问题，但是容易导致空心微球破损，且制备过程温度较高，容易导致空心微球与基体发生界面反应。此外，对设备密封性要求较高，因此制造成本增加。
2.1.3 搅拌铸造法
搅拌铸造法是指在气体保护下将熔融金属与空心微球在坩埚中进行机械搅拌，使空心微球全部分散至金属基体熔液中，然后铸入金属模或砂模中。此方法不需要专用的设备、高昂的成本和能源消耗。搅拌铸造法非常流行且有效地用于制造含有固体硬质颗粒的金属基复合材料(MMC)，但将其用于含有空心微球的复合材料仍存在许多困难，主要问题是在搅拌过程中，空心微球壳会被机械破坏[6, 21, 22]。脆性空心微球与搅拌臂的碰撞可能会导致其破裂，然后被熔融的基体合金填充；同时，难以精确把握搅拌时间与温度，在浇注过程中，部分未充分润湿的空心微球会发生上浮，导致材料阶梯化分层。Mondal等[23]采用搅拌铸造法制备出空心微球体积分数为30%~50%、密度为1.5~1.9 g·cm-3的铝基复合泡沫材料。具体步骤如下：先将A2014铝合金加热至熔融状态，同时将空心微珠预热，然后通过机械搅拌将预热的空心微珠在熔体中混合，并加以轻微压力(1~3 MPa)，在预热的模具中铸造得到闭孔金属基复合泡沫材料。结果发现，通过搅拌铸造制备的闭孔金属基复合泡沫材料的压缩变形行为与传统方法制备的低密度复合泡沫材料相似，但前者的平台应力值更高。而且，金属基复合泡沫材料的平台应力与空心微球的密度及其体积分数有关，可以通过以下的公式进行计算：
$${\sigma _{\rm{sf}}} = C\left\{ {{\sigma _0}{{\left( {1 - {f_{\rm{c}}}} \right)}^n} + C{\sigma _{{\rm{mu}}}}{{\left[ {\left( {1 - {f_{{\rm{vsh}}}}} \right)\left( {1 - {f_{\rm{cv}}}} \right)} \right]}^n}} \right\}$$ (2) 式中：σsf是合成的金属基复合泡沫材料的压缩强度，σ0是空心微球的抗压强度，σmu是对应实心微球的抗压强度，fc是空心微球的实验体积分数，fvsh是空心微球球壳空心的体积分数，fcv是空心微球空心部位的体积分数，C、n值为常数，随材料、测量方法而变化。
Huang等[7]通过搅拌铸造法制备出质量分数分别为4%、6%、8%、10%的飞灰/AZ91D镁基复合泡沫材料。结果表明，微球未发生聚集且均匀分布在基本中，部分微球破损并被填充了Mg合金，分析发现飞灰与AZ91D的界面产物主要为MgAl2O4。
2.1.4 重力铸造法
重力铸造是指金属溶液在自身重力作用下，注入已放入空心微球的铸型中而制备的一种工艺方法。该方法优点在于实验中无需抽真空、施加压力，工艺设备简单、成本低，更适合工业化生产。Rabiei等人[24]采用重力铸造法制备闭孔铝基复合泡沫材料，其密度达到2.4 g·cm-3，相对密度为41.5%，并显示出优异的压缩强度和吸能能力，在10%~50%的应变量下，平均压缩强度达到了67 MPa，在近50%应变量时，复合泡沫材料开始发生致密化行为，此时吸收能为30 MJ·m-3。其具体过程如下：将铁空心微球装入到模具中，振动达到致密状态，然后在700 ℃下预热装好的模具，以避免铝液在铸造过程中与模具或空心微球接触时过早凝固；同时，在熔炉中将铝加热到700 ℃使其完全熔化，然后将铝液浇注到模具中，在重力作用下填充满铁空心微球间的空隙，最终空冷后取样。对于密度较大的空心微球，可以采用重力铸造法制备闭孔金属基泡沫复合材料，如果选择低密度空心微球，浇注过程中空心微球容易悬浮，导致无法制备出孔隙均匀的泡沫材料。
综上所述，重力铸造法是目前制备金属基复合泡沫材料的主要方法。但该方法也存在着一些问题，如搅拌铸造过程中易卷入气体，很难把握搅拌的时间与温度，在浇注过程中如果不采取措施，未湿润的空心微球会上浮，导致空心微球偏聚，从而导致材料发生分层。压力浸渗法虽然能够解决空心微球偏聚问题，但如上所述，其设备封闭要求很高；且与重力铸造法类似，压力浸渗法难以浸渗到小粒径空心微球之间的间隙中；在铸造过程中，铸型中的气体很难完全排除，常以气孔形式留在铸件中，使其无法进行热处理，也不宜在高温条件下工作。
2.2 固态法
闭孔金属基复合泡沫材料固态制备法主要有粉末冶金法、热挤压法、喷射沉积法等。
2.2.1 粉末冶金法
固态法制备金属基复合泡沫材料最常用的就是粉末冶金法，其典型的工艺流程如图 3所示[25]。粉末冶金法常采用机械法来混粉制备复合粉末，空心微球的含量可任意调整并准确控制，且基体能与空心微球均匀混合；此外制备时烧结温度一般都低于基体的熔点，可以有效避免基体与空心微球发生界面反应，生成有害的脆性相从而破坏材料的综合性能。这种低温合成工艺还可以有效控制空心微球与基体的界面并限制基体晶粒的尺寸。但在粉末冶金法制备中，施加的压力容易导致空心微球发生破碎，并被基体粉末填充[26]。因此，粉末冶金制备中需要注意在压制过程中选择合适的压力。
![]()
图 3 粉末冶金法制备闭孔金属基复合泡沫材料工艺流程[31]Figure 3. Typical preparation process of the closed-cell metal matrix syntactic foams by powder metallurgy(1) 预冷压烧结法
Neville等人[27]采用粉末冶金技术将钢粉末填充到紧密堆积的钢空心微球之间制备复合泡沫材料。所制备的复合泡沫材料具有优异的抗压性和吸能性，并且具有较高的比强度。Cho等[28]采用粉末冶金法制备玻璃微珠/铁基复合泡沫材料，在其生坯预冷压过程中，随着压实应力的提高，基体发生致密化，微珠出现破裂、软化、收缩，复合泡沫材料的相对密度增加。研究还发现，引起微珠破裂的临界压实压力与微珠的体积分数成反比，因此在制备时需要控制合适的压实压力。Vogiatzis等人[21]通过粉末冶金法将陶瓷空心微球添加到纯铝中，在610~710 ℃下制备铝基复合泡沫材料。结果表明，陶瓷空心微球的二氧化硅与铝颗粒之间发生原位反应形成共晶铝硅相。Akinwekomi等[29]通过粉末冶金和微波烧结技术成功合成飞灰/铝复合泡沫材料。结果表明，复合微波烧结的烧结时间极短，可抑制不良界面反应的发生；随着飞灰体积分数的增加，复合泡沫材料的密度、峰值强度和能量吸收能力降低；样品的应力–应变曲线较长且具有相对稳定的平稳区域，说明此种复合泡沫材料在能量吸收和低密度应用领域有较好的前景。王庆平等[30]采用粉末冶金法制备了漂珠/Al–25%Mg复合泡沫材料，研究结果表明，随着漂珠含量的增加，复合泡沫材料的硬度呈现先增大而后减小的趋势。
(2) 金属粉末注射成形
金属粉末注射成形法制备时将金属粉末、空心微球、粘结剂和润滑剂均匀混合，去气、制粒之后用注射成形机注射成形，然后用化学法或热分解法去除原坯中的粘结剂，最后经烧结致密化得到闭孔金属基复合泡沫材料。Lehmhus等[[31]采用金属粉末注射成形法分别制备了质量分数5%、10%的玻璃珠/316不锈钢复合泡沫材料。原料注射过程在110~130 ℃和50~60 ℃模具温度下进行，将制成的原坯在己烷中进行化学处理，30 ℃保温约24 h，然后进行热处理并进行金属粉末的烧结，以0.1 K·min-1缓慢升温至500 ℃，并保温1 h，之后以5 K·min-1进一步升温至1000 ℃，保持3 h，再以5 K·min-1升温至1200 ℃，并保温1.5 h进行最终烧结。结果表明，空心微球在烧结过程中能够保持其完整性，力学性能明显提高，其比强度超过基体材料，且延展性保持较好。
(3) 热压烧结法
热压烧结法是将基体合金粉末与空心微球混合后的复合粉末放入模具型腔，在保护气氛或真空条件下加压加热制备复合泡沫材料。烧结时施加压力可以有效抑制基体晶粒的长大，且复合粉末在压力的作用下通过塑性流动而致密化，可节约烧结时间，这也使材料晶粒粗化的几率大幅度降低。本课题组采用热压烧结法制备了不同温度和不同体积分数条件下的空心Al2O3/AZ91D及空心玻璃/AZ91D闭孔金属基复合泡沫材料，该复合泡沫材料显微结构如图 4所示。由图 4可知，空心微球在基体中均匀分布，大多数空心微球完整，小部分被填充了基体颗粒，经测量，该复合泡沫材料密度最低可达到1.5 g·cm-3。
![]()
图 4 热压烧结法制备闭孔金属基复合泡沫材料的微观结构：(a)空心Al2O3/AZ91D；(b)空心玻璃/AZ91DFigure 4. Microstructure of the closed-cell metal matrix syntactic foams prepared by hot pressing sintering: (a) Al2O3/AZ91D, (b) hollow glass microsphere/AZ91D2.2.2 热挤压制备工艺
热挤压法是把挤压坯料放入与坯料外形相同的挤压筒中，在一定温度和压力的作用下从挤压模的另一端孔中挤出，使材料发生塑性变形，进而提高材料性能。Sudarshan[32]利用搅拌铸造和热挤压的方法，采用宽粒径范围(0.5~400 μm)和窄粒径范围(53~106 μm)的漂珠制备了漂珠/A356复合材料，并研究其力学性能。结果表明，与基体材料相比，复合材料的硬度、弹性模量和屈服强度等性能得到提高，窄粒径范围的漂珠/A356复合泡沫材料的力学性能优于宽粒径范围的复合材泡沫料。
2.2.3 喷射沉积法
Manakari等[33]通过喷射沉积法合成空心玻璃/镁复合泡沫材料，并研究了干磨条件(外加载荷30 N)下的摩擦磨损行为。结果显示，与基体合金相比，空心微球的存在为累积磨料提供了空间，使复合泡沫材料的摩擦磨损性能明显改善，且空心微球的添加含量会影响材料的磨损机制。
综上所述，固态法制备可控制基体金属或合金与空心微球之间的界面反应，同时可通过控制基体与空心微球的比例获得不同孔隙量的金属基复合泡沫材料，并且容易实现空心微球在基体中的均匀分布。
3. 闭孔金属基复合泡沫材料的结构与性能
闭孔金属基复合泡沫材料的优异性能使其在轻质、吸能、声控、热控等应用领域具有重大潜力，因此在舰船航母、航天航空、土木工程等领域具有广泛的应用前景。
(1) 轻质
金属基复合泡沫材料的轻质特性，可应用于提高工程结构件的比刚度，如给定重量、宽度和长度的泡沫板弯曲刚度与其厚度成正比，与其密度成反比。
(2) 吸能性
基于闭孔金属基复合泡沫材料的高孔隙率，其在变形时可以吸收大量的机械能。图 5所示为Al2O3/AZ91D闭孔金属基复合泡沫材料在动态冲击下的真应力应变曲线，其中曲线与X轴间的积分面积可表示吸收能。闭孔金属基复合泡沫材料由于高能量吸收能力和大压缩应变，可以充当冲击能吸收器，从而在碰撞时限制加速度，可在车辆和装甲中得到广泛应用。分离式霍普金森压力杆可用于金属基复合泡沫材料高应变率的压缩测试。Zhang等[27]研究了玻璃空心微珠/5A03的准静态和动态压缩性能。结果表明，在准静态压缩下，玻璃空心微珠/5A03的抗压强度为110.5 MPa，平台应力为90.6 MPa，吸能能力为51.2 MJ·m-3；而在动态载荷下，玻璃空心微珠/5A03的抗压强度为159.0 MPa，平台应力为125.4 MPa，吸能能力为63.4 MJ·m-3，说明金属基复合泡沫材料具有较好的能量吸收能力。
![]()
图 5 Al2O3/AZ91D闭孔金属基复合泡沫材料动态冲击下的真应力应变曲线Figure 5. The true stress-strain curve of the Al2O3/AZ91D closed-cell MMSFs in dynamic impact(3) 声控与热控
闭孔金属基复合泡沫材料能够在某些情况下阻碍振动、吸收声波。与高分子泡沫相比，金属基复合泡沫材料热导率低，吸声吸热性能并不是非常出色，但该泡沫的内部构造与金属基复合材料的其他功能结合使用却很有优势。例如，金属基复合泡沫材料的多孔泡沫结构可以减少噪音，并在发生碰撞时吸收能量[34]。
(4) 摩擦磨损性能
与基体合金相比，空心微球的嵌入为累积磨料提供了空间，使金属基复合泡沫材料的摩擦磨损性能明显改善。空心微球的添加量可影响材料的磨损机制，当空心微球的添加量较低时，金属基复合泡沫材料的磨损机理主要是磨粒磨损和黏着磨损；当空心微球的添加量较高时，以剥层磨损和磨粒磨损为主[30]。
4. 结论与展望
闭孔金属基复合泡沫材料具有密度低、比刚度高、比强度高、吸能性好、损伤容限高、可抑制机械振动和衰减波的传播等特点，在工业应用中有很大的潜力与优势。本文介绍了闭孔金属基复合泡沫材料的填充材料以及制备方法，并总结了其制备中存在的部分问题。
作为填充材料的空心微球，虽然种类较多，但是微球存在粒度不均、壳壁存在缺陷、壁厚不均等局限性，因此需要开发高质量、均匀粒径的空心微球，以满足高性能金属基复合泡沫材料的制备需求。现有制备工艺尚不成熟，迫切需要开发新型制备工艺及后续相应的热处理工艺，以确保降低其密度的同时，解决其强度低的问题。
-
![]()
![]()
![]()
![]()
![]()
![]()
材料 密度 / (g·cm−3) 热导率 / (W·m−1·K−1) 热膨胀系数 / (10−6·K−1) Si 2.30 150 4.1 GaAs 5.30 39 5.8 Al2O3 (96%) 3.70 21 7.3 BeO 2.90 250 6.7～8.0 AlN 3.26 70～260 3.5 SiC 3.18 65～200 3.5 Kovar 8.10 17 5.2 Inovar 8.04 11 0.4 W/Cu 15.70 200 7.0 Mo/Cu 10.00 398 17.8 
下载: 导出CSV
表 2 几种常用高导热铝基复合材料性能
Table 2 Properties of the common high thermal conductivity aluminum matrix composites
下载: 导出CSV
表 3 高导热用金属基复合材料制备方法及性能
Table 3 Preparation methods and properties of the metal matrix composites for the high thermal conductivity
材料 制备方法 界面改性方法 热导率 / (W·m−1·K−1) 热膨胀系数 / (10−6K−1) 文献 Sip/Al 热压烧结 — 120～140 6~12 [6] Sip/Al 放电等离子烧结 — 110～150 7～17 [64] Sip/Al 铸造法 — 100～150 8 [65] Sip/Al 熔渗法 — 90～130 5～8 [11] SiCp/Al 热压烧结 — 180～270 — [20] SiCp/Al 放电等离子烧结 — 160～191 14～23 [53] SiCp/Al 熔渗法 — ～230 8 [7] 金刚石/Al 热压烧结 — 300～430 6～10 [42] 金刚石/Al 放电等离子烧结 — 403 — [52] 金刚石/Al 熔渗法 颗粒表面金属化 320～340 4.0～4.3 [8] 金刚石/Cu 热压烧结 颗粒表面金属化 721 — [9] 金刚石/Cu 放电等离子烧结 — 330～400 8～14 [26] 金刚石/Cu 高温高压烧结 — 300～430、700～900 — [42，44−46] 金刚石/Cu 熔渗法 颗粒表面金属化 580～657 — [30] 金刚石/Cu 熔渗法 基体合金化 711 7.24 [32] 金刚石/Cu 热轧法 基体合金化 433 — [34] 金刚石/Cu 热轧法 基体合金化 550 7 [35] 鳞片石墨/Cu 热压烧结 基体合金化 560～628 5 [41] 鳞片石墨/Cu 放电等离子烧结 颗粒表面金属化 466～532 −1.4～12.8 [38]
下载: 导出CSV
-
[1] Molina-Jordá J M. Thermal conductivity of metal matrix composites with coated inclusions: a new modelling approach for interface engineering design in thermal management. J Alloys Compd, 2018, 745: 849 DOI: 10.1016/j.jallcom.2018.02.092
[2] Mallik S, Ekere N, Best C, et al. Investigation of thermal management materials for automotive electronic control units. Appl Therm Eng, 2011, 31(2-3): 355 DOI: 10.1016/j.applthermaleng.2010.09.023
[3] 常国, 段佳良, 王鲁华, 等. 新一代高导热金属基复合材料界面热导研究进展. 材料导报, 2017, 31(7): 72 DOI: 10.11896/j.issn.1005-023X.2017.07.011Thermal Chang G, Duan J L, Wang L H, et al. Thermal boundary conductance of a new generation of high thermal conductivity metal matrix composites: A review. Mater Rev, 2017, 31(7): 72 DOI: 10.11896/j.issn.1005-023X.2017.07.011Thermal
[4] 任淑彬, 陈志宝, 曲选辉. 电子封装用金属基复合材料的研究进展. 江西科学, 2013, 31(4): 501 DOI: 10.3969/j.issn.1001-3679.2013.04.020 Ren S B, Chen Z B, Qu X H. Research progress on metal matrix composites for electronic packaging. Jiangxi Sci, 2013, 31(4): 501 DOI: 10.3969/j.issn.1001-3679.2013.04.020
[5] 刘骞. 非连续石墨/铜复合材料的制备与热性能研究[学位论文]. 北京: 北京科技大学, 2015 Liu Q. Research of Preparation and Thermal Properties of Discontinous Graphite/Copper Composites [Dissertation]. Beijing: University of Science and Technology Beijing, 2015
[6] Liu J W, Zhou X X, Xin H X. High-Si reinforced Al matrix composites prepared by powder semi-solid squeeze. J Alloys Compd, 2017, 726: 772 DOI: 10.1016/j.jallcom.2017.08.049
[7] Cui Y, Wang L F, Ren J Y. Multi-functional SiC/Al composites for aerospace applications. Chin J Aeronaut, 2008, 21(6): 578 DOI: 10.1016/S1000-9361(08)60177-6
[8] 郭开金. 高导热金刚石/铝复合材料界面构建及组织性能研究[学位论文]. 北京: 北方工业大学, 2020 Guo K J. Design on Interface Construction and Research on Microstructure and Properties of High Thermal Conductivity Diamond/Aluminum Composite [Dissertation]. Beijing: North China University of Technology, 2020
[9] Zhang C, Wang R, Cai Z, et al. Effects of dual-layer coatings on microstructure and thermal conductivity of diamond/Cu composites prepared by vacuum hot pressing. Surf Coat Technol, 2015, 277: 299 DOI: 10.1016/j.surfcoat.2015.07.059
[10] Qu X, Zhang L, Wu M, et al. Review of metal matrix composites with high thermal conductivity for thermal management applications. Prog Nat Sci Mater Int, 2011, 21(3): 189 DOI: 10.1016/S1002-0071(12)60029-X
[11] Jacobson D M, Ogilvy A J W, Leatham A G. Applications of Osprey lightweight controlled expansion (CE) alloys. Technol Rep, 2004: 1
[12] Liu Y, Fan J, Hao X, et al. Advanced hermetic electronic packaging based on lightweight silicon/aluminum composite produced by powder metallurgy technique. Rare Met, 2020, 39: 1307 DOI: 10.1007/s12598-016-0833-1
[13] 张志麒. 常压烧结制备高硅Sip/6061Al复合材料的研究[学位论文]. 合肥: 合肥工业大学, 2017 Zhang Z Q. Study on Preparation of High Silicon Sip/6061Al Composites by Atmospheric Sintering [Dissertation]. Hefei: Hefei University of Technology, 2017
[14] Zuo L, Zhao X, Li Z, et al. A review of friction stir joining of SiCp/Al composites. Chin J Aeronaut, 2020, 33(3): 792 DOI: 10.1016/j.cja.2019.07.019
[15] 郝世明. 中体积分数SiCp/Al复合材料的制备和微结构及性能研究[学位论文]. 郑州: 郑州大学, 2015 Hao S M. Study on Preparation, Micro Structure and Properties of Medium Volume Fraction SiCp/Al Composites [Dissertation]. Zhengzhou: Zhengzhou University, 2015
[16] 吴孟武, 华林, 周建新, 等. 导热铝合金及铝基复合材料的研究进展. 材料导报, 2018, 32(9): 1486 DOI: 10.11896/j.issn.1005-023X.2018.09.013 Wu M W, Hua L, Zhou J X, et al. Advances in thermal conductive aluminum alloys and aluminum matrix composites. Mater Rev, 2018, 32(9): 1486 DOI: 10.11896/j.issn.1005-023X.2018.09.013
[17] 张荻, 谭占秋, 熊定邦, 等. 热管理用金属基复合材料的应用现状及发展趋势. 中国材料进展, 2018, 37(12): 994 Zhang D, Tan Z Q, Xiong D B, et al. Application and prospect of metal matrix composites for thermal management: an overview. Mater China, 2018, 37(12): 994
[18] Chen C W, Lee S L, Lin J C, et al. Effects of Sip size and volume fraction on properties of Al/Sip composites. Mater Lett, 2002, 52(4-5): 334 DOI: 10.1016/S0167-577X(01)00418-9
[19] 李泽华, 冯志军, 李宇飞, 等. SiC颗粒增强铝基复合材料发展历程及制备方法与应用现状 // 中国铸造活动周论文集. 成都, 2016: 332 Li Z H, Feng Z J, Li Y F, et al. The development of SiCp/Al matrix composites and its preparative technique and application status // Collection of Chinese Casting Activities. Chengdu, 2016: 332
[20] Chen Z, Tan Z, Ji G, et al. Effect of interface evolution on thermal conductivity of vacuum hot pressed SiC/Al composites. Adv Eng Mater, 2015, 17(7): 1076 DOI: 10.1002/adem.201400412
[21] Johnson W B, Sonuparlak B. Diamond/Al metal matrix composites formed by the pressureless metal infiltration process. J Mater Res, 1993, 8(5): 1169 DOI: 10.1557/JMR.1993.1169
[22] Natishan P M, Everett R K, Glesener J W, et al. Electrochemical behavior of diamond-reinforced composites. Mater Sci Eng A, 1995, 197(1): 79 DOI: 10.1016/0921-5093(94)09738-0
[23] Beffort O, Vaucher S, Khalid F A. On the thermal and chemical stability of diamond during processing of Al/diamond composites by liquid metal infiltration (squeeze casting). Diamond Relat Mater, 2004, 13(10): 1834 DOI: 10.1016/j.diamond.2004.04.014
[24] Ruch P W, Beffort O, Kleiner S, et al. Selective interfacial bonding in Al (Si)–diamond composites and its effect on thermal conductivity. Compos Sci Technol, 2006, 66(15): 2677 DOI: 10.1016/j.compscitech.2006.03.016
[25] 冯号, 于家康, 薛晨, 等. 电子封装用金刚石/铝复合材料的显微组织与热膨胀性能. 热加工工艺, 2010, 39(14): 59 DOI: 10.3969/j.issn.1001-3814.2010.14.019 Feng H, Yu J K, Xue C, et al. Microstructure and thermal expansion of diamond/Al composites used for electronic packaging. Hot Working Technol, 2010, 39(14): 59 DOI: 10.3969/j.issn.1001-3814.2010.14.019
[26] Kerns J A, Colella N J, Makowiecki D, et al. Dymalloy: a composite substrate for high power density electronic components // International Symposium on Microelectronics: Showcasing the Stars of Microelectronics and International Symposium on Ball Grid Array. Los Angeles, 1995: 22
[27] 唐仕英, 刘晓新, 郑开伟, 等. 纳米石墨/铝基复合材料的摩擦磨损性能. 机械工程材料, 2007, 31(3): 43 Tang S Y, Liu X X, Zhang K W, et al. Friction and wear performance of nano-graphite/Al matrix composite material. Mater Mech Eng, 2007, 31(3): 43
[28] 罗伟, 王宇, 薛令, 等. 制备高导热金刚石/铜复合材料的影响因素及研究进展. 四川冶金, 2020, 42(6): 2 DOI: 10.3969/j.issn.1001-5108.2020.06.002 Luo W, Wang Y, Xue L, et al. Influence factors and research progress of preparing high thermal conductivity diamond copper composites. Sichuan Metall, 2020, 42(6): 2 DOI: 10.3969/j.issn.1001-5108.2020.06.002
[29] Abyzov A M, Kidalov S V, Shakhov F M. Filler-matrix thermal boundary resistance of diamond-copper composite with high thermal conductivity. Phys Solid State, 2012, 54(1): 210 DOI: 10.1134/S1063783412010027
[30] Ma S, Zhao N, Shi C, et al. Mo2C coating on diamond: Different effects on thermal conductivity of diamond/Al and diamond/Cu composites. Appl Surf Sci, 2017, 402: 372 DOI: 10.1016/j.apsusc.2017.01.078
[31] Weber L, Tavangar R. On the influence of active element content on the thermal conductivity and thermal expansion of Cu–X (X = Cr, B) diamond composites. Scr Mater, 2007, 57(11): 988 DOI: 10.1016/j.scriptamat.2007.08.007
[32] Fan Y, Guo H, Xu J, et al. Effects of boron on the microstructure and thermal properties of Cu/diamond composites prepared by pressure infiltration. Int J Miner Metall Mater, 2011, 18(4): 472 DOI: 10.1007/s12613-011-0465-2
[33] Mizuuchi K, Inoue K, Agari Y, et al. Effect of boron addition on the thermal properties of diamond-particle-dispersed Cu-matrix composites fabricated by SPS. J Mater Sci Chem Eng, 2016, 4(9): 1
[34] Jia S Q, Bolzoni L, Li T, et al. Unveiling the interface characteristics and their influence on the heat transfer behavior of hot-forged Cu-Cr/Diamond composites. Carbon, 2021, 172: 390 DOI: 10.1016/j.carbon.2020.10.036
[35] Lei L, Bolzoni L, Yang F. High thermal conductivity and strong interface bonding of a hot-forged Cu/Ti-coated-diamond composite. Carbon, 2020, 168: 553
[36] Hutsch T, Schubert T, Weissgaerber T, et al. Graphite metal composites with tailored physical properties. Emerg Mater Res, 2012, 1(2): 107 DOI: 10.1680/emr.11.00021
[37] Yang L, Miyoshi Y, Sugio K, et al. Effect of graphite orientation distribution on thermal conductivity of Cu matrix composite. Mater Chem Phys, 2021, 257: 123702 DOI: 10.1016/j.matchemphys.2020.123702
[38] Chen J, Ren S, He X, et al. Properties and microstructure of nickel-coated graphite flakes/copper composites fabricated by spark plasma sintering. Carbon, 2017, 121: 25 DOI: 10.1016/j.carbon.2017.05.082
[39] Moustafa S, Daoush W, Ibrahim A, et al. Hot forging and hot pressing of AlSi powder compared to conventional powder metallurgy route. Mater Sci Appl, 2011, 2(8): 1127
[40] Gorbatyuk S M, Pashkov A N, Zarapin A Y, et al. Development of hot-pressing technology for production of aluminum-based metal-matrix composite materials. Metallurgist, 2019, 62(11): 1261
[41] Ren S B, Chen J H, He X B, et al. Effect of matrix-alloying-element chromium on the microstructure and properties of graphite flakes/copper composites fabricated by hot pressing sintering. Carbon, 2018, 127: 412 DOI: 10.1016/j.carbon.2017.11.033
[42] 薛晨, 白华, 吕继磊, 等. 钛镀层对金刚石/铝导热复合材料的显微组织与热学性能的影响. 硬质合金, 2016, 33(4): 217 Xue C, Bai H, Lü J L, et al. Effect of Ti coating on microstructure and thermal property of diamond/Al composite. Cement Carb, 2016, 33(4): 217
[43] Ekimov E A, Suetin N V, Popovich A F, et al. Thermal conductivity of diamond composites sintered under high pressures. Diamond Relat Mater, 2008, 17(4-5): 838 DOI: 10.1016/j.diamond.2007.12.051
[44] 侯领, 沈维霞, 房超, 等. 高导热金刚石/铝复合材料的高温高压制备. 高压物理学报, 2020, 34(5): 93 Hou L, Shen W X, Fang C, et al. High thermal conductivity of diamond/al composites via high pressure and high temperature sintering. Chin J High Pressure Phys, 2020, 34(5): 93
[45] Yoshida K, Morigami H. Thermal properties of diamond/copper composite material. Microelectron Reliab, 2004, 44(2): 303 DOI: 10.1016/S0026-2714(03)00215-4
[46] 胡美华, 于昆鹏, 毕宁, 等. 金刚石粒度对颗粒增强铜基复合材料性能影响的研究. 功能材料, 2018, 49(1): 1059 Hu M H, Yu K P, Bi N, et al. Effect of diamond size on properties of particles reinforced diamond/Cu composites. J Funct Mater, 2018, 49(1): 1059
[47] 赵龙, 宋平新, 张迎九, 等. 高温高压法制备金刚石/铜复合材料的研究. 金刚石与磨料磨具工程, 2018, 38(2): 15 Zhao L, Song P X, Zhang Y J, et al. Study on preparation of diamond/copper composites by high temperature and high pressure method. Diamond Abras Eng, 2018, 38(2): 15
[48] Song S X, Wang Z, Shi G P. Heating mechanism of spark plasma sintering. Ceram Int, 2013, 39(2): 1393 DOI: 10.1016/j.ceramint.2012.07.080
[49] Orrù R, Licheri R, Locci A M, et al. Consolidation/synthesis of materials by electric current activated/assisted sintering. Mater Sci Eng R, 2009, 63(4-6): 127 DOI: 10.1016/j.mser.2008.09.003
[50] Saheb N, Iqbal Z, Khalil A, et al. Spark plasma sintering of metals and metal matrix nanocomposites: a review. J Nanomater, 2012, 2012: 1
[51] Liu Q, He X B, Ren S B, et al. Thermophysical properties and microstructure of graphite flake/copper composites processed by electroless copper coating. J Alloys Compd, 2014, 587: 255 DOI: 10.1016/j.jallcom.2013.09.207
[52] Mizuuchi K, Inoue K, Agari Y, et al. Thermal conductivity of diamond particle dispersed aluminum matrix composites fabricated in solid–liquid co-existent state by SPS. Composites Part B, 2011, 42(5): 1029 DOI: 10.1016/j.compositesb.2011.03.028
[53] 张昂昂. CNTs-SiC复合颗粒的制备及其对铝基复合材料性能的影响[学位论文]. 西安: 西安理工大学, 2019 Zhang A A. Preparation of CNTs-SiC Composites and Its Effect on Properties of Aluminum Composites [Dissertation]. Xian: Xian University of Technology, 2019
[54] Mazahery A, Shabani M O. Microstructural and abrasive wear properties of SiC reinforced aluminum-based composite produced by compocasting. Trans Nonferrous Met Soc China, 2013, 23(7): 1905 DOI: 10.1016/S1003-6326(13)62676-X
[55] Chaudhury S K, Singh A K, Sivaramakrishnan C S S, et al. Preparation and thermomechanical properties of stir cast Al-2Mg-11TiO2 (rutile) composite. Bull Mater Sci, 2004, 27(6): 517 DOI: 10.1007/BF02707279
[56] 苏海, 高文理, 毛成, 等. 搅拌铸造SiCp/2024复合材料的研究. 湖南大学学报(自然科学版), 2009, 36(8): 54 Su H, Gao W L, Mao C, et al. Study of stir cast SiCp/2024 composite. J Hunan Univ Nat Sci, 2009, 36(8): 54
[57] Hashim J, Looney L, Hashmi M S J. The wettability of SiC particles by molten aluminium alloy. J Mater Process Technol, 2001, 119(1-3): 324 DOI: 10.1016/S0924-0136(01)00975-X
[58] Hashim J, Looney L, Hashmi M S J. Metal matrix composites: production by the stir casting method. J Mater Process Technol, 1999, 92-93: 1 DOI: 10.1016/S0924-0136(99)00118-1
[59] 李通, 李金权, 王文广, 等. 影响碳/金属复合材料导热性能的主要因素探讨. 材料导报, 2018, 32(15): 2640 DOI: 10.11896/j.issn.1005-023X.2018.15.015 Li T, Li J Q, Wang W G, et al. A discussion on the main factors affecting thermal conductivity of carbon/metal matrix composites. Mater Rev, 2018, 32(15): 2640 DOI: 10.11896/j.issn.1005-023X.2018.15.015
[60] Monje I E, Louis E, Molina J M, et al. Optimizing thermal conductivity in gas-pressure infiltrated aluminum/diamond composites by precise processing control. Composites Part A, 2013, 48: 9 DOI: 10.1016/j.compositesa.2012.12.010
[61] 车子璠. 金刚石增强铝基复合材料界面形成机理及导热性能[学位论文]. 北京: 北京科技大学, 2017 Che Z F. The Mechanism of Interfacial Structure Formation and Thermal Properties of Al/Diamond Composite [Dissertation]. Beijing: University of Science and Technology Beijing, 2017
[62] 洪庆楠, 任淑彬, 陈志宝, 等. Co对熔渗法制备金刚石/Cu复合材料性能的影响. 粉末冶金技术, 2015, 33(1): 49 Hong Q N, Ren S B, Chen Z B, et al. Effect of Co on properties of diamond/Cu composites by infiltration. Powder Metall Technol, 2015, 33(1): 49
[63] 张永杰, 董应虎, 张瑞卿, 等. 金刚石/铜复合材料导热性能的数值模拟. 材料热处理学报, 2018, 39(6): 110 Zhang Y J, Dong Y H, Zhang R Q, et al. Numerical simulation of thermal conductivity of diamond/copper composites. Trans Mater Heat Treat, 2018, 39(6): 110
[64] 余金辉. Sip/Al复合材料的放电等离子烧结及其热性能研究[学位论文]. 武汉: 武汉理工大学, 2013 Yu J H. Preparation and Properties of Sip/Al Composites by Spark Plasma Sintering [Dissertation]. Wuhan: Wuhan University of Technology, 2013
[65] 修子扬, 张强, 武高辉, 等. 高体积分数电子封装用铝基复合材料性能研究. 电子与封装, 2006(2): 16 DOI: 10.3969/j.issn.1681-1070.2006.02.004 Xiu Z Y, Zhang Q, Wu G H, et al. Study on properties of high reinforcement-content aluminum matrix composites for electronic packaging. Electron Packag, 2006(2): 16 DOI: 10.3969/j.issn.1681-1070.2006.02.004
-
期刊类型引用(2)
1. 梁凯，刘忠军，姬帅，高博阳. 过滤用金属多孔材料力学性能研究进展. 粉末冶金技术. 2024(01): 59-67 . 
本站查看
2. 亓昌，杨孟欣，于晨，崔丽萍，杨姝. 金属空心球复合材料重力铸造工艺研究. 中国材料进展. 2024(05): 420-428 . 百度学术
其他类型引用(2)
计量
- 文章访问数: 2471
- HTML全文浏览量: 493
- PDF下载量: 270
- 被引次数: 4