摘要:
等离子旋转电极制粉技术是当前生产高品质球形金属粉末的重要技术之一，通过电极高速旋转产生的离心力将液膜甩出形成液滴，在惰性气氛中雾化凝固成球形粉末。该技术制备的粉末已成为增材制造、热等静压、表面喷涂等制造技术的重要原料。本文回顾了国内外等离子旋转电极制粉技术的发展历史，综述了近年来国内外发展现状，特别是总结了等离子旋转电极装备和技术在中国的发展情况，指出了该技术尚需研究的科学技术问题和发展方向。
Abstract:Plasma rotating electrode process (PREP) is one of the key technologies for producing high quality spherical metal powders. The liquid film is thrown out to form the droplets by the centrifugal force generated by the high-speed rotation of the electrode, which will atomize and solidify into the spherical powders in an inert atmosphere. The metal powders prepared by PREP have become the important raw materials for additive manufacturing, hot isostatic pressing, surface spraying, and other manufacturing technologies. The history and current status of PREP technology at home and abroad were reviewed in this paper, and the development situation of the PREP equipment and technology in China was summarized. Finally, the development trends and the main scientific issues were pointed out for the further research.
-
Keywords:
- plasma rotating electrode /
- metal powders /
- equipments /
- additive manufacturing /
- powder metallurgy
-
阴极是电真空器件的电子源，是器件的核心部件。热阴极是电真空器件中应用最广的一类阴极，它靠热能使阴极内的电子逸出表面，产生电子发射。经过百余年的发展，热阴极不论是在工作环境、耐受性还是在发射密度方面都取得长足进步，可满足器件1~100 A·cm-2发射电流密度的需求[1]。将阴极装配成间热式的组件结构应用更广泛，阴极发射体自身不通电加热，有利于获取高质量的电子注；热子一般置于发射表面之后，为阴极供热；两者功能不同，但在结构上需紧密相连，组成一个整体，即阴极热子组件，以保证高效传热，阴极稳定工作。多数氧化物阴极和所有扩散式阴极均制备成为阴极热子组件，特别是扩散阴极中的新型钪系阴极，其发射能力高于100 A·cm-2[2]，具有广阔的发展应用前景。
三维快速成型打印简称3D打印，又被称为增材制造技术，可将需要产品的三维模型文件通过3D打印设备进行分层离散处理，再经激光照射等方式将材料逐层叠加、精确堆积，迅速完成产品的成型[3-4]。常规的阴极热子组件制备流程是每个零件分别通过车削加工达到所需形状尺寸，随后进行钎焊组合，而通过3D打印的方式可以实现阴极热子组件整体的连续一体化制造，改变原有装配连接工艺。增材制造方式可快速高效地完成复杂结构的成型，特别适用于制造热子，可省去配套模具的使用和多次进炉烧结，降低制造难度。
国内外3D打印领域中已有近20种不同的工艺体系，其中应用最典型、最成熟的包括立体光刻、叠层实体制造、熔融沉积成型、三维打印与胶粘、选择性激光烧结、选择性激光熔融等。虽然基本原理一致，但由于所用打印材料存在差异，各自特点和具体应用场合也有所不同。选择性激光熔化技术（selective laser melting, SLM）是一种新型“净成形”增材制造技术，主要成形过程包括对零件三维模型切片分层，计算截面轮廓数据并生成激光扫描路径，设备聚焦激光束对预置铺展的粉末进行选取熔化，冷却固化并逐层堆叠成所需零件[5-6]。选择性激光熔化成型件的力学性能好，与相同材料的铸造件相当，相对密度接近100%[7-8]。阴极热子组件的材料主要为难熔金属钨粉，近年来用于钨材料的3D打印技术取得快速发展，已能打印相对密度为97%的钨块体[9-10]。本文采用选择性激光熔化技术一体化3D打印了阴极热子组件模型，并对组件样品的热子加热和阴极发射性能进行了研究和讨论，希望通过完善模型设计和后处理工艺，达到可观的电子发射。
1. 3D打印阴极热子组件模型设计
利用3D打印工艺中的选择性激光熔化技术制备阴极热子组件，其基本原理为将三维模型输入系统，逐层打印、精密堆积，同时还应满足一体化的制备流程，即自下而上将阴极和热子整体连续打印出来。研究人员要重新设计阴极热子组件模型，并根据后续工艺处理的实施情况进行迭代优化。
1.1 材料的单一性
常规的阴极热子组件为套筒结构，不适用于3D打印的一体化成型流程，必须按各个组成部分的功能抽象成层次结构。为避免不同材料在打印过程中的界面连接问题，最好采用同一种粉末材料进行打印。钨粉是制备阴极钨海绵的原料，此外热子的丝料也主要采用钨或钨合金，因此考虑使用钨粉作为原料粉末，直接进行阴极热子组件的3D打印成型。
1.2 支撑结构的合理性
3D打印的成型方式是自下而上的逐层精密堆积[11]，具有方向性，在成型的过程中，必须考虑自身结构的支撑，即在上方连接结构未打印完成之前，下方分离的结构要有独立的支撑，否则无法成型。对支撑结构必须进行合理设计，使其能起到支撑作用的同时，必须在后期易于去除；在设计之初，须考虑所使用的去除手段不会对组件造成破坏。
1.3 热子的电性能
为达到对阴极热子组件的性能要求，使用3D打印的成型方式必须使热子具备足够大的电阻，即进行合理的热子结构设计。在保证自身结构支撑的同时，充分利用空间，尽量延长热子结构的总长。故将热子设计为竖直圆柱阵列，并将每个圆柱首尾顺次连接，形成串联。
按以上设计原则进行多轮优化，适用于3D打印的阴极热子组件模型如图 1所示。如图所示，组件自下而上依次为阴极钨饼、致密层、支撑体、热子和热子引腿，这种模型能够与3D打印逐层精确堆积的成型过程相匹配，其中阴极发射体的孔隙度可通过密度进行调节，即控制激光的功率和扫描速率[12]。
此外，3D打印适合成型复杂形状，该技术特性为热子引腿的构造带来更多想象空间，可以不再拘泥于简单圆柱形状。如图 2所示，异形台阶结构热子引腿的横截面积大于发热丝，能够减小电阻，通电加热时，可降低引腿发热，以提高热子加热阴极的效率；异形结构引腿的自身重量减小，可减轻热子的承重压力；异形结构引腿可增加与热子电位引出带的接触面积，方便可靠连接。
![]()
图 2 热子引腿结构：（a）简单圆柱；（b）和（c）异形台阶Figure 2. Potential pin structures of the heaters: (a)column; (b)and(c)specific steps2. 一体化打印阴极热子组件
将设计好的模型输入选择性激光熔化系统中，经过软件切片分析，并进行逐层打印。阴极热子组件一体化成型过程如图 3所示。在实际成型过程中，钨饼与致密层紧密相连，激光照射粉末，形成具有一定深度的熔池，构成密度渐变的过渡层。为精确检测钨饼密度，使用相同的打印参数，打印形状规则、易于测量的标定样块。如图 4所示，样块尺寸为11 mm×8.19 mm×6.03 mm，重量为7.8 g，计算后可得其相对密度为74.8%，即孔隙度约为25%。确定了钨饼的打印参数后，进行阴极热子组件的一体化打印。
共打印完成两组组件样品：（1）直径为5 mm样品，热丝丝径分别为0.25 mm、0.3 mm和0.4 mm; (2）直径为3 mm样品，丝径为0.25 mm的样品，其宏观形貌如图 5所示。在光学显微镜下（如图 6所示），打印出来的热丝表面粗糙，有粘连的颗粒，这源自选择性激光熔化技术具有的“球化效应”和“粉末粘附”加工特性[13-14]。丝越细，间距越小，虽然可以增大热子的电阻，但也增大了颗粒搭接造成短路的风险；此外，较细的热丝力学强度低，易发生整体变形，为后期去掉支撑结构带来更大的困难。综上所述，直径5 mm的组件应使用0.4 mm的丝径，直径3 mm的组件由于尺寸限制，热丝直径不应超过0.25 mm。
![]()
图 5 3D打印的阴极热子组件样品宏观形貌Figure 5. Macromorphology of the 3D-printed cathode-heater assembly sample![]()
图 6 3D打印的阴极热子组件样品光学形貌Figure 6. Optical morphology of the 3D-printed cathode-heater assembly sample3. 后处理工艺
组件打印完成后，需要进行后续处理，从而使阴极热子组件具备稳定可靠的热发射性能。后处理工艺主要包括去除多余支撑结构、热丝绝缘防护和阴极发射活性物质浸渍等。
3.1 去除多余支撑结构
支撑结构是圆柱阵列，去除后才能断开热丝与阴极的直接相连，使热丝串联并获得高于导线的热子电阻。采用高能激光照射的方式能够将支撑柱熔断，实现稳定可靠的去除操作。去除后的阴极热子组件如图 7所示。去除操作可在光学放大系统下进行精准控制，有效避免伤害中心支柱。中心支柱固定了热子与阴极的相对位置，构成组件，若受损将导致热子与阴极分离；此外要防止热丝受损，由于热丝整体串联，因此只要有一处断点就会产生成片地脱落。
![]()
图 7 去除支撑结构的阴极热子组件样品Figure 7. Cathode-heater assembly samples after removing the supporting columns去除支撑结构后，室温下热子电阻达到0.4Ω。为了直观地检测热子加热性能，在制备绝缘填料之前将样品固定安装在玻璃测试管内，抽真空，同时逐步增加热子电压。在21.6 W加热功率下，选择性激光熔化技术制备的热子温度能够达到1250℃，如见图 8所示。
3.2 热丝绝缘防护与浸盐
通电加热实验验证了去除支撑结构后，打印成型的热丝通过串联的方式能够使热子具备足够的电阻并正常发热。为保证热丝长时间可靠工作，需要进行绝缘防护，并降低热子与阴极温差。常用的处理方式是灌注氧化铝填料并烧结致密。将去除了支撑结构的组件放入模具中，灌注流动性良好的氧化铝粉末浆料，填充热子发热丝之间以及热子和阴极钨饼之间的空隙，干燥固化后从模具内脱出，最后在氢气气氛中高温烧结。图 9所示为直径5 mm和3 mm的样品绝缘防护处理，其中前者的热丝热子引腿打印成了台阶形状。
![]()
图 9 阴极热子组件样品绝缘防护处理Figure 9. Cathode-heater assembly samples after the insulation protection treatment为使阴极具备良好的发射能力，需要在阴极钨饼内浸渍发射盐，浸盐温度低于氧化铝绝缘填料的烧结温度，以减少损伤。清除多余发射盐后，3D打印阴极热子组件的后处理全部完成，随后对该新型阴极热子组件进行排气测试。
4. 阴极热子性能测试
首先对新型阴极热子组件的加热性能进行测试，阴极表面达到工作温度是热发射的前提。如图 10所示，将样品装架于玻璃管壳内，通电加热。通过提高电压逐步增加热子加热功率，表 1所示为在不同加热功率下，热子和阴极发射表面的温度。由表可知，随着加热功率的提高，阴极与热子的温差逐渐提高，保持在150~200℃的范围。常规阴极和钼筒组成的组件温差为100℃，这主要是由于新型阴极热子组件样品没有常规阴极钼筒组件的侧壁辅助传热。
表 1 加热功率及阴极热子温度Table 1. Heating powers and the corresponding temperatures of cathode and heater热子电/V 热子加热功率/W 热子温度/℃ 阴极发射表面温度/℃ 阴极热子温差/℃ 6 12.30 983 830 153 7 16.03 1050 883 167 8 19.28 1129 941 188 9 22.95 1176 987 189 10 26.90 1233 1035 198 11 30.25 1272 1071 201 选用ϕ3 mm的组件样品进行电子发射测试，图 11显示了阴极发射表面宏观形貌。图中可观察到多孔结构，孔径明显大于传统车削加工表面，这种孔分布于整个表面，排列无明显规律。图 12为不同制备工艺得到的阴极表面显微形貌。如图所示，不同于常规粉末冶金工艺制备的阴极表面，选择性激光熔化工艺制备的阴极表面没有明显的粉末烧结多孔结构，且表面存在微裂纹，发射盐填充在这些裂缝之中。进一步能谱分析发现，新型阴极热子组件的阴极表面成分与浸渍铝酸盐阴极一致，如表 2。
![]()
图 12 不同制备工艺得到的阴极表面微观组织：（a）选择性激光熔化工艺；（b）常规粉末冶金工艺Figure 12. Microstructures of the cathode surfaces: (a)SLM; (b)the conventional powder metallurgy process表 2 新型阴极热子组件的阴极表面能谱分析Table 2. Energy spectrum analysis of the new type cathode-heater assembly surface元素 质量分数/% 原子数分数/% O 13.90 59.73 Al 3.36 8.55 Ba 6.19 3.10 W 76.55 28.62 制备常规阴极钨基体时，可通过高温活化烧结形成烧结颈和固相迁移来增加相对密度，形成多孔体。在使用选择性激光熔化工艺打印阴极钨饼的过程中，高能激光将钨粉熔化，冷却凝固后叠加生长成钨饼，微观上已经不存在原有粉末颗粒的形貌特征。激光光斑直径受选择性激光熔化设备限定，为百微米量级，远小于阴极直径，打印时光斑照射钨粉，形成局部熔池，按一定路径移动后，完成整个单层的固化成型。非平衡的凝固过程和不同步的微观组织结构变化能够产生局部应力，形成微裂纹等缺陷[15-16]。调节激光功率和光斑移动速率能够影响熔池范围，控制微裂纹的分布和尺寸。因此，与常规阴极不同，由选择性激光熔化打印制备的阴极基体相对密度较低，可通过微裂纹的产生来控制活性物质浸渍，其宏观检测依然使用密度表征孔度。
图 13为水冷阳极二极管外观形貌，利用水冷阳极二极管检测阴极热子组件发射电流密度。图 14显示了阴极温度为1100℃时，样品的拐点发射电流密度达到7.94 A∙cm-2，取得了可观的电子发射。
![]()
图 13 测试用水冷阳极二极管外观形貌Figure 13. Appearance of the water-cooled diode used in the cathode emission performance testing![]()
图 14 阴极热子组件的阴极发射伏安特性Figure 14. Voltage current characteristics of the cathode emission for the cathode-heater assembly5. 结论
(1）根据3D打印技术的特殊成型方式和工艺特点，构建了合理可行的新型阴极热子组件三维模型，并使用选择性激光熔化设备实现了组件的一体化打印成型。
(2）对新型组件进行多余支撑结构去除、热子绝缘防护和浸盐的后处理，阴极热子组件样品在1100℃下达到约8 A∙cm‒2的拐点发射电流密度。
(3）选择性激光熔化技术通过微裂纹的产生形成非致密的阴极基体，浸渍发射盐后能够获取可观的电子发射，为阴极热子组件研制提供了新的设计方案，即将3D打印技术应用于组件的制备。利用增材制造成型复杂形状的零件，为新结构研发提供了新技术和新思路。
-
![]()
图 2 非转移弧型等离子旋转电极制粉技术三棍压紧驱动示意图（a）及原理图（b）
Figure 2. Sketch map of the three-bar compacting drive (a) and the schematic diagram of the non-transfer arc type PREP (b)
![]()
图 3 湖南顶立科技有限公司工业级（a）及西安赛隆公司工业级（b）、桌面级（c）及中型（d）转移弧型等离子旋转电极装备
Figure 3. Industrial grade transfer arc PREP equipment of Advanced Corporation for Materials & Equipment (a), and the industrial grade (b), desktop (c), and medium (d) transfer arc PREP equipment of Xi'an Sailong Metal Materials Co., Ltd.
![]()
![]()
![]()
图 6 等离子旋转电极技术制备的难熔金属球形粉末：（a）W粉；（b）Mo粉；（c）Ta粉；（d）Nb粉
Figure 6. Refractory metal spherical powders prepared by PREP: (a) tungsten powders; (b) molybdenum powders; (c) tantalum powders; (d) niobium powders
表 1 典型等离子旋转电极金属粉末氧质量分数和氧增量[1]
Table 1 Oxygen mass fraction and oxygen increment of the typical PREP metal powders[1]
材料 原材料氧质量分数 / ×10‒6 粉末氧质量分数 / ×10‒6 氧增量 / ×10‒6 IN718 54 70 16 TC4 600 700 100 17-4PH 95 130 35 316L 160 200 40 Ta1 20 30 10 W 30 50 20 TiAl4822 560 650 90 Cu(T2) 10 30 20 Mo 75 110 35 注：TiAl4822为Ti48Al2Cr2Nb缩写。 
下载: 导出CSV
材料 流动性 / [s·(50g)‒1] 松装密度 / (g·cm‒3) 振实密度 / (g·cm‒3) IN718 12.50 4.74 5.23 TC4 28.30 2.64 2.70 17-4PH 14.10 4.59 4.82 316L 12.80 4.72 4.98 Ta1 6.00 9.97 10.60 W 5.70 11.62 12.00 TiAl4822 29.40 2.30 2.40 Cu(T2) 14.40 5.18 5.70 Mo 11.20 5.98 6.41
下载: 导出CSV
-
[1] 杨星波, 朱纪磊, 陈斌科, 等. 等离子旋转电极雾化技术及粉末粒度控制研究现状. 粉末冶金工业, 2022, 32(2): 90 DOI: 10.13228/j.boyuan.issn1006-6543.20210047 Yang X B, Zhu J L, Chen B K, et al. Research status of plasma rotating electrode atomization technology and powder particle size control. Powder Metall Ind, 2022, 32(2): 90 DOI: 10.13228/j.boyuan.issn1006-6543.20210047
[2] 杨洪涛, 卢志辉, 孙志杨, 等. 等离子旋转电极雾化制粉设备国内研究现状. 粉末冶金工业, 2021, 31(4): 88 DOI: 10.13228/j.boyuan.issn1006-6543.20200190 Yang H T, Lu Z H, Sun Z Y, et al. Domestic research status of plasma rotation electrode process equipment. Powder Metall Ind, 2021, 31(4): 88 DOI: 10.13228/j.boyuan.issn1006-6543.20200190
[3] Demir F, Yurtkuran E, Unal R, et al. 3D Cfd modelling of non-transferred argon plasma torch. Mater Today Proceed, 2020, 32(1): 10
[4] Kaufmann A R. Production of Pure, Spherical Powders: United State Patent, 3802816. 1974-4-9
[5] Ozols A, Sirkin H R, Vicente E E. Segregation in stellite powders produced by the plasma rotating electrode process. Mater Sci Eng A, 1999, 262(1-2): 64 DOI: 10.1016/S0921-5093(98)01021-1
[6] 孙念光, 陈斌科, 向长淑, 等. 等离子旋转电极雾化制粉技术现状和创新. 粉末冶金工业, 2020, 30(5): 84 DOI: 10.13228/j.boyuan.issn1006-6543.20190133 Sun N G, Chen B K, Xiang C S, et al. The plasma rotating electrode processing technology current situation and innovation. Powder Metall Ind, 2020, 30(5): 84 DOI: 10.13228/j.boyuan.issn1006-6543.20190133
[7] 张义文, 迟悦. 俄罗斯粉末冶金高温合金研制新进展. 粉末冶金工业, 2012, 22(5): 37 DOI: 10.3969/j.issn.1006-6543.2012.05.009 Zhang Y W, Chi Y. Recent developments of Powders metallurgy superalloy in Russia. Powder Metall Ind, 2012, 22(5): 37 DOI: 10.3969/j.issn.1006-6543.2012.05.009
[8] 张莹. 俄罗斯粉末高温合金涡轮盘的生产工艺. 钢铁研究学报, 2000, 12(3): 63 DOI: 10.3321/j.issn:1001-0963.2000.03.015 Zhang Y. Production technology of powder metallurgy superalloy turbine disk in Russia. J Iron Steel Res, 2000, 12(3): 63 DOI: 10.3321/j.issn:1001-0963.2000.03.015
[9] 张义文, 贾建, 刘建涛, 等. 俄罗斯新型粉末高温合金研究最新进展. 粉末冶金工业, 2020, 30(6): 102 DOI: 10.13228/j.boyuan.issn1006-6543.20200193 Zhang Y W, Jia J, Liu J T, et al. Recent development of new type powder metallurgy superalloys in Russia. Powder Metall Ind, 2020, 30(6): 102 DOI: 10.13228/j.boyuan.issn1006-6543.20200193
[10] 孙兼, 邹金文, 刘培英. 盘件用粉末高温合金的研究与发展. 航空工程与维修, 2001(1): 28 Sun J, Zou J W, Liu P Y. Research and development of powder metallurgy superalloy. Aviat Mainten Eng, 2001(1): 28
[11] 赵风琴, 王长京. 等离子旋转电极制粉设备中的等离子发生器装置的设计与制造. 稀有金属材料与工程, 1988, 17(6): 66 DOI: 10.3321/j.issn:1002-185X.1988.06.012 Zhao F Q, Wang C J. Design and manufacture of plasma generator in plasma rotating electrode pulverizing equipment. Rare Met Mater Eng, 1988, 17(6): 66 DOI: 10.3321/j.issn:1002-185X.1988.06.012
[12] 张义文, 张莹, 陈生大, 等. PREP制取高温合金粉末的特点. 粉末冶金技术, 2001, 19(1): 12 DOI: 10.3321/j.issn:1001-3784.2001.01.003 Zhang Y W, Zhang Y, Chen S D, et al. Characteristics of PREP in preparing superalloy powder. Powder Metall Technol, 2001, 19(1): 12 DOI: 10.3321/j.issn:1001-3784.2001.01.003
[13] Miller S. Rotating electrode process //ASM Handbook Vol 7. Geauga: ASM International, 1998
[14] Arkon Ltd. PREP powder production unit for additive manufacturing. [2022-06-09]. https://arkon3d.ru/en/equipment_category/prep-powder-production-unit-for-additive-manufacturing/
[15] 中机新材料研究院. 等离子旋转电极制粉设备. [2022-06-09]. http://campowder.com/index.php/cases_20.html China Machinery Institute of Advanced Materials. Plasma rotary electrode powder making equipment. [2022-06-09]. http://campowder.com/index.php/cases_20.html
[16] Cui Y J, Zhao Y F, Numata H, et al. Effects of process parameters and cooling gas on powder formation during the plasma rotating electrode process. Powder Technol, 2021, 393: 301 DOI: 10.1016/j.powtec.2021.07.062
[17] Cui Y J, Zhao Y F, Numata H, et al. Effects of plasma rotating electrode process parameters on the particle size distribution and microstructure of Ti‒6Al‒4V alloy powder. Powder Technol, 2020, 376: 363 DOI: 10.1016/j.powtec.2020.08.027
[18] Zhao Y F, Cui Y J, Numata H, et al. Centrifugal granulation behavior in metallic powder fabrication by plasma rotating electrode process. Sci Rep, 2020, 10: 18446 DOI: 10.1038/s41598-020-75503-w
[19] Kaplanskii Y Y, Zaitsev A A, Sentyurina Z A, et al. The structure and properties of pre-alloyed NiAl‒Cr(Co, Hf) spherical powders produced by plasma rotating electrode processing for additive manufacturing. J Mater Res Technol, 2018, 7(4): 461 DOI: 10.1016/j.jmrt.2018.01.003
[20] Yamanoglu R, German R, Karagoz S, et al. Microstructural investigation of as cast and PREP atomised Ti–6Al–4V alloy. Powder Metall, 2011, 54(5): 604 DOI: 10.1179/1743290110Y.0000000006
[21] 陶宇, 冯涤, 张义文, 等. 优化等离子旋转电极工艺提高FGH95合金粉末的收得率. 粉末冶金工业, 2003, 13(2): 33 DOI: 10.3969/j.issn.1006-6543.2003.02.007 Tao Y, Feng D, Zhang Y W, et al. Study on improving the yield of FGH95 alloy powder in plasma rotating electrode process. Powder Metall Ind, 2003, 13(2): 33 DOI: 10.3969/j.issn.1006-6543.2003.02.007
[22] 陶宇, 冯涤, 张义文, 等. PREP工艺参数对FGH95高温合金粉末特性的影响. 钢铁研究学报, 2003, 15(5): 46 DOI: 10.3321/j.issn:1001-0963.2003.05.011 Tao Y, Feng D, Zhang Y W, et al. Effect of PREP process parameters on powder properties for FGH95 superalloy. J Iron Steel Res, 2003, 15(5): 46 DOI: 10.3321/j.issn:1001-0963.2003.05.011
[23] 刘建涛, 张义文. 等离子旋转电极雾化工艺制备FGH96合金粉末颗粒的组织. 材料热处理学报, 2012, 33(1): 31 DOI: 10.13289/j.issn.1009-6264.2012.01.002 Liu J T, Zhang Y W. Microstructure of FGH96 superalloy powders atomized plasma rotating electrode process. Trans Mater Heat Treat, 2012, 33(1): 31 DOI: 10.13289/j.issn.1009-6264.2012.01.002
[24] 张莹, 黄虎豹, 刘明东, 等. PREP工艺制取镍基高温合金粉末中的异常颗粒. 稀有金属材料与工程, 2017, 46(11): 3485 Zhang Y, Huang H B, Liu M D, et al. Abnormal particles in Ni-base superalloy powder by PREP process. Rare Met Mater Eng 2017, 46(11): 3485
[25] 胡家齐, 王长军, 魏来, 等. VIGA法与PREP法制备不锈钢粉末的内部孔洞对比研究. 粉末冶金工业, 2021, 31(4): 11 DOI: 10.13228/j.boyuan.issn1006-6543.20190073 Hu J Q, Wang C J, Wei L, et al. A comparative research of porosity in stainless steel powders manufactured by vacuum induction-melting gas atomization and plasma rotating electrode process. Powder Metall Ind, 2021, 31(4): 11 DOI: 10.13228/j.boyuan.issn1006-6543.20190073
[26] 王晨, 赵霄昊, 马逸驰, 等. 超高转速等离子旋转电极工艺制备钬铜球形粉末的研究. 粉末冶金技术, 2020, 38(3): 227 DOI: 10.19591/j.cnki.cn11-1974/tf.2020.03.011 Wang C, Zhao X H, Ma Y C, et al. Study of the spherical HoCu powders prepared by supreme-speed plasma rotating electrode process. Powder Metall Technol, 2020, 38(3): 227 DOI: 10.19591/j.cnki.cn11-1974/tf.2020.03.011
[27] 王华, 陈蕾蕾, 瞿宗宏. 热处理冷却速率对粉末TC11组织及性能的影响. 中国新技术新产品, 2021(11): 84 DOI: 10.3969/j.issn.1673-9957.2021.11.029 Wang H, Chen L L, Zhai Z H. Effect of heat treatment cooling rate on microstructure and properties of powder TC11. New Technol New Prod China, 2021(11): 84 DOI: 10.3969/j.issn.1673-9957.2021.11.029
[28] 兰剑, 刘立科, 王庆相, 等. 齿科用Co25Cr5W5Mo合金粉末制备及激光选区熔化成形打印件性能分析. 粉末冶金工业, 2021, 31(6): 13 DOI: 10.13228/j.boyuan.issn1006-6543.20200273 Lan J, Liu L K, Wang Q X, et al. Preparation of Co25Cr5W5Mo alloy powder for dentistry and its performance analysis of SLM printed parts. Powder Metall Ind, 2021, 31(6): 13 DOI: 10.13228/j.boyuan.issn1006-6543.20200273
[29] 相敏, 韩志宇, 闫飞, 等. 热等静压对Ti6Al4V粉末冶金件组织和性能的影响. 钛工业进展, 2017, 34(4): 30 Xiang M, Han Z Y, Yan F, et al. Effect of hot isostatic press process on microstructure and properties of PM Ti6Al4V alloy part. Titanium Ind Prog, 2017, 34(4): 30
[30] 康路, 王松, 李鑫, 等. 一种提高镍基金属离心雾化细粉收得率的冶金方法: 中国专利, 201711397083. 2018-05-04 Kang L, Wang S, Li X, et al. Metallurgy Method for Improving Yield of Centrifugal Atomization Fine Powder of Nickel-based Metal: China Patent, 201711397083. 2018-05-04
[31] 刘洋, 韩志宇, 王庆相, 等. 一种制备微细球形金属粉末的设备及方法: 中国专利, 201611174429. 2017-05-17 Liu Y, Han Z Y, Wang Q X, et al. Rotating Electrode Preparing Micro Spherical Metal Powder and Method of Rotating Electrode: China Patent, 201611174429. 2017-05-17
[32] 韩志宇, 梁书锦, 曾光, 等. 一种去除金属粉末中非金属夹杂的装置: 中国专利, 201420231747. 2014-08-27 Han Z Y, Liang S Y, Zeng G, et al. Device for Removing Nonmetallic Inclusions in Metallic Powder: China Patent, 201420231747. 2014-08-27
[33] 赵霄昊, 王晨, 潘霏霏, 等. 球形钛合金粉末制备技术及增材制造应用研究进展. 粉末冶金工业, 2019, 29(6): 71 DOI: 10.13228/j.boyuan.issn1006-6543.20180092 Zhao X H, Wang C, Pan F F, et al. A review on the methods and additive manufacturing application of spherical titanium alloy powder. Powder Metall Ind, 2019, 29(6): 71 DOI: 10.13228/j.boyuan.issn1006-6543.20180092
[34] Liu Y, Zhao X H, Lai Y J, et al. A brief introduction to the selective laser melting of Ti6Al4V powders by supreme-speed plasma rotating electrode process. Prog Nat Sci Mater Int, 2020, 30(1): 94 DOI: 10.1016/j.pnsc.2019.12.004
[35] Liu Y, Liang S J, Han Z Y, et al. A novel model of calculating particle sizes in plasma rotating electrode process for superalloys. Powder Technol, 2018, 336: 406 DOI: 10.1016/j.powtec.2018.06.002
[36] Frost A R. Rotary atomization in the ligament formation mode. J Agric Eng Res, 1981, 26(1): 63 DOI: 10.1016/0021-8634(81)90127-X
[37] 陶珍东, 郑少华. 粉体工程与设备. 北京: 化学工业出版社, 2010 Tao Z D, Zhen S H. Powder Engineering and Equipment. Beijing: Chemical Industry Press, 2010
[38] Han Z Y, Zhang P X, Lei L M, et al. Morphology and particle analysis of the Ni3Al-based spherical powders manufactured by supreme-speed plasma rotating electrode process. J Mater Res Technol, 2020, 9(6): 13937 DOI: 10.1016/j.jmrt.2020.09.102
[39] 金园园, 贺卫卫, 陈斌科, 等. 球形难熔金属粉末的制备技术. 航空制造技术, 2019, 62(22): 64 DOI: 10.16080/j.issn1671-833x.2019.22.064 Jin Y Y, He W W, Chen B K, et al. Preparation of spherical refractory metal powders. Aeron Manuf Technol, 2019, 62(22): 64 DOI: 10.16080/j.issn1671-833x.2019.22.064
[40] 李晓辉, 陈斌科, 凤治华, 等. 等离子旋转电极雾化制备钨粉及性能表征. 粉末冶金工业, 2022, 32(1): 15 DOI: 10.13228/j.boyuan.issn1006-6543.20210017 Li X H, Chen B K, Feng Z H, et al. Preparation and properties of spherical tungsten powders by plasma rotating electrode process for additive manufacturing. Powder Metall Ind, 2022, 32(1): 15 DOI: 10.13228/j.boyuan.issn1006-6543.20210017
[41] He W, Liu Y, Tang H, et al. Microstructural characteristics and densification behavior of high-Nb TiAl powder produced by plasma rotating electrode process. Mater Des, 2017, 132: 275 DOI: 10.1016/j.matdes.2017.06.072
[42] Qiu S, Chen B K, Xiang C S. Preparation and properties of spherical Mo powders by plasma rotating electrode process for additive manufacturing. Mater Sci Forum, 2020, 993: 391 DOI: 10.4028/www.scientific.net/MSF.993.391
[43] Chen G, Zhao S Y, Tan P, et al. Shape memory TiNi powders produced by plasma rotating electrode process for additive manufacturing. Trans Nonferrous Met Soc China, 2017, 27(12): 2647 DOI: 10.1016/S1003-6326(17)60293-0
[44] Yin J O, Chen G, Zhao S Y, et al. Microstructural characterization and properties of Ti-28Ta at.% powders produced by plasma rotating electrode process. J Alloys Compd, 2017, 713: 222
[45] 杨鑫, 奚正平, 刘咏, 等. 等离子旋转电极法制备钛铝粉末性能表征. 稀有金属材料与工程, 2010, 39(12): 2251 Yang X, Xi Z P, Liu Y, et al. Characterization of TiAl powders prepared by plasma rotating electrode processing. Rare Met Mater Eng, 2010, 39(12): 2251
[46] Chen G, Zhao S Y, Tan P, et al. A comparative study of Ti6Al4V powders for additive manufacturing by gas atomization, plasma rotating electrode process and plasma atomization. Powder Technol, 2018, 333: 38 DOI: 10.1016/j.powtec.2018.04.013
[47] 赵少阳, 殷京瓯, 沈垒, 等. PREP法制备Ti‒60Ta合金粉末及其性能. 稀有金属材料与工程, 2017, 46(6): 1679 Zhao S Y, Yin J G, Shen L, et al. Ti‒60Ta powders produced by PREP and their properties. Rare Met Mater Eng, 2017, 46(6): 1679
[48] Nie Y, Tang J, Teng J, et al. Particle defects and related properties of metallic powders produced by plasma rotating electrode process. Adv Powder Technol, 2020, 31(7): 2912 DOI: 10.1016/j.apt.2020.05.018
[49] Nie Y, Tang J, Yang B, et al. Comparison in characteristic and atomization behavior of metallic powders produced by plasma rotating electrode process. Adv Powder Technol, 2020, 31(5): 2152 DOI: 10.1016/j.apt.2020.03.006
[50] Liu W, Duan Y, Ma Y, et al. Surface characterization of plasma rotating electrode atomized 30CrMnSiNi2A steel powder. Appl Surf Sci, 2020, 528: 147004 DOI: 10.1016/j.apsusc.2020.147004
[51] Tang J, Nie Y, Lei Q, et al. Characteristics and atomization behavior of Ti‒6Al‒4V powder produced by plasma rotating electrode process. Adv Powder Technol, 2019, 30(10): 2330 DOI: 10.1016/j.apt.2019.07.015
[52] Li Q J, Zhang L, Chen X, et al. Characterization of plasma rotating electrode atomized Nb-Ti based alloy powder. Met Powder Rep, 2020, 75(2): 82 DOI: 10.1016/j.mprp.2019.04.064
[53] 陈焕铭, 胡本芙, 李慧英, 等. 等离子旋转电极雾化FGH95高温合金粉末颗粒凝固组织特征. 金属学报, 2003, 39(1): 30 DOI: 10.3321/j.issn:0412-1961.2003.01.008 Chen H M, Hu B F, Li H Y, et al. Microstructure characteristics of FGH95 superalloy powders prepared by PREP. Acta Metall Sinica, 2003, 39(1): 30 DOI: 10.3321/j.issn:0412-1961.2003.01.008
[54] 陈焕铭, 胡本芙, 余泉茂, 等. 等离子旋转电极雾化熔滴的热量传输与凝固行为. 中国有色金属学报, 2002, 12(5): 883 DOI: 10.3321/j.issn:1004-0609.2002.05.006 Chen H M, Hu B F, Yu Q M, et al. Heat transfer and solidification behavior of droplets during plasma rotating electrode processing. Chin J Nonferrous Met, 2002, 12(5): 883 DOI: 10.3321/j.issn:1004-0609.2002.05.006
[55] 李礼, 戴煜, 吕攀. 等离子旋转电极法制取AlSi10Mg铝合金粉末工艺的研究. 新材料产业, 2018(12): 23 DOI: 10.19599/j.issn.1008-892x.2018.12.006 Li L, Dai Y, Lü P. Study on the technology of producing AlSi10Mg aluminum alloy powder by plasma rotating electrode method. Adv Mater Ind, 2018(12): 23 DOI: 10.19599/j.issn.1008-892x.2018.12.006
[56] 王华, 白瑞敏, 周晓明, 等. PREP法和AA法制取Inconel 718粉末对比分析. 中国新技术新产品, 2019(19): 1 DOI: 10.3969/j.issn.1673-9957.2019.19.002 Wang H, Bai R M, Zhou X M, et al. Comparative analysis of Inconel 718 powder prepared by PREP method and AA method. New Technol New Prod China, 2019(19): 1 DOI: 10.3969/j.issn.1673-9957.2019.19.002
[57] Hsu T I, Wei C M, Wu L D, et al. Nitinol powders generate from plasma rotation electrode process provide clean powder for biomedical devices used with suitable size, spheroid surface and pure composition. Sci Rep, 2018, 8(1): 13776 DOI: 10.1038/s41598-018-32101-1