Atomization simulation and preparation of GH3536 powders at different atomization pressures
-
摘要:
使用真空感应熔炼气体雾化方法，在不同雾化压力（7、8、9 MPa）下制备了球形GH3536合金粉末。通过使用多相流模型和离散相模型对喷嘴下方区域进行了数值模拟，再现了不同雾化气压下的一次雾化和二次雾化过程。实验和模拟的结果表明：回流区的气体速度和滞止压力随雾化气压的提高而增加，雾化气压的增加使粉末粒度不断减小，模拟结果与实验结果吻合，验证了雾化模型的可靠性。提高雾化气压可提高细粉收得率，但颗粒尺寸的减小和颗粒形貌的改变会对粉末的流动性能造成直接影响，在雾化压力8 MPa下制备的粉末具有最佳的流动性和松装密度，分别为14.34 (s·50g−1)和4.728 g·cm−3。
Abstract:Spherical GH3536 alloy powders were prepared by vacuum induction-melting gas atomization method at the different atomization pressures (7, 8, 9 MPa). The region below the nozzle was numerically simulated by multiphase flow model and discrete phase model, and the primary and secondary atomization processes at the different atomization pressures were reproduced. In the results, the flow velocity and stagnation pressure in the recirculation zone increase with the increase of atomization pressure. With the increase of atomization pressure, the powder particle size decreases continuously. The simulation results are similar with the experimental results, verifying the reliability of the atomization model. The increase of atomization pressure can increase the yield of fine powders, but the decrease of particle size and the change of particle morphology may directly affect the powder flowability. The powders prepared at the atomization pressure of 8 MPa show the best flowability and the optimum apparent density, which are 14.34 (s·50g−1) and 4.728 g·cm−3, respectively.
-
烧结是将粉末或粉末压坯加热到低于其基本成分熔点温度，并在适当的气氛或真空条件下，以一定的方法和速度冷却到室温的过程。烧结使粉末颗粒之间发生粘结，压坯中颗粒相互键联，晶粒长大，空隙（气孔）和晶界渐趋减少，通过物质的传递，总体积收缩，密度增加，烧结体的强度增加，最后成为具有某种显微结构的致密多晶烧结体，最终获得所需力学性能的制品或材料。烧结是粉末冶金工艺中的一个重要环节，对最终产品质量有着决定性影响。烧结产生的缺陷及问题难以通过后续工艺调节或弥补，所以深入细致地对烧结行为进行研究探索是十分必要的[1–3]。
钼（Mo）是元素周期表中VIB族元素，原子序数42，原子量95.94。高熔点与高沸点是Mo的显著特点之一，其熔点为2620 ℃，仅次于C、W、Re、Ta和Os。由于Mo的熔点高，属难熔金属，Mo及Mo合金主要采用粉末冶金方法制备。首先获得高纯度Mo粉，再加入所需合金元素粉末，经油压机模压或冷等静压成形，最终经低于熔点的温度烧结成Mo合金制品。在生产实践中，科研人员对原料Mo粉、烧结后的Mo产品性能研究较多，对烧结过程，仅限于记录烧结温度、气氛、升温保温时间等工艺参数，对Mo合金本身在烧结过程中的变化研究较少。本文采用原位测量法，对比研究了放电等离子烧结与真空热压烧结法制备Mo–30W合金的烧结行为，更加准确地掌握Mo合金的烧结收缩和致密化规律。
1. 实验材料及方法
实验采用商用Mo粉和W粉，Mo粉费氏粒度为3.5 μm，W粉费氏粒度为3.0 μm。经过混料、压制成形，制备成ϕ20 mm×15 mm试样，分别使用放电等离子烧结（spark plasma sintering，SPS）设备和真空热压设备进行烧结实验，压力设定为35 MPa。采用排水法测试试样烧结密度，使用扫描电子显微镜（scanning electron microscope，SEM）观察试样断口形貌。图1为研究Mo合金烧结行为的实验系统，图中Mo合金样品的直径与模具阴模孔径相同，烧结过程中保持不变，上模冲、下模冲位置固定。烧结开始时微加压力于样品，行程反馈清零，上下模冲压力保持恒定。当系统开始加热时，样品轴向的变化通过上模冲实时表现出来，精度为微米级。
实验主要目的是通过样品在不同温度下的轴向微小变化来反映Mo合金在烧结过程中的行为，这种直观反映Mo合金在高温烧结过程中的变化在行业中尚未发现相关研究信息。直观研究Mo合金烧结变化更加有助于深入掌握Mo合金的烧结规律，为Mo合金产品质量提升和行业进步产生积极的推动作用。
2. 结果与讨论
2.1 Mo–30W合金放电等离子烧结轴向收缩变化
根据石墨模具内径大小确定Mo–30W合金样品直径为20 mm、高度为15 mm。将试样装入模具，包好石墨毡保温，置于上下模冲的中心位置。调整上下模冲距离，使油缸压力稳定在0.3 MPa，将此位置作为试样零点。关闭炉门，抽真空。在真空度达到10 Pa以下时，调节电流，试样开始升温，记录试样轴向伸缩试验数据。
图2为Mo–30W合金试样轴向伸缩和烧结温度随烧结时间的变化趋势。由图可知，温度曲线从室温开始上升，20 min后温度上升到1500 ℃，随后上升速度变缓，基本进入保温阶段。44 min时断电随炉自然降温，68 min时温度已接近室温。在起始3 min，Mo–30W合金试样轴向有微小收缩；随后随温度升高试样开始膨胀，在约13 min、1200 ℃膨胀达到最大值；之后开始收缩，且收缩速度较快；30 min、1600 ℃时试样收缩趋势变缓。44 min、1600 ℃时断电降温开始有明显较大的收缩，温度接近室温时，收缩基本停止。
![]()
图 2 Mo–30W合金试样轴向伸缩和烧结温度随烧结时间的变化Figure 2. Axial shrinkage and sintering temperature of the Mo–30W alloy specimens at different sintering times一般认为粉末冶金的烧结过程按温度–时间关系大致可划分黏结阶段、烧结颈长大及黏塑性流动阶段、闭孔隙球化和缩小阶段等三个界限不十分明显的阶段。黏结阶段属烧结初期，颗粒间原始接触点的原子由于温度升高、振幅加大、扩散加剧，使颗粒间的接触由点扩展到面。在这一阶段中颗粒内的晶粒不发生变化，颗粒外形也基本未变，整个坯体不发生明显的收缩，密度增加极微[4–7]。
Mo–30W合金属于无限固溶[8]，在1200 ℃之前整个坯体不但没有发生收缩，反而有明显的膨胀现象，轴向膨胀量约为6%左右。这是由于原子温度升高，振幅加大颗粒体积膨胀，反映在宏观就是坯体有明显的膨胀现象。之前坯体在烧结过程中难以进行直接观测，所以不能深入了解坯体烧结时的变化规律。
在1200～1600 ℃为烧结颈长大及黏塑性流动阶段，整个坯体收缩显著，而且收缩速度较快，与理论认识相符。主要是由于孔隙大量消失使坯体迅速收缩。在烧结颈长大及黏塑性流动阶段，原子向颗粒结合面大量迁移使烧结颈长大，颗粒间距缩小，形成连续的孔隙网络；同时由于晶粒长大，晶界越过孔隙移动，被晶界扫过的地方，孔隙大量消失。这一阶段坯体收缩、密度和强度显著增加。
如图2所示，整个坯体在1600 ℃保温一段时间后，收缩趋势变缓，收缩缓慢。相对于原始坯体，试样轴向收缩量约为6%左右，相对于膨胀最大值，试样轴向收缩量可达12%左右。这是因为在闭孔隙球化和缩小阶段，多数孔隙被完全分隔，闭孔数量大为增加，孔隙形状趋近于球形并不断缩小。在这个阶段，整个坯体收缩缓慢，主要是靠小孔的消失和孔隙的减少来实现。在降温开始后，整个坯体又产生一个较大的收缩。在降温阶段，整个坯体已被烧结呈现金属化，具有明显的金属特征所以随着温度的降低会产生较大的收缩。降温完成后，整个烧结体收缩率可达15%以上，这与中频烧结类似合金的收缩率基本相符。
通过实验及分析可以确定，Mo–30W合金样品烧结规律为：在烧结升温开始之时，样品有微小收缩，随后随温度升高，试样开始膨胀；温度升到一定程度（1200 ℃）时，样品膨胀达到最大值，之后开始收缩，且收缩速度较快；随着温度继续升高，样品收缩趋势变缓；随着降温的开始，样品有明显较大的收缩，在温度接近室温时，收缩基本停止。
2.2 Mo–30W合金真空热压烧结轴向收缩变化
图3为Mo–30W合金试样经真空热压烧结后，在烧结温度1600 ℃时，试样轴向伸缩率随时间的变化趋势。当烧结温度一定，随着保温时间的延长，Mo–30W合金样品的收缩率逐渐增大。在保温180 min时，收缩率达到最大值9%，此时样品的烧结完成，对应的相对密度也达最大值89.98%。
![]()
图 3 1600 ℃真空热压烧结的Mo–30W合金试样收缩率随烧结时间的变化Figure 3. Shrinkage of the Mo–30W alloys by vacuum hot pressing sintering at 1600 ℃ at different sintering times真空热压烧结的加热方式为电阻辐射加热，在整个烧结过程中，石墨模具、Mo–30W合金样品及真空热压烧结炉腔体的温度基本一致，石墨模具和Mo–30W合金样品一同收缩，所以上模冲的位移变化并不仅代表Mo–30W合金的位移变化。在放电等离子烧结过程中，烧结的热量主要作用在Mo–30W合金坯料上，整个烧结腔体的温度远低于Mo–30W合金坯料的温度，所以上模冲的位移变化能代表Mo–30W合金的位移变化。
2.3 Mo–30W合金样品烧结质量分析
放电等离子烧结是一种比较特殊的烧结方式，样品的烧结质量对本文提出的Mo–30W合金样品烧结规律是一个重要条件，如果烧结质量不好，其烧结规律也不具备普遍意义，从而失去参考价值。样品的烧结密度是判断烧结质量的关键指标，以下是采用排水法测出的样品烧结后的密度，结果如表1所示。
表 1 Mo–30W合金样品烧结密度Table 1. Sintering density of the Mo–30W alloys烧结方法 压坯密度 / (g·cm−3) 压坯相对密度 / % 烧结密度 / (g·cm−3) 烧结相对密度 / % 放电等离子烧结 8.91 69.70 11.89 93.00 真空热压烧结 8.90 69.62 11.50 89.98 从表1中数据可以看出，Mo–30W合金样品经放电等离子烧结后密度有大幅提高，并且相对密度达到93%，可以判断基本达到烧结状态。Mo–30W合金样品原始高度为15 mm，烧结过程中样品直径受限，基本没有产生变化，降温后样品高度收缩3 mm，收缩率达到20%，相对于实测样品密度升高约25%，两者之间相互吻合。Mo–30W合金经真空热压烧结后，样品相对密度达到89.98%，样品原始高度为15 mm，烧结过程中样品直径受限，基本没有产生变化，降温后样品高度收缩2 mm，收缩率达到13.33%。经对比可发现，经放电等离子烧结Mo–30W合金的相对密度高于经真空热压烧结Mo–30W合金的相对密度。放电等离子烧结与真空热压烧结法均为加压和加热同时进行，但二者加热方式完全不同，真空热压烧结法是采用电阻辐射加热的方式实现烧结，放电等离子烧结是利用直流脉冲电流直接通电烧结的加压烧结方式，通过调节脉冲直流电的大小来控制升温速率和烧结温度。直流脉冲电流的主要作用是产生高温等离子体、放电冲击压力、焦耳热和电场扩散作用，同时放电效应能够清除粉末颗粒表面及内部残留的气体，清洁粉末颗粒表面，提高了颗粒的烧结能力[9–12]。放电等离子烧结与真空热压烧结相比，能够在更短的时间内获得高致密的材料。
图4为Mo–30W合金样品经放电等离子烧结和真空热压烧结后的扫描电子显微形貌，从图中可以看出，经放电等离子烧结的样品虽然存在较多的孔洞，但晶粒间界线清晰、平直，与正常Mo合金烧结微观形貌相似，说明样品已产生金属化，已基本完成烧结过程，晶粒大小约30 μm。样品中孔洞较多是放电等离子烧结特点决定，放电等离子烧结是一种快速烧结方式[13–15]，升温速度快，烧结时间较短，晶体内孔洞虽然已经产生了圆化、迁移、融合，但还没有完全收缩消除，这也印证了所测样品相对密度只有93%的结果。经真空热压烧结的样品晶粒之间结合较紧密，晶界处存在孔洞，晶粒大小约50 μm。
![]()
图 4 放电等离子烧结（a）和真空热压烧结（b）Mo–30W合金扫描电子显微形貌Figure 4. SEM images of the Mo–30W alloys by SPS (a) and vacuum hot pressing sintering (b)通过对Mo–30W合金样品的密度和形貌的分析，发现采用放电等离子烧结方法，Mo–30W合金样品产生明显收缩，完成了基本的烧结行为，具备粉末冶金烧结过程的全部特点。随后对纯Mo、Mo–Cu合金、MoS2等不同的样品进行测试发现，不论是纯金属还是合金，或者是非金属都具有相似的烧结行为，这说明本文所探究的粉末冶金烧结行为具有普遍的适用性。
3. 结论
（1）采用放电等离子烧结制备Mo–30W合金时，在烧结初期，1200 ℃之前坯体不但没有收缩，反而有较为明显的膨胀现象，膨胀最大可达6%。
（2）采用放电等离子烧结制备Mo–30W合金时，Mo–30W合金样品粉末冶金烧结基本规律为：在烧结升温开始时，样品有微小收缩，并随温度升高试样开始膨胀；温度升到一定程度（如1200 ℃）时，样品膨胀达到最大值，随后开始收缩，且收缩速度较快；随着温度继续升高，样品收缩趋势变缓；随着降温的开始，样品有明显较大的收缩，当温度接近室温时，收缩基本停止。
（3）使用放电等离子烧结设备可以对Mo–30W合金样品进行烧结，其相对密度可达到93%，基本完成烧结。
（4）在直观反映Mo–30W合金烧结过程中的收缩变化规律方面，放电等离子烧结优于真空热压烧结。
-
![]()
图 3 单相气体流场速度分布（a）和流场内速度方向（b）
Figure 3. Velocity distribution of the single-phase gas vector field (a) and the velocity direction in the vector field (b)
![]()
图 5 不同雾化压力下雾化流场中心线上压力变化曲线
Figure 5. Static pressure curves at the different atomization pressures
![]()
图 7 一次雾化过程中不同雾化气压下熔滴尺寸：（a）7 MPa；（b）8 MPa；（c）9 MPa
Figure 7. Droplet size at the different atomization pressures during the primary atomization simulation: (a) 7 MPa; (b) 8 MPa; (c) 9 MPa
![]()
图 9 二次雾化后的颗粒尺寸分布：（a）7 MPa；（b）8 MPa；（c）9 MPa；（d）累积分布曲线
Figure 9. Particle size distribution obtained by the secondary atomization simulation: (a) 7 MPa; (b) 8 MPa; (c) 9 MPa; (d) cumulative distribution curves
![]()
图 10 不同雾化气压下真空感应熔炼气体雾化法制备GH3536颗粒扫描电子显微形貌：（a）7 MPa；（b）8 MPa；（c）9 MPa
Figure 10. SEM images of the GH3536 alloy powders prepared by VIGA at the different atomization pressures: (a) 7 MPa; (b) 8 MPa; (c) 9 MPa
![]()
图 11 不同雾化气压下粉末粒径分布：（a）7 MPa；（b）8 MPa；（c）9 MPa；（d）累积分布曲线
Figure 11. Particle size distribution at the different atomization pressures: (a) 7 MPa; (b) 8 MPa; (c) 9 MPa; (d) cumulative distribution curves
![]()
图 12 不同雾化气压下GH3536粉末流动性和松装密度
Figure 12. Flowability and apparent density of the GH3536 powders at the different atomization pressures
表 1 真空感应熔炼气体雾化过程模拟中氩气和GH3536合金物理性质[21]
Table 1 Physical properties of the argon and GH3536 superalloys in VIGA process simulation[21]
材料 密度 / (kg·m−3) 比热容 / (J·kg−1·K−1) 热导率 / (W·m−1·K−1) 黏度 / (kg·m−1·s−1) 温度 / K 氩气 1.66 520.64 0.02 2.13×10−5 300 GH3536 7280.00 677.00 29.00 5.50×10−3 1780 
下载: 导出CSV
表 2 不同雾化气压下真空感应熔炼气体雾化制备粉末和数值模拟粉末中位粒径
Table 2 Experimental and simulation data of the median particle size for the GH3536 superalloy powders by VIGA
雾化气压 / MPa 模拟中值粒径 / μm 实验中值粒径 / μm 7 42.53 41.48 8 38.36 36.88 9 34.88 32.63
下载: 导出CSV
-
[1] Liu L, Meng J, Liu J L, et al. Influence of Re on low-cycle fatigue behaviors of single crystal superalloys at intermediate temperature. J Mater Sci Technol, 2019, 35(9): 1917 DOI: 10.1016/j.jmst.2019.05.026
[2] Hou G C, Xie J, Yu J J, et al. Room temperature tensile behaviour of K640S Co-based superalloy. Mater Sci Technol, 2019, 35(5): 350
[3] Ni M, Chen C, Wang X J, et al. Anisotropic tensile behavior of in situ precipitation strengthened Inconel 718 fabricated by additive manufacturing. Mater Sci Eng A, 2017, 701(7): 344
[4] Mireles J, Kim H, Lee H, et al. Development of a fused deposition modeling system for low temperature metal alloys. J Electron Packag, 2013, 13(5): 18
[5] 孙晓峰, 宋巍, 梁静静, 等. 激光增材制造高温合金材料与工艺研究进展. 金属学报, 2021, 57(11): 1471 DOI: 10.11900/0412.1961.2021.00371 Sun X F, Song W, Liang J J, et al. Research and development in materials and processes of superalloy fabricated by laser additive manufacturing. Acta Metall Sinica, 2021, 57(11): 1471 DOI: 10.11900/0412.1961.2021.00371
[6] Tang L, Liang J J, Cui C Y, et al. Influence of Co content on the microstructures and mechanical properties of a Ni−Co base superalloy made by specific additive manufacturing process. Mater Sci Eng A, 2020, 786(1): 139438
[7] 郑明月. 气雾化法制备增材制造用钛合金粉末研究[学位论文]. 北京: 北京科技大学, 2019 Zheng M Y. Gas Atomization Technology Research of Titanium Alloy Powders for Additive Manufacturing [Dissertation]. Beijing: University of Science and Technology Beijing, 2019
[8] 雷囡芝. 等离子旋转电极雾化法制备球形金属粉末的工艺及性能研究[学位论文]. 西安: 西安理工大学, 2019 Lei N Z. Study on Process and Properties of Spherical Metal Powder Prepared by Plasma Rotating Electrode Process [Dissertation]. Xi’an: Xi’an University of Technology, 2019
[9] 张强, 郑亮, 许文勇, 等. 氩气雾化镍基粉末高温合金及粉末特性研究进展. 粉末冶金技术, 2022, 40(5): 387 Zhang Q, Zheng L, Xu W Y, et al. Research progress on argon atomized nickel-based powder metallurgy superalloys and powder characteristics. Powder Metall Technol, 2022, 40(5): 387
[10] Antipas. Review of gas atomisation and spray forming phenomenology. Powder Metall, 2013, 56(4): 317 DOI: 10.1179/1743290113Y.0000000057
[11] Zeoli N, Gu S. Numerical modelling of droplet break-up for gas atomisation. Comput Mater Sci, 2006, 38(2): 282 DOI: 10.1016/j.commatsci.2006.02.012
[12] Wei M W, Chen S Y, Sun M, et al. Atomization simulation and preparation of 24CrNiMoY alloy steel powder using VIGA technology at high gas pressure. Powder Technol, 2020, 367: 724 DOI: 10.1016/j.powtec.2020.04.030
[13] 张建文, 杨玉芳, 孙亚楠, 等. 液气组合雾化过程的多相流动研究. 粉末冶金技术, 2012, 30(6): 403 DOI: 10.19591/j.cnki.cn11-1974/tf.2012.06.001 Zhang J W, Yang Y F, Sun Y N, et al. Multiphase fluid flow in an atomization process by combined liquid and gas flows. Powder Metall Technol, 2012, 30(6): 403 DOI: 10.19591/j.cnki.cn11-1974/tf.2012.06.001
[14] 夏敏, 汪鹏, 张晓虎, 等. 电极感应熔化气雾化制粉技术中非限制式喷嘴雾化过程模拟. 物理学报, 2018, 67(17): 41 Xia M, Wang P, Zhang X H, et al. Computational fluid dynamic investigation of the primary and secondary atomization of the free-fall atomizer in electrode induction melting gas atomization process. Acta Phys Sinica, 2018, 67(17): 41
[15] 郭快快, 陈进, 刘常升, 等. 数值模拟喷射夹角对VIGA制粉雾化过程的影响. 东北大学学报(自然科学版), 2020, 41(5): 729 Guo K K, Chen J, Liu C S, et al. Numerical simulation of the intersection angle influence on atomization process of powders produced by VIGA. J Northeast Univ Nat Sci, 2020, 41(5): 729
[16] Thompson J, Hassan O, Rolland S, et al. The identification of an accurate simulation approach to predict the effect of operational parameters on the particle size distribution (PSD) of powders produced by an industrial close-coupled gas atomiser. Powder Technol, 2016, 291: 75 DOI: 10.1016/j.powtec.2015.12.001
[17] Zhao W, Cao F, Ning Z, et al. A computational fluid dynamics (CFD) investigation of the flow field and the primary atomization of the close coupled atomizer. Comput Chem Eng, 2012, 40(11): 58
[18] Aydin O, Unal R. Experimental and numerical modeling of the gas atomization nozzle for gas flow behavior. Comput Fluids, 2010, 42(1): 37
[19] Kim D, Kim Y, Lee H, et al. Gas atomization parametric study on the VIGA-CC based synthesis of titanium powder. Arch Metall Mater, 2020, 65(3): 997
[20] Shi Y T, Lu W Y, Sun W H, et al. Impact of gas pressure on particle feature in Fe-based amorphous alloy powders via gas atomization: Simulation and experiment. J Mater Sci Technol, 2022, 105: 203 DOI: 10.1016/j.jmst.2021.06.075
[21] Mills K. Recommended Values of Thermophysical Properties for Selected Commercial Alloys. Cambridge: Woodhead Publishing Ltd and ASM International, 2002
[22] Ting J, Anderson E. A computational fluid dynamics (CFD) investigation of the wake closure phenomenon. Mater Sci Eng A, 2004, 379(1): 264
-
期刊类型引用(1)
1. 陈昆昆，孟晗琪，杨阳. 致密铼粒的制备研究. 广州化工. 2024(17): 34-36 . 
百度学术
其他类型引用(0)
计量
- 文章访问数: 2065
- HTML全文浏览量: 147
- PDF下载量: 81
- 被引次数: 1