Effect of plasma sintering process on the mechanical properties of WC/Cr3C2/La2O3 cutting tool materials
-
摘要:
针对传统硬质合金刀具高速切削过程中粘结相易于磨损等问题，采用放电等离子烧结制备了WC/Cr3C2/La2O3刀具材料，研究了Cr3C2添加量（质量分数，0%～2.00%）和工艺参数（烧结温度
1500 ～1700 ℃，烧结压力15～45 MPa）对刀具材料微观组织和力学性能的影响。结果表明，添加质量分数0.50%的Cr3C2并在1550 ℃和25 MPa条件下烧结，得到的WC/Cr3C2/La2O3刀具材料相对密度、抗弯强度和硬度分别为97.5%、1281.0 MPa和HV2124.3 。随着烧结温度增加，材料的相对密度增加，微观组织逐渐均匀；但过高温度会导致晶粒异常长大，组织分布不均，孔隙增多，综合力学性能下降。随着烧结压力增加，材料晶粒细小，组织更加均匀，力学性能增加；但当压力超过25 MPa后，材料力学性能有所下降。Abstract:To solve the problem of adhesive phase wear for the traditional cemented carbide tools in the high-speed cutting process, the WC/Cr3C2/La2O3 tool materials were prepared by spark plasma sintering (SPS). The effects of Cr3C2 addition amount (mass fraction, 0%~2.00%) and process parameters (sintering temperature
1500 ~1700 ℃ and sintering pressure 15~45 MPa) on the microstructure and mechanical properties of the tool materials were studied. The results show that, the optimum Cr3C2 content is 0.50%, and the WC/Cr3C2/La2O3 cemented carbide sintered at1550 ℃ and 25 MPa has the best comprehensive properties as the relative density, bending strength, and Vickers hardness are 97.5%,1281.0 MPa, and HV2124.3 , respectively. With the increase of sintering temperature, the relative density increases and the microstructure becomes more even for the WC-based tool materials. However, too high temperature leads to the abnormal growth of grains, the uneven distribution of microstructure, more porosity, and the lower mechanical properties. As the sintering pressure increases, the grain size reduces, the microstructure becomes more even, and the mechanical properties increase. While the sintering pressure is above 25 MPa, the mechanical properties of tool materials decrease. -
硬质合金刀具拥有较高强度、硬度和良好的高温耐磨性能，被广泛应用于高速切削、勘探开采、航空航天等重要领域[1‒2]。传统硬质合金刀具在加工过程中因粘结相易于软化和氧化腐蚀，从而导致刀具耐磨性不足、使用寿命明显减少和加工质量下降等问题，限制了其的广泛应用[3‒8]。无粘结相WC基硬质合金既具有传统硬质合金的高强高硬等特点，同时又有高耐磨性、耐腐蚀性和良好抗氧化性能，在难加工材料切削方面优势明显，是近年的研究热点[9‒12]。王永[13]结合热压烧结和热等静压技术在2000 ℃烧结制备了尺寸细小的WC陶瓷，材料硬度为26 GPa，断裂韧性为4.5 MPa·m1/2。Sun等[14]以WO3、W、炭黑作为原始粉末，采用放电等离子烧结技术在烧结温度
1500 ℃原位制备纯WC陶瓷，其硬度高达27.1 GPa。纯WC陶瓷存在烧结难以致密化和晶粒异常长大等缺点，因此许多学者通过优化刀具成分和改进制备技术获得高致密WC硬质合金。Taimatsu等[15]研究了不同晶粒生长抑制剂对WC‒SiC材料力学性能的影响。结果表明，添加少量的Cr3C2能改善其力学性能，材料的硬度高达21 GPa，韧性为7～8 MPa·m1/2。Ren等[16]制备了WC‒La2O3复合材料，结果表明La2O3质量分数为1%时，材料的硬度和抗弯强度分别达到21 GPa和1300 MPa，La2O3可以净化WC晶粒间的晶界，提高结合强度和材料的力学性能。Poetschke等[17]研究了Cr3C2、VC晶粒长大抑制剂对WC基硬质合金材料组织和性能的影响。结果表明，1900 ℃下烧结制备WC‒1%Cr3C2、WC‒1%VC材料的硬度分别为25.9 GPa、26.1 GPa，WC晶粒尺寸明显减小，硬度明显提高，且Cr3C2的综合抑制效果更佳。王彬等[18]利用放电等离子烧结制备了晶须增强相WC/SiCw硬质合金。结果表明，在1800 ℃下烧结，其相对密度为99.0%，维氏硬度为26.0 GPa，断裂韧性为5.0 MPa·m1/2。本文采用Cr3C2和La2O3作晶粒抑制剂，经放电等离子烧结（spark plasma sintering，SPS）制备WC/Cr3C2/La2O3刀具材料，研究Cr3C2质量分数和烧结工艺对材料微观组织和力学性能的影响，优化工艺参数，获得综合力学性能优良的WC基硬质合金刀具材料。1. 实验材料与方法
表1为实验原材料的基本参数。WC/Cr3C2/La2O3刀具材料成分（质量分数）为La2O3 1%、Cr3C2 0～2%、WC 97%～99%。在球料比20:1条件下，用球磨机球磨30 h后得到混合粉末。把装入混合粉末的石墨模具转移到等离子烧结炉中（日本住友石炭，320MKII），升温速率设置为100 ℃/min，预压抽真空后分别在
1500 ～1700 ℃和15～45 MPa下进行烧结，保温10 min，最后在水循环条件下随炉冷却，获得ϕ20 mm×5 mm块体材料。采用排水法测量无粘结相WC/Cr3C2/La2O3刀具材料的相对密度，利用HVS-1000 型维氏硬度计测试其硬度，使用压痕法测试其断裂韧性，并通过三点抗弯法在WHY-7740 型压力试验机上测试其抗弯强度。采用D8-Advance型X射线衍射仪（X-ray diffraction，XRD）分析样品物相，利用FEI-Q45型扫描电镜（scanning electron microscope，SEM）观察其断口形貌。表 1 实验原材料基本性能Table 1. Basic properties of the raw materials材料名称 纯度 粒度 / μm 采购渠道 WC 99.90% 1～5 厦门金鹭硬质合金有限公司 Cr3C2 99.90% 10 厦门金鹭硬质合金有限公司 La2O3 分析纯 3～5 上海国药集团 2. 结果与分析
2.1 Cr3C2质量分数对WC/Cr3C2/La2O3刀具材料微观组织和力学性能的影响
图1（a）为不同Cr3C2质量分数下WC/Cr3C2/La2O3复合粉末X射线衍射图谱。由图可知，复合粉末主要物相为WC。图1（b）为
1550 ℃和45 MPa下制备的烧结体X射线衍射图谱。由图对比可知，烧结前复合粉体的晶体化程度并不高，烧结后刀具材料的WC晶体化程度高，衍射峰尖锐。Cr3C2和La2O3由于含量低而未被检测到，X射线衍射图谱中无Cr3C2和La2O3衍射峰。![]()
图 1 添加不同质量分数Cr3C2的WC/Cr3C2/La2O3刀具材料X射线衍射图谱：（a）复合粉末；（b）烧结样品Figure 1. XRD of the WC/Cr3C2/La2O3 tool materials with different mass fraction of Cr3C2: (a) composite powders; (b) sintered specimens图2为不同Cr3C2质量分数下刀具材料的断口形貌。由图可知，随着Cr3C2质量分数增加，WC晶粒总体上得到细化，在Cr3C2质量分数为0.50%时，晶粒细小且组织分布均匀。Cr3C2质量分数超过0.75%时，材料孔洞较多。在Cr3C2质量分数较低时，微观组织中出现三角棱柱形晶粒，但Cr3C2质量分数超过1.00%时，微观组织分布不均匀，在2.00%时出现粗大WC晶粒，并有微裂纹产生。综合分析可知，Cr3C2质量分数为0.50%较为合适。
![]()
图 2 添加不同质量分数Cr3C2的WC/Cr3C2/La2O3刀具材料断口形貌：（a）0%；（b）0.25%；（c）0.50%；（d）0.75%；（e）1.00%；（f）1.50%；（g）2.00%Figure 2. Fracture morphology of the WC/Cr3C2/La2O3 tool materials with different mass fraction of Cr3C2: (a) 0%; (b) 0.25%; (c) 0.50%; (d) 0.75%; (e) 1.00%; (f) 1.50%; (g) 2.00%图3为在
1550 ℃和45 MPa条件下添加不同质量分数Cr3C2制备的WC基刀具材料力学性能。随着Cr3C2质量分数增加，材料的相对密度先升高后降低，在0.50%时材料相对密度高达99%。Cr3C2质量分数较低时，对WC晶粒长大抑制作用不明显，孔隙较多，相对密度较低；Cr3C2质量分数增加可以抑制WC晶粒长大，改善合金耐腐性能[19]，但材料本身密度随之降低，再加上第二相和孔隙等产生，导致相对密度下降和微观组织分布不均。随Cr3C2质量分数增加，硬度先降低再增加，在0.50%时达到HV2092.3 ，随后硬度降低，总体趋向于水平，这与材料相对密度变化规律大致相同。材料的抗弯强度和断裂韧性总体上呈先上升后降低的趋势，在Cr3C2质量分数为0.50%时，抗弯强度高达1092.0 MPa，最大断裂韧性为8.7 MPa·m1/2。综上所述，材料的综合性能在Cr3C2质量分数为0.50%时最好。![]()
图 3 添加不同质量分数Cr3C2的WC/Cr3C2/La2O3刀具材料相对密度和力学性能：（a）相对密度和维氏硬度；（b）抗弯强度和断裂韧性Figure 3. Relative density and mechanical properties of the WC/Cr3C2/La2O3 tool materials with different mass fraction of Cr3C2: (a) relative density and Vickers hardness; (b) bending strength and fracture toughness2.2 烧结温度对WC/Cr3C2/La2O3样品材料微观组织和力学性能的影响
图4为不同烧结温度下WC/Cr3C2/La2O3刀具材料X射线衍射图谱，主要物相为WC相。在
1550 ℃时衍射峰最为尖锐，晶体化程度较高；在1600 ℃时烧结体衍射峰则较低，这与WC晶粒的生长不均匀有关。图5为不同烧结温度下WC/Cr3C2/La2O3材料的断口形貌。随着烧结温度从1500 ℃增加到1600 ℃，原子扩散加快，颗粒受热膨胀并易于结合和致密化，内部气体加速流动，有助于气体逸出，因而微观组织分布均匀，晶粒细小和孔洞少，三角棱柱形晶粒少。当烧结温度处于1600 ～1700 ℃时，剧烈扩散的原子会导致晶粒异常长大，WC三角棱柱形晶粒增多，组织分布不均匀且出现孔洞。![]()
图 4 不同烧结温度下WC基刀具材料X射线衍射图普Figure 4. XRD of the WC-based tool materials at different sintering temperatures![]()
图 5 不同烧结温度下WC/Cr3C2/La2O3样品材料的断口形貌：（a）1500 ℃；（b）1550 ℃；（c）1600 ℃；（d）1650 ℃；（e）1700 ℃Figure 5. Fracture morphology of the WC/Cr3C2/La2O3 sintered samples at different sintering temperatures: (a)1500 ℃; (b)1550 ℃; (c)1600 ℃; (d)1650 ℃; (e)1700 ℃图6为不同烧结温度下WC/Cr3C2/La2O3刀具材料的相对密度和力学性能。随着烧结温度上升，材料的相对密度先升高后降低，在
1550 ℃时材料相对密度高达99.0%。材料的维氏硬度先上升后下降，在1550 ℃高达2092.3 HV。材料的抗弯强度呈现先上升后降低的趋势，在1550 ℃时，抗弯强度和断裂韧性分别达到1092.0 MPa 和8.7 MPa·m1/2。因此，在烧结温度1550 ℃时材料的综合力学性能较好。![]()
图 6 不同烧结温度下WC/Cr3C2/La2O3烧结体相对密度和力学性能：（a）相对密度和维氏硬度；（b）抗弯强度和断裂韧性Figure 6. Relative density and mechanical properties of the WC/Cr3C2/La2O3 sintered samples at different sintering temperatures: (a) relative density and Vickers hardness; (b) bending strength and toughness2.3 烧结压力对WC/Cr3C2/La2O3刀具材料微观组织和力学性能的影响
图7为不同烧结压力下WC/Cr3C2/La2O3样品材料X射线衍射图谱。由图可知，WC衍射峰尖锐，晶化程度高。在15 MPa时检测到游离碳的存在，这可能与碳的溶解析出有关，也有可能是烧结时原样品上包覆的石墨残留。
![]()
图 7 不同烧结压力下WC基刀具材料X射线衍射图谱Figure 7. XRD of the WC-based tool materials at different sintering pressure图8为不同烧结压力下WC/Cr3C2/La2O3材料的断口形貌。在图8（a）压力较低时，内部物质相互扩散缓慢，微观组织分布不均匀，间隙填充不足，气孔较多，局部晶粒变大。在图8（b）和图8（c）中，晶粒细小，组织分布均匀，孔洞少而小，第二相弥散分布在WC晶粒周围，但在图8（c）中存在微裂纹。在图8（d）中，晶粒尺寸略微增大，孔洞较多。这是由于压力过大，导致颗粒孔隙球化速度加快，晶界的比表面能和体积能减小，驱动晶粒长大[20]。因此，选用25 MPa作为WC/Cr3C2/La2O3刀具材料的烧结压力。
![]()
图 8 不同烧结压力下WC/Cr3C2/La2O3材料的断口形貌：（a）15 MPa；（b）25 MPa；（c）35 MPa；（d）45 MPaFigure 8. Fracture morphology of the WC/Cr3C2/La2O3 sintered materials at different sintering pressures: (a) 15 MPa; (b) 25 MPa; (c) 35 MPa; (d) 45 MPa图9为不同烧结压力下WC/Cr3C2/La2O3刀具材料的相对密度和力学性能。由图9（a）可知，随着烧结压力增加，材料的相对密度呈升高降低再升高的趋势，在25 MPa时材料相对密度为97.5%，45 MPa时达到99.0%。硬度出现先上升再降低变化趋势，在35 MPa时达到最大HV
2253.1 。由图9（b）可知，随着烧结压力增加，抗弯强度呈先上升后降低趋势，在25 MPa时达到最大1281.0 MPa。综合比较可知，烧结压力为25 MPa时合金材料的性能最好，其相对密度为97.5%，硬度HV2124.3 ，抗弯强度为1281.0 MPa，断裂韧性为8.7 MPa·m1/2。![]()
图 9 不同烧结压力下WC/Cr3C2/La2O3烧结体相对密度和力学性能：（a）相对密度和维氏硬度；（b）抗弯强度和断裂韧性Figure 9. Relative density and mechanical properties of the WC/Cr3C2/La2O3 sintered samples at different sintering pressure: (a) relative density and Vickers hardness; (b) bending strength and toughness3. 结论
（1）添加适量Cr3C2有助于抑制WC/Cr3C2/La2O3刀具材料的晶粒生长，促进致密化，过量Cr3C2会降低材料的力学性能。烧结温度的升高会加快内部原子扩散，提升相对密度和力学性能，过高的烧结温度则会导致晶粒异常长大，使性能下降。烧结压力的改变对材料的力学性能影响较小，在超过25 MPa后趋于稳定。
（2）在WC/Cr3C2/La2O3合金刀具材料中，Cr3C2较适合添加量（质量分数）为0.50%。最佳烧结工艺参数为烧结温度
1550 ℃和烧结压力25 MPa。在此烧结条件下制备材料的相对密度、硬度和抗弯强度分别为97.5%、2124.3 HV和1281.0 MPa。材料的微观组织分布均匀，晶粒细小，抑制效果较好。 -
![]()
图 1 添加不同质量分数Cr3C2的WC/Cr3C2/La2O3刀具材料X射线衍射图谱：（a）复合粉末；（b）烧结样品
Figure 1. XRD of the WC/Cr3C2/La2O3 tool materials with different mass fraction of Cr3C2: (a) composite powders; (b) sintered specimens
![]()
图 2 添加不同质量分数Cr3C2的WC/Cr3C2/La2O3刀具材料断口形貌：（a）0%；（b）0.25%；（c）0.50%；（d）0.75%；（e）1.00%；（f）1.50%；（g）2.00%
Figure 2. Fracture morphology of the WC/Cr3C2/La2O3 tool materials with different mass fraction of Cr3C2: (a) 0%; (b) 0.25%; (c) 0.50%; (d) 0.75%; (e) 1.00%; (f) 1.50%; (g) 2.00%
![]()
图 3 添加不同质量分数Cr3C2的WC/Cr3C2/La2O3刀具材料相对密度和力学性能：（a）相对密度和维氏硬度；（b）抗弯强度和断裂韧性
Figure 3. Relative density and mechanical properties of the WC/Cr3C2/La2O3 tool materials with different mass fraction of Cr3C2: (a) relative density and Vickers hardness; (b) bending strength and fracture toughness
![]()
图 4 不同烧结温度下WC基刀具材料X射线衍射图普
Figure 4. XRD of the WC-based tool materials at different sintering temperatures
![]()
图 5 不同烧结温度下WC/Cr3C2/La2O3样品材料的断口形貌：（a）
1500 ℃；（b）1550 ℃；（c）1600 ℃；（d）1650 ℃；（e）1700 ℃Figure 5. Fracture morphology of the WC/Cr3C2/La2O3 sintered samples at different sintering temperatures: (a)
1500 ℃; (b)1550 ℃; (c)1600 ℃; (d)1650 ℃; (e)1700 ℃![]()
图 6 不同烧结温度下WC/Cr3C2/La2O3烧结体相对密度和力学性能：（a）相对密度和维氏硬度；（b）抗弯强度和断裂韧性
Figure 6. Relative density and mechanical properties of the WC/Cr3C2/La2O3 sintered samples at different sintering temperatures: (a) relative density and Vickers hardness; (b) bending strength and toughness
![]()
图 7 不同烧结压力下WC基刀具材料X射线衍射图谱
Figure 7. XRD of the WC-based tool materials at different sintering pressure
![]()
图 8 不同烧结压力下WC/Cr3C2/La2O3材料的断口形貌：（a）15 MPa；（b）25 MPa；（c）35 MPa；（d）45 MPa
Figure 8. Fracture morphology of the WC/Cr3C2/La2O3 sintered materials at different sintering pressures: (a) 15 MPa; (b) 25 MPa; (c) 35 MPa; (d) 45 MPa
![]()
图 9 不同烧结压力下WC/Cr3C2/La2O3烧结体相对密度和力学性能：（a）相对密度和维氏硬度；（b）抗弯强度和断裂韧性
Figure 9. Relative density and mechanical properties of the WC/Cr3C2/La2O3 sintered samples at different sintering pressure: (a) relative density and Vickers hardness; (b) bending strength and toughness
表 1 实验原材料基本性能
Table 1 Basic properties of the raw materials
材料名称 纯度 粒度 / μm 采购渠道 WC 99.90% 1～5 厦门金鹭硬质合金有限公司 Cr3C2 99.90% 10 厦门金鹭硬质合金有限公司 La2O3 分析纯 3～5 上海国药集团 
下载: 导出CSV
-
[1] 龙坚战, 陆必志, 易茂中, 等. 新型粘结相硬质合金的研究进展. 硬质合金, 2015, 32(3): 204 Long J Z, Lu B Z, Yi M Z, et al. Research progress on cemented carbide with novel binders. Cement Carb, 2015, 32(3): 204
[2] 薛艺, 田青超. 硬质合金切削刀具研究进展. 材料导报, 2019, 33(S1): 353 Xue Y, Tian Q C. Research progress on cemented carbide cut tools. Mater Rep, 2019, 33(S1): 353
[3] 董丽丽, 张宁, 王磊, 等. WC‒10Co硬质合金刀具材料超低温处理研究. 稀有金属与硬质合金, 2019, 47(3): 86 Dong L L, Zhang N, Wang L, et al. Study on deep cryogenic treatment of WC‒10Co cemented carbide as cutting tool material. Rare Met Cement Carbi, 2019, 47(3): 86
[4] 刘胤, 王金星, 张德玉, 等. TiAlN涂层硬质合金刀具铣削4J32低膨胀合金的磨损机理分析. 工具技术, 2019, 53(9): 47 DOI: 10.3969/j.issn.1000-7008.2019.09.011 Liu Y, Wang J X, Zhang D Y, et al. Wear mechanism analysis of TiALN coated carbide cutter in milling of 4J32 low expansion alloy. Tool Eng, 2019, 53(9): 47 DOI: 10.3969/j.issn.1000-7008.2019.09.011
[5] 邹芹, 李爽, 李艳国. 无粘结相WC硬质合金的研究进展. 硬质合金, 2021, 38(4): 297 DOI: 10.3969/j.issn.1003-7292.2021.04.010 Zou Q, Li S, Li Y G. Research progress of binderless WC tungsten carbide. Cement Carb, 2021, 38(4): 297 DOI: 10.3969/j.issn.1003-7292.2021.04.010
[6] 郑清艺. 超细WC‒Ni网状结构硬质合金的制备与性能研究[学位论文]. 大连: 大连理工大学, 2017 Zheng Q Y. Study on Preparation and Characterization of Ultrafine WC‒Ni Cellular Cemented Carbide [Dissertation]. Dalian: Dalian University of Technology, 2017
[7] Zhang Z Z, Chen Y B, Zuo L L, et al. The effect of volume fraction of WC particles on wear behavior of in-situ WC/Fe composites by spark plasma sintering. Int J Refract Met Hard Mater, 2017, 69: 196 DOI: 10.1016/j.ijrmhm.2017.08.009
[8] Marek T, Jakob K, Kristjan J, et al. Ferritic chromium steel as binder metal for WC cemented carbides. Int J Refract Met Hard Mater, 2018, 73: 183 DOI: 10.1016/j.ijrmhm.2018.02.010
[9] 胡涛, 胡忠举, 郭世柏, 等. 无粘结相WC基硬质合金刀具材料的研究现状与前景. 工具技术, 2019, 53(2): 7 DOI: 10.3969/j.issn.1000-7008.2019.02.002 Hu T, Hu Z J, Guo S B, et al. Research progress of WC-based cemented carbide cutting tool materials without bonding phase. Tool Eng, 2019, 53(2): 7 DOI: 10.3969/j.issn.1000-7008.2019.02.002
[10] Qu H X, Zhu S G. Two step hot pressing sintering of dense fine grained WC–Al2O3 composites. Ceram Int, 2013, 39(5): 5415 DOI: 10.1016/j.ceramint.2012.12.049
[11] 陈国清, 任媛媛, 付雪松, 等. SiCw对WC‒ZrO2材料微观组织及力学性能的影响. 现代技术陶瓷, 2019, 40(3): 191 Chen G Q, Ren Y Y, Fu X S, et al. Effect of SiCW on the microstructure and mechanical properties of WC‒ZrO2. Adv Ceram, 2019, 40(3): 191
[12] 易正翼. 无粘结相(W, Mo)C/Al2O3/La2O3材料的制备及其微织构摩擦磨损性能研究[学位论文]. 湘潭: 湖南科技大学, 2020 Yi Z Y. Preparation of (W, Mo)C/Al2O3/La2O3 Materials Without Bonding Phase and Its Microtexture Friction and Wear Properties [Dissertation]. Xiangtan: Hunan University of Science and Techology, 2020
[13] 王永. 纯碳化钨的制备工艺与性能[学位论文]. 成都: 西南交通大学, 2014 Wang Y. Preparation and Properties of Pure Tungsten Carbide [Dissertation]. Chengdu: Southwest Jiaotong University, 2014
[14] Sun S K, Zhang G J, Wu W W, et al. Reactive spark plasma sintering of binderless WC ceramics at 1500 ℃. Int J Refract Met Hard Mater, 2014, 43: 42 DOI: 10.1016/j.ijrmhm.2013.10.013
[15] Taimatsu H, Sugiyama S, Komatsu M. Effects of Cr3C2 and V8C7 on the microstructure and mechanical properties of WC‒SiC whisker ceramics. Mater Trans, 2009, 50(10): 2435 DOI: 10.2320/matertrans.M2009169
[16] Ren X Y, Peng Z J, Wang C B, et al. Influence of nano-sized La2O3 addition on the sintering behavior and mechanical properties of WC‒La2O3 composites. Ceram Int, 2015, 41(10): 14811 DOI: 10.1016/j.ceramint.2015.08.002
[17] Poetschke J, Richter V, Holke R. Influence and effectivity of VC and Cr3C2 grain growth inhibitors on sintering of binderless tungsten carbide. Int J Refract Met Hard Mater, 2012, 31: 218 DOI: 10.1016/j.ijrmhm.2011.11.006
[18] 王彬, 陈睿智, 李剑峰, 等. 放电等离子烧结制备无粘结相SiCw/WC硬质合金. 粉末冶金技术, 2023, 41(1): 38 Wang B, Chen R Z, Li J F, et al. Preparation of binderless SiCW/WC cemented carbides by spark plasma sintering. Powder Metallu Technol, 2023, 41(1): 38
[19] 王倩玉, 秦明礼, 吴昊阳, 等. 新型纳米晶硬质合金的研究现状及发展趋势. 粉末冶金技术. 2022, 40(4): 362 Wang Q Y, Qin M L, Wu H Y, et al. Research status and development trend of new nanocrystalline cemented carbides. Powder Metall Technol, 2022, 40(4): 362
[20] 黄丽蓉, 王云, 谢俊杰, 等. 超声振动辅助压制粗晶WC‒10Co硬质合金. 粉末冶金技术. 2023, 41(6): 586 Huang L R, Wang Y, Xie J J, et al. Pressing the coarse-grained WC‒10Co cemented carbide assisted by ultrasonic vibration. Powder Metall Technol, 2023, 41(6): 586
计量
- 文章访问数: 583
- HTML全文浏览量: 18
- PDF下载量: 53