高级检索
席晓丽, 聂祚仁, 邹景霞, 翟立力, 蒋亚宝, 童培云, 左铁镛. 纳米钨粉的制备及其表征[J]. 粉末冶金技术, 2006, 24(5): 327-330. DOI: 10.3321/j.issn:1001-3784.2006.05.002
引用本文: 席晓丽, 聂祚仁, 邹景霞, 翟立力, 蒋亚宝, 童培云, 左铁镛. 纳米钨粉的制备及其表征[J]. 粉末冶金技术, 2006, 24(5): 327-330. DOI: 10.3321/j.issn:1001-3784.2006.05.002
shu
Xi Xiaoli, Nie Zuoren, Zou Jingxia, Zhai Lili, Jiang Yabao, Tong Peiyun, Zuo Tieyong. Preparation and characterization of tungsten nanopowder[J]. Powder Metallurgy Technology, 2006, 24(5): 327-330. DOI: 10.3321/j.issn:1001-3784.2006.05.002
Citation: Xi Xiaoli, Nie Zuoren, Zou Jingxia, Zhai Lili, Jiang Yabao, Tong Peiyun, Zuo Tieyong. Preparation and characterization of tungsten nanopowder[J]. Powder Metallurgy Technology, 2006, 24(5): 327-330. DOI: 10.3321/j.issn:1001-3784.2006.05.002
shu

纳米钨粉的制备及其表征

Preparation and characterization of tungsten nanopowder

    摘要
  • 摘要: 以钨酸和氨水为原料,采用液氮预冻-冷冻干燥-两段还原方法制备获得了30nm的纳米W粉末.并对粉末制备过程中的各阶段产物进行了表征:采用XRD、SEM、FESEM对冻干粉、一次还原粉和二次还原粉的物相组成和形貌进行了分析.结果表明,冻干粉是呈现非晶态的,粉末呈絮状团聚在一起,没有明显的颗粒形貌,表面平滑.一次还原粉末也是呈现非晶态,疏松的海绵体结构.最终产物是晶态的W粉,粒度分布均匀.红外光谱分析结果表明,冻干粉末仍保持Keggin结构;热分析表明,冻干粉分三个阶段失去其吸附水、结晶水、结构水.

     