氧对Fe(Cr,Mo)粉末冶金钢的显微组织与断口形态的影响

Lorenz S.Sigl, Patrice Delarbre, 韩凤麟

Lorenz S.Sigl, Patrice Delarbre, 韩凤麟. 氧对Fe(Cr,Mo)粉末冶金钢的显微组织与断口形态的影响[J]. 粉末冶金技术, 2013, 31(5): 385-391. DOI: 10.3969/j.issn.1001-3784.2013.05.013
引用本文: Lorenz S.Sigl, Patrice Delarbre, 韩凤麟. 氧对Fe(Cr,Mo)粉末冶金钢的显微组织与断口形态的影响[J]. 粉末冶金技术, 2013, 31(5): 385-391. DOI: 10.3969/j.issn.1001-3784.2013.05.013
shu
Impact of oxygen on the microstructure and fracture morphology of Fe(Cr, Mo)-PM steels[J]. Powder Metallurgy Technology, 2013, 31(5): 385-391. DOI: 10.3969/j.issn.1001-3784.2013.05.013
Citation: Impact of oxygen on the microstructure and fracture morphology of Fe(Cr, Mo)-PM steels[J]. Powder Metallurgy Technology, 2013, 31(5): 385-391. DOI: 10.3969/j.issn.1001-3784.2013.05.013
shu

氧对Fe(Cr,Mo)粉末冶金钢的显微组织与断口形态的影响

Impact of oxygen on the microstructure and fracture morphology of Fe(Cr, Mo)-PM steels

摘要

    摘要
  • 摘要: 有一些粉末冶金(Cr,Mo)合金钢是由大量生产的Astaloy CrM粉末(3％ Cr,0.5％ Mo)制造的,并且烧结件具有不同的含氧量.对这些材料的显微组织与断口形态进行了分析.发现,氧一般是以Cr2O3颗粒析出,聚集在沿以前颗粒边界的平面上.这种空间形相(spatial configuration)控制着烧结颈塑性变形时的晶核形成与微小孔隙的间距,因此,含氧量增高时,韧性与疲劳强度都会大大减低.最后表明,用高温烧结可制成兼具高强度与韧性好的粉末冶金(Cr,Mo)合金钢.这是因为高温烧结可将这些材料的含氧量(质量分数)减小到＜0.05％.
    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
    • 资源附件(0)
计量
  • 文章访问数:  149
  • HTML全文浏览量:  35
  • PDF下载量:  12
  • 被引次数: 0
出版历程

目录

摘要
HTML全文
    参考文献(0)
    相关文章
    施引文献
    资源附件(0)

    /

    返回文章
    返回

    网站版权 《粉末冶金技术》编辑部京ICP备13030111号

    本系统由 北京仁和汇智信息技术有限公司 开发  百度统计