增塑挤压法制备不锈钢多孔过滤管

迟煜頔, 汤慧萍, 汪强兵, 荆鹏, 康新婷, 葛渊

迟煜頔, 汤慧萍, 汪强兵, 荆鹏, 康新婷, 葛渊. 增塑挤压法制备不锈钢多孔过滤管[J]. 粉末冶金技术, 2011, 29(1): 34-37.
引用本文: 迟煜頔, 汤慧萍, 汪强兵, 荆鹏, 康新婷, 葛渊. 增塑挤压法制备不锈钢多孔过滤管[J]. 粉末冶金技术, 2011, 29(1): 34-37.
shu
Chi Yudi, Tang Huiping, Wang Qiangbing, Jing Peng, Kang Xinting, Ge Yuan. Preparation of stainless steel porous filter tube by powder extrusion molding and sintering[J]. Powder Metallurgy Technology, 2011, 29(1): 34-37.
Citation: Chi Yudi, Tang Huiping, Wang Qiangbing, Jing Peng, Kang Xinting, Ge Yuan. Preparation of stainless steel porous filter tube by powder extrusion molding and sintering[J]. Powder Metallurgy Technology, 2011, 29(1): 34-37.
shu

增塑挤压法制备不锈钢多孔过滤管

  • 西北有色金属研究院金属多孔材料国家重点实验室,西安,710016

  • 西北有色金属研究院

详细信息

  • 中图分类号: TF12

Preparation of stainless steel porous filter tube by powder extrusion molding and sintering

摘要

    摘要
  • 摘要: 采用316L不锈钢粉末与增塑剂的混合物,用增塑挤压烧结法制备了不锈钢过滤管,研究了烧结温度和时间对挤压管组织结构和性能的影响.结果表明:合适的挤压料配比为8%～14%,挤压力为30～50kN;随烧结温度、时间的提高,挤压管的烧结收缩率和抗拉强度都提高;最大孔径和相对透气系数呈现先增大后降低的趋势;温度的影响大于时间的影响.最佳烧结参数为1100℃及2h,此时多孔体的最大孔径为5.8μm、相对透气系数为30.5 m3/(h·kPa·m2).孔隙度与抗拉强度有密切关系,当孔隙度为32%时,抗拉强度达到136MPa.
    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
    • 资源附件(0)
计量
  • 文章访问数:  211
  • HTML全文浏览量:  29
  • PDF下载量:  12
  • 被引次数: 0
出版历程

目录

摘要
HTML全文
    参考文献(0)
    相关文章
    施引文献
    资源附件(0)

    /

    返回文章
    返回

    网站版权 《粉末冶金技术》编辑部京ICP备13030111号

    本系统由 北京仁和汇智信息技术有限公司 开发  百度统计