CUI Lei, MA Hongqiu, ZHAO Gang, MENG Lingbing, GUAN Lidong, FENG Xuefeng. Preparation of spherical FeSiCr powders by improved combination atomization process[J]. Powder Metallurgy Technology, 2024, 42(5): 481-488. DOI: 10.19591/j.cnki.cn11-1974/tf.2023020007
|
The conventional combined atomization smelting process was improved and optimized in this paper, the powder morphology was improved by enhancing the effect of the primary atomization stage and prolonging the time of droplet spheroidization. Spherical powders with different particle sizes were prepared by the improved combination atomization process and compared with those prepared by the conventional combination atomization. The results show that the powders prepared by the improved atomization process show the characteristics as good morphology, small specific surface area, and low oxygen content. At the same time, the permeability is lower than that of the conventional atomized powders, but the DC bias ability of magnetic core is significantly improved, and the hysteresis loss and eddy current loss are significantly reduced.
| [1] |
李天应, 丁文涛, 耿文斌, 等. 软磁合金粉末特性对金属软磁粉芯的影响. 材料导报, 2018, 32(增刊1): 124
Li T Y, Ding W T, Geng W B, et al. Influence of soft magnetic powder characteristics on the performance of metallic soft magnetic powder core. Mater Rev, 2018, 32(Suppl 1): 124
|
| [2] |
孟令兵, 于海琛, 吕世雅, 等. 水雾化制备FeSiCr软磁粉末磁性能研究. 粉末冶金技术, 2021, 39(4): 345
Meng L B, Yu H S, Lü S Y, et al, Study on magnetic properties of FeSiCr soft magnetic powders prepared by water atomization. Powder Metall Technol, 2021, 39(4): 345
|
| [3] |
Zhao T C, Chen C G, Wu X J, et al. FeSiBCrC amorphous magnetic powder fabricated by gas-water combined atomization. J Alloys Compd, 2021, 857: 157991. DOI: 10.1016/j.jallcom.2020.157991
|
| [4] |
Hibino T, Bitoh T. Ternary Fe‒B‒C and quaternary Fe‒B‒C‒Si amorphous alloys with glass transition and high magnetization. J Alloys Compd, 2017, 707: 82 DOI: 10.1016/j.jallcom.2016.12.060
|
| [5] |
Xu H P, Wang R W, Wei D, et al. Crystallization kinetics and magnetic properties of FeSiCr amorphous alloy powder cores. J Magn Magn Mater, 2015, 385: 326 DOI: 10.1016/j.jmmm.2015.03.038
|
| [6] |
Lagutkin S, Achelis L, Sheikhaliev S, et al. Atomization process for metal powder. Mater Sci Eng A, 2004, 383(1): 1 DOI: 10.1016/j.msea.2004.02.059
|
| [7] |
柏海明, 聂敏, 朱小辉, 等. 粉末形貌及粒度对铁硅磁粉心性能的影响. 磁性材料及器件, 2012, 43(6): 42 DOI: 10.3969/j.issn.1001-3830.2012.06.011
Bai H M, Nie M, Zhu X H, et al. Influence of powder morphology and particle size on the performance of iron silicon magnetic powder core. J Magn Mater Dev, 2012, 43(6): 42 DOI: 10.3969/j.issn.1001-3830.2012.06.011
|
| [8] |
麻洪秋, 贾成厂, 金成海, 等. 急冷水雾化工艺对金属粉末性能的影响. 粉末冶金技术, 2002, 20(6): 346 DOI: 10.3321/j.issn:1001-3784.2002.06.006
Ma H Q, Jia C C, Jin C H, et al. Effects of rapid solidification water atomization process on properties of metal powder. Powder Metall Technol, 2002, 20(6): 346 DOI: 10.3321/j.issn:1001-3784.2002.06.006
|
| [9] |
Korobeinikov I, Perminov A, Dubberstein T, et al. Modification of liquid steel viscosity and surface tension for inert gas atomization of metal powder. Metals, 2021, 11(3): 521 DOI: 10.3390/met11030521
|
| [10] |
司佳佳, 苏晓磊. 超细球形镍粉的制备. 粉末冶金技术, 2021, 39(2): 177
Si J J, Su X L. Preparation of ultrafine spherical nickel powders. Powder Metall Technol, 2021, 39(2): 177
|
| [11] |
赵少阳, 谈萍, 李增峰, 等. 增材制造用球形TiAl合金粉末制备工艺研究. 粉末冶金技术, 2022, 40(6): 488
Zhao S Y, Tan P, Li Z F, et al. Study on preparation technology of spherical TiAl alloy powders used for additive manufacturing. Powder Metall Technol, 2022, 40(6): 488
|
| [12] |
See J B, Johnston G H. Interactions between nitrogen jets and liquid lead and tin streams. Powder Technol, 1978, 21(1): 119 DOI: 10.1016/0032-5910(78)80115-6
|
| [13] |
Nichiporenko O S, Naida Y I. Heat exchange between metal particles and gas in the atomization process. Sov Powder Metall Met Ceram, 1968, 7: 509 DOI: 10.1007/BF00774694
|
| [14] |
尚竹亚. 几种不锈钢材料高温氧化行为的研究[学位论文]. 太原: 太原理工大学, 2012
Shang Z Y, Research on High Temperature Oxidation Behavior of Several Stainless Steels [Dissertation]. Taiyuan: Taiyuan University of Technology, 2012
|
| [15] |
Karlsson H, Nyborg L, Berg S. Surface chemical analysis of prealloyed water atomised steel powder. Powder Metall, 2005, 48(1): 51 DOI: 10.1179/0032589005X37675
|
| [16] |
张昊. FeSiCr软磁粉末的水雾化制备技术研究[学位论文]. 北京: 北京有色金属研究总院, 2018
Zhang H. Preparation of FeSiCr Soft Magnetic Powder by Water Atomization [Dissertation]. Beijing: General Research Institute for Nonferrous Metals, 2018
|
| [17] |
段美琪, 王瑞珍, 曹建春, 等. 合金元素和退火工艺对电磁纯铁矫顽力的影响. 金属热处理, 2020, 45(1): 130
Duan M Q, Wang R Z, Cao J C, et al. Effects of alloying elements and annealing process on coercivity of electromagnetic iron. Heat Treat Met, 2020, 45(1): 130
|
| [18] |
潘旭. 整形处理对Fe‒Si‒B非晶粉芯磁性能的影响[学位论文]. 北京: 北京有色金属研究总院, 2018
Pan X. Effect of Shaping Processing on Properties of Fe‒Si‒B Amorphous Powder and Magnetic Powder Core [Dissertation]. Beijing: General Research Institute for Nonferrous Metals, 2018
|
| [19] |
Geng K J, Xie Y Y, Yan L, et al. Fe‒Si/ZrO2 composites with core-shell structure and excellent magnetic properties prepared by mechanical milling and spark plasma sintering. J Alloys Compd, 2017, 718: 53 DOI: 10.1016/j.jallcom.2017.05.114
|
| [20] |
李杰超. 高频低损耗铁基软磁复合材料的制备及磁特性研究[学位论文]. 郑州: 郑州轻工业大学, 2022
Li J C. Study on Preparation and Magnetic Properties of High Frequency and Low Loss Iron-Based Soft Magnetic Composite [Dissertation]. Zhengzhou: Zhengzhou University of Light Industry, 2022
|
Supported by: Beijing Renhe Information Technology Co., Ltd. 
DownLoad: