Fan Tao, Liu Bowen, Sun Yanrong, Wang Hu, Tang weizhong, Jia Chengchang. Study on Wear Resistance of Al2O3 Particle Reinforced Al Matrix Composites[J]. Powder Metallurgy Technology, 2015, 33(3): 186-189. DOI: 10.3969/j.issn.1001-3784.2015.03.006
Citation: Fan Tao, Liu Bowen, Sun Yanrong, Wang Hu, Tang weizhong, Jia Chengchang. Study on Wear Resistance of Al2O3 Particle Reinforced Al Matrix Composites[J]. Powder Metallurgy Technology, 2015, 33(3): 186-189. DOI: 10.3969/j.issn.1001-3784.2015.03.006
shu

Al2O3颗粒增强铝基复合材料的耐磨性研究

Study on Wear Resistance of Al2O3 Particle Reinforced Al Matrix Composites

    摘要
  • 摘要: 以粒度≤74 μm的Al2O3为增强相,粒度≤30 μm的铝粉为基体,采用粉末冶金法制备了Al2O3颗粒增强铝基复合材料.采用金相显微镜、SEM等分析手段对制备的复合材料进行组织观察,并对其进行耐磨性测试.结果表明,Al2O3含量为10％,烧结温度为660℃,混粉时间为90 min时,相对磨损率最小为0.1684％.随着Al2O3的含量的增加和烧结温度的升高,试样的耐磨性呈现出先升高后降低的趋势,混粉时间对试样的耐磨性影响不明显.

     