高级检索
宋杰光, 徐明晗, 王芳, 李世斌, 纪岗昌, 王志刚, 张泽忠, 胡祯. 共沉淀法制备A1(OH)3-Y(OH)3/ZrB2复合粉体的热力学形成条件研究[J]. 粉末冶金技术, 2012, 30(4): 250-254. DOI: 10.3969/j.issn.1001-3784.2012.04.002
引用本文: 宋杰光, 徐明晗, 王芳, 李世斌, 纪岗昌, 王志刚, 张泽忠, 胡祯. 共沉淀法制备A1(OH)3-Y(OH)3/ZrB2复合粉体的热力学形成条件研究[J]. 粉末冶金技术, 2012, 30(4): 250-254. DOI: 10.3969/j.issn.1001-3784.2012.04.002
shu
Song Jieguang, Xu Minghan, Wang Fang, Li Shibin, Ji Gangchang, Wang Zhigang, Zhang Zezhong, Hu Zhen. Thermodynamics conditions of preparing A1(OH)3-Y(OH) 3/ZrB2 composite powder via the co-precipitation method[J]. Powder Metallurgy Technology, 2012, 30(4): 250-254. DOI: 10.3969/j.issn.1001-3784.2012.04.002
Citation: Song Jieguang, Xu Minghan, Wang Fang, Li Shibin, Ji Gangchang, Wang Zhigang, Zhang Zezhong, Hu Zhen. Thermodynamics conditions of preparing A1(OH)3-Y(OH) 3/ZrB2 composite powder via the co-precipitation method[J]. Powder Metallurgy Technology, 2012, 30(4): 250-254. DOI: 10.3969/j.issn.1001-3784.2012.04.002
shu

共沉淀法制备A1(OH)3-Y(OH)3/ZrB2复合粉体的热力学形成条件研究

Thermodynamics conditions of preparing A1(OH)3-Y(OH) 3/ZrB2 composite powder via the co-precipitation method

    摘要
  • 摘要: 由于ZrB2的独特晶体结构,使其兼有金属和陶瓷的许多优异的物理和化学性能,因此在许多领域得到广泛应用.本文利用共沉淀法制备Al(OH)3-Y(OH)3/ZrB2复合粉体,并研究其形成热力学条件.经过热力学计算并用实验验证得出:ZrB2悬浮液的pH值必须大于8.3,才符合Al3+与Y3+共沉淀所需热力学条件;当ZrB2悬浮液的pH值为9时,Al (OH)3-Y(OH)3/ZrB2复合粉体的壳-核结构最好.在溶液浓度较低的情况下,可以获得具有理想壳-核结构的Al (OH)3-Y(OH)3/ZrB2复合粉体,即c(Al3+) =0.017mol/L,c( Y3+) =0.010mol/L,分别接近于Al( NO3)3和Y(NO3)3浓度的热力学条件计算拟定值,即:0.012 60mol/L和0.007 56mol/L.

     