陈大军, 吴护林, 李忠盛, 张隆平, 付扬帆. 高含量La2O3/Y2O3对钼合金微观组织与性能的影响[J]. 粉末冶金技术, 2016, 34(1): 26-30. DOI: 10.3969/j.issn.1001-3784.2016.01.005
引用本文: 陈大军, 吴护林, 李忠盛, 张隆平, 付扬帆. 高含量La2O3/Y2O3对钼合金微观组织与性能的影响[J]. 粉末冶金技术, 2016, 34(1): 26-30. DOI: 10.3969/j.issn.1001-3784.2016.01.005
shu
Chen Dajun, Wu Hulin, Li Zhongsheng, Zhang Longping, Fu Yangfan. Effects of the high content La2O3/Y2O3 on microstructure and mechanical properties of Mo-alloy[J]. Powder Metallurgy Technology, 2016, 34(1): 26-30. DOI: 10.3969/j.issn.1001-3784.2016.01.005
Citation: Chen Dajun, Wu Hulin, Li Zhongsheng, Zhang Longping, Fu Yangfan. Effects of the high content La2O3/Y2O3 on microstructure and mechanical properties of Mo-alloy[J]. Powder Metallurgy Technology, 2016, 34(1): 26-30. DOI: 10.3969/j.issn.1001-3784.2016.01.005
shu

高含量La2O3/Y2O3对钼合金微观组织与性能的影响

Effects of the high content La2O3/Y2O3 on microstructure and mechanical properties of Mo-alloy

    摘要
  • 摘要: 采用粉末冶金方法制备了不同质量分数La2O3/Y2O3复合稀土氧化物掺杂的钼合金,观察了钼合金物相构成、显微组织和断口形貌,测试了其力学性能.结果表明:掺杂La2O3/Y2O3钼合金的物相组成为La2O3、Y2O3和Mo;锻造态钼合金横截面的晶粒尺寸随La2O3/Y2O3含量增加而减小,锻造态钼合金纵截面的显微组织为明显的纤维状织构组织形态;锻造态Mo(La2O3)3.0(Y2O3)0.5钼合金的横截面断口为韧窝断裂和少量解理断裂,纵截面断口为沿晶脆性断裂;合金抗弯强度和弯曲角随La2O3/Y2O3含量的增加先增加后降低,Mo(La2O3)3.0(Y2O3)0.5钼合金抗弯强度达到1133 MPa,弯曲角达到38°.

     