ZrO2(Y2O3)对燃烧合成A12O3/YSZ自生复合陶瓷显微结构与力学性能的影响

张靖,  赵忠民,  张龙,  叶明惠,  潘传增,  宋亚林,  朱浩

downloadPDF
文章导航 > 粉末冶金技术  > 2008 >  (2): 100-105
张靖, 赵忠民, 张龙, 叶明惠, 潘传增, 宋亚林, 朱浩. ZrO2(Y2O3)对燃烧合成A12O3/YSZ自生复合陶瓷显微结构与力学性能的影响[J]. 粉末冶金技术, 2008, (2): 100-105.
引用本文: 张靖, 赵忠民, 张龙, 叶明惠, 潘传增, 宋亚林, 朱浩. ZrO2(Y2O3)对燃烧合成A12O3/YSZ自生复合陶瓷显微结构与力学性能的影响[J]. 粉末冶金技术, 2008, (2): 100-105.
shu
Zhang Jing, Zhao Zhongmin, Zhang Long, Ye Minghui, Pan Chuanzeng, Song Yalin, Zhu Hao. Influence of ZrO2(Y2O3)on the microstructures and mechanical properties of self-growth A12O3/YSZ eutectic composite ceramics prepared by combustion synthesis[J]. Powder Metallurgy Technology, 2008, (2): 100-105.
Citation: Zhang Jing, Zhao Zhongmin, Zhang Long, Ye Minghui, Pan Chuanzeng, Song Yalin, Zhu Hao. Influence of ZrO2(Y2O3)on the microstructures and mechanical properties of self-growth A12O3/YSZ eutectic composite ceramics prepared by combustion synthesis[J]. Powder Metallurgy Technology, 2008, (2): 100-105.
shu

ZrO2(Y2O3)对燃烧合成A12O3/YSZ自生复合陶瓷显微结构与力学性能的影响

  • 军械工程学院先进材料研究所,石家庄,050003

  • 解放军军械工程学院

基金项目: 国家自然科学基金(50672131)
详细信息

  • 中图分类号: TF12

Influence of ZrO2(Y2O3)on the microstructures and mechanical properties of self-growth A12O3/YSZ eutectic composite ceramics prepared by combustion synthesis

    摘要
  • 摘要: 在铝热剂中引入不同量ZrO2(3Y)微米粉末,以燃烧合成技术,制备出A12O3/10%、17%、21%、27%、33%ZrO2(3Y)系列成分自生复合陶瓷棒材.XRD分析与SEM观察显示:具有亚共晶成分的陶瓷熔体因以离异共晶方式生长,使得凝固后的陶瓷基体主要由α-A12O3片晶、t-ZrO2枝晶或块晶组成;而随ZrO2(3Y)添加量的增多,陶瓷晶体生长方式又由离异共晶向共生共晶生长发生转化,共晶棒晶体积分数增多,使得A12O3/33%ZrO2(3Y)的陶瓷基体以微米、亚微米t-ZrO2纤维镶嵌其上的A12O3共晶棒晶和少量α-A12O3片晶构成.经力学性能测试,系列陶瓷棒材的硬度与断裂韧度随ZrO2(3Y)添加量增多而逐渐升高,陶瓷棒材硬度最高值达15.7GPa,断裂韧度最高可达10MPa·m1/2.
    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  202
  • HTML全文浏览量:  42
  • PDF下载量:  5
  • 被引次数: 0
出版历程

目录

    /

    返回文章
    返回

    网站版权 《粉末冶金技术》编辑部京ICP备13030111号

    本系统由 北京仁和汇智信息技术有限公司开发    百度统计