氩弧熔敷原位自生TiC/Ni60A复合涂层的滑动磨损特性

氩弧熔敷原位自生TiC/Ni60A复合涂层的滑动磨损特性

王振廷, 孟君晟, 赵国刚

文章导航 > 粉末冶金技术 > 2008 > 26(3): 183-186

王振廷, 孟君晟, 赵国刚. 氩弧熔敷原位自生TiC/Ni60A复合涂层的滑动磨损特性[J]. 粉末冶金技术, 2008, 26(3): 183-186.

引用本文:

王振廷, 孟君晟, 赵国刚. 氩弧熔敷原位自生TiC/Ni60A复合涂层的滑动磨损特性[J]. 粉末冶金技术, 2008, 26(3): 183-186.

Wang Zhenting, Meng Junsheng, Zhao Guogang. Sliding wear behaviors of in-situ synthesis TiC/Ni60A composite coatings by argon arc cladding[J]. Powder Metallurgy Technology, 2008, 26(3): 183-186.

Citation:

Wang Zhenting, Meng Junsheng, Zhao Guogang. Sliding wear behaviors of in-situ synthesis TiC/Ni60A composite coatings by argon arc cladding[J]. Powder Metallurgy Technology, 2008, 26(3): 183-186.

王振廷, 孟君晟, 赵国刚. 氩弧熔敷原位自生TiC/Ni60A复合涂层的滑动磨损特性[J]. 粉末冶金技术, 2008, 26(3): 183-186.

引用本文:

王振廷, 孟君晟, 赵国刚. 氩弧熔敷原位自生TiC/Ni60A复合涂层的滑动磨损特性[J]. 粉末冶金技术, 2008, 26(3): 183-186.

Wang Zhenting, Meng Junsheng, Zhao Guogang. Sliding wear behaviors of in-situ synthesis TiC/Ni60A composite coatings by argon arc cladding[J]. Powder Metallurgy Technology, 2008, 26(3): 183-186.

Citation:

Wang Zhenting, Meng Junsheng, Zhao Guogang. Sliding wear behaviors of in-situ synthesis TiC/Ni60A composite coatings by argon arc cladding[J]. Powder Metallurgy Technology, 2008, 26(3): 183-186.

氩弧熔敷原位自生TiC/Ni60A复合涂层的滑动磨损特性

黑龙江科技学院材料科学与工程学院,哈尔滨,150027
黑龙江科技学院

基金项目: 国家自然科学基金(50075085)

中图分类号: TF12
计量
- 文章访问数: 200
- HTML全文浏览量: 46
- PDF下载量: 4
- 被引次数: 0
出版历程

Sliding wear behaviors of in-situ synthesis TiC/Ni60A composite coatings by argon arc cladding

摘要: 利用氩弧熔敷技术,以Ni60A自熔合金粉、钛粉和石墨粉为原料,在16Mn钢表面原位合成了TiC增强Ni基复合材料涂层以提高基体的耐磨性.借助扫描电镜、X射线衍射仪、显微硬度计对复合涂层的组织和性能进行了分析.结果表明:熔敷层与基体呈冶金结合,无裂纹、气孔等缺陷,TiC颗粒弥散分布于熔敷层中;复合涂层有很高的硬度,在室温干滑动磨损试验条件下具有优异的耐磨性能并随着(Ti+C)含量的增加而提高.
- 氩弧熔敷 /
- 原位自生 /
- TiC颗粒 /
- 复合材料 /
- 耐磨性

参考文献(0)

资源附件(0)

WeChat

点击查看大图

计量

文章访问数: 200
HTML全文浏览量: 46
PDF下载量: 4
被引次数: 0

/

下载: 全尺寸图片幻灯片

分享

用微信扫码二维码

分享至好友和朋友圈

返回

网站版权《粉末冶金技术》编辑部京ICP备13030111号

本系统由北京仁和汇智信息技术有限公司开发