气体雾化Al-Zn-Mg-Cu铝合金粉末的形貌及组织性能研究

Microstructure and mechanical properties of Al-Zn-Mg-Cu alloy powders prepared by gas atomization process

    摘要
  • 摘要: 利用氮气雾化法制备了Al-Zn-Mg-Cu合金粉末,通过扫描电镜、光学显微镜和X射线衍射仪对粉末的形貌及组织特征进行了研究;检测了粉末热挤压法制备的合金棒材的力学性能,并对其断口进行了分析.结果表明:随着粉末颗粒尺寸减小,颗粒形状由以长条形为主转变为以近球形为主.同时,显微组织中的枝晶臂间距减小,晶粒细化效果明显;合金以α-Al相为主,还有少量η-MgZn_2平衡相存在.随粉末颗粒尺寸减小基体过饱和度增加,基体相和MgZn_2相衍射峰宽化;粉末粒度减小,挤压合金力学性能提高;挤压合金拉伸断口属于韧性断裂.

     