真空蒸发-冷凝法制备片状CU粉

真空蒸发-冷凝法制备片状CU粉

时圣店, 杨斌

文章导航 > 粉末冶金技术 > 2011 > 29(2): 110-114,119

时圣店, 杨斌. 真空蒸发-冷凝法制备片状CU粉[J]. 粉末冶金技术, 2011, 29(2): 110-114,119.

引用本文:

时圣店, 杨斌. 真空蒸发-冷凝法制备片状CU粉[J]. 粉末冶金技术, 2011, 29(2): 110-114,119.

Shi Shengdian, Yang Bin. Preparation of flake copper powder by the evaporation and condensation in vacuum[J]. Powder Metallurgy Technology, 2011, 29(2): 110-114,119.

Citation:

Shi Shengdian, Yang Bin. Preparation of flake copper powder by the evaporation and condensation in vacuum[J]. Powder Metallurgy Technology, 2011, 29(2): 110-114,119.

时圣店, 杨斌. 真空蒸发-冷凝法制备片状CU粉[J]. 粉末冶金技术, 2011, 29(2): 110-114,119.

引用本文:

时圣店, 杨斌. 真空蒸发-冷凝法制备片状CU粉[J]. 粉末冶金技术, 2011, 29(2): 110-114,119.

Shi Shengdian, Yang Bin. Preparation of flake copper powder by the evaporation and condensation in vacuum[J]. Powder Metallurgy Technology, 2011, 29(2): 110-114,119.

Citation:

Shi Shengdian, Yang Bin. Preparation of flake copper powder by the evaporation and condensation in vacuum[J]. Powder Metallurgy Technology, 2011, 29(2): 110-114,119.

真空蒸发-冷凝法制备片状CU粉

时圣店,
杨斌

昆明理工大学真空冶金国家工程实验室,昆明650093;云南省有色金属真空冶金重点实验室,昆明650093
昆明理工大学

基金项目: 国家自然科学基金-云南联合基金资助项目(u0837604)%高等学校博士学科点专项科研基金(20095314110003)

中图分类号: TB383
计量
- 文章访问数: 126
- HTML全文浏览量: 22
- PDF下载量: 4
- 被引次数: 0
出版历程

Preparation of flake copper powder by the evaporation and condensation in vacuum

摘要: 采用蒸发-冷凝法在真空条件下制备了片状Cu粉,并用激光粒度分析仪(SL)、扫描电镜(SEM)、辉光放电质谱仪(GDMS)和X射线衍射仪(XRD)对片状Cu粉进行表征.结果表明,制备的Cu粉为面心立方结构,表面平整,分散性好,粒径为10～30μm,厚1～2μm.试验考察了蒸发温度、真空度、保温时间和冷凝高度4个因素对片状Cu粉粒径和形貌的影响,发现蒸发温度和真空度对蒸发速率有较大影响;探讨了Cu粉颗粒的形成机制.
- 片状Cu粉 /
- 真空 /
- 蒸发-冷凝法 /
- 形貌表征

参考文献(0)

资源附件(0)

WeChat

点击查看大图

计量

文章访问数: 126
HTML全文浏览量: 22
PDF下载量: 4
被引次数: 0

/

下载: 全尺寸图片幻灯片

分享

用微信扫码二维码

分享至好友和朋友圈

返回

网站版权《粉末冶金技术》编辑部京ICP备13030111号

本系统由北京仁和汇智信息技术有限公司开发