HIP对65WNiCu合金力学性能的影响

HIP对65WNiCu合金力学性能的影响

刘桂荣, 王玲, 裴燕斌, 葛启录

文章导航 > 粉末冶金技术 > 2011 > 29(3): 210-213

刘桂荣, 王玲, 裴燕斌, 葛启录. HIP对65WNiCu合金力学性能的影响[J]. 粉末冶金技术, 2011, 29(3): 210-213.

引用本文:

刘桂荣, 王玲, 裴燕斌, 葛启录. HIP对65WNiCu合金力学性能的影响[J]. 粉末冶金技术, 2011, 29(3): 210-213.

Liu Guirong, Wang Ling, Pei Yanbin, Ge Qilu. Effect of HIP on mechanical properties of 65WNiCu alloys[J]. Powder Metallurgy Technology, 2011, 29(3): 210-213.

Citation:

Liu Guirong, Wang Ling, Pei Yanbin, Ge Qilu. Effect of HIP on mechanical properties of 65WNiCu alloys[J]. Powder Metallurgy Technology, 2011, 29(3): 210-213.

刘桂荣, 王玲, 裴燕斌, 葛启录. HIP对65WNiCu合金力学性能的影响[J]. 粉末冶金技术, 2011, 29(3): 210-213.

引用本文:

刘桂荣, 王玲, 裴燕斌, 葛启录. HIP对65WNiCu合金力学性能的影响[J]. 粉末冶金技术, 2011, 29(3): 210-213.

Liu Guirong, Wang Ling, Pei Yanbin, Ge Qilu. Effect of HIP on mechanical properties of 65WNiCu alloys[J]. Powder Metallurgy Technology, 2011, 29(3): 210-213.

Citation:

Liu Guirong, Wang Ling, Pei Yanbin, Ge Qilu. Effect of HIP on mechanical properties of 65WNiCu alloys[J]. Powder Metallurgy Technology, 2011, 29(3): 210-213.

HIP对65WNiCu合金力学性能的影响

安泰科技股份有限公司，北京100081;钢铁研究总院，北京100081
安泰科技股份有限公司,北京,100081
钢铁研究总院,北京,100081
安泰科技股份有限公司
钢铁研究总院

基金项目: 民口配套项目(MKPT-05-132)

中图分类号: TG113.25
计量
- 文章访问数: 94
- HTML全文浏览量: 20
- PDF下载量: 6
- 被引次数: 0
出版历程

Effect of HIP on mechanical properties of 65WNiCu alloys

摘要: 研究了W含量为65％(质量分数)的两种不同Ni与Cu质量比的钨合金,m(Ni):m(Cu)=1(Ⅰ)和m(Ni)∶m(Cu)＜1(Ⅱ),在1050℃下对两种合金进行了热等静压(mP),测试了烧结态和HIP态的密度、拉伸强度以及伸长率并做对比,HIP后两种合金的致密度均约为100％,抗拉强度分别达到750MPa和760MPa,伸长率分别达到18.5％和19.0％.
- HIP /
- W-Ni-Cu合金 /
- 拉伸强度

参考文献(0)

资源附件(0)

WeChat

点击查看大图

计量

文章访问数: 94
HTML全文浏览量: 20
PDF下载量: 6
被引次数: 0

/

下载: 全尺寸图片幻灯片

分享

用微信扫码二维码

分享至好友和朋友圈

返回

网站版权《粉末冶金技术》编辑部京ICP备13030111号

本系统由北京仁和汇智信息技术有限公司开发