Y2O<em>3</em>对YG10超细硬质合金组织和性能的影响

Y2O3对YG10超细硬质合金组织和性能的影响

文章导航 > 粉末冶金技术 > 2015 > 33(1): 8-12

陈慧. Y2O3对YG10超细硬质合金组织和性能的影响[J]. 粉末冶金技术, 2015, 33(1): 8-12.

引用本文:

陈慧. Y2O3对YG10超细硬质合金组织和性能的影响[J]. 粉末冶金技术, 2015, 33(1): 8-12.

Effects of Y2O3 Addition on Microstructure and Properties of Ultra-fine YG10 Cemented Carbides[J]. Powder Metallurgy Technology, 2015, 33(1): 8-12.

Citation:

Effects of Y2O3 Addition on Microstructure and Properties of Ultra-fine YG10 Cemented Carbides[J]. Powder Metallurgy Technology, 2015, 33(1): 8-12.

陈慧. Y2O3对YG10超细硬质合金组织和性能的影响[J]. 粉末冶金技术, 2015, 33(1): 8-12.

引用本文:

陈慧. Y2O3对YG10超细硬质合金组织和性能的影响[J]. 粉末冶金技术, 2015, 33(1): 8-12.

Effects of Y2O3 Addition on Microstructure and Properties of Ultra-fine YG10 Cemented Carbides[J]. Powder Metallurgy Technology, 2015, 33(1): 8-12.

Citation:

Effects of Y2O3 Addition on Microstructure and Properties of Ultra-fine YG10 Cemented Carbides[J]. Powder Metallurgy Technology, 2015, 33(1): 8-12.

Y2O3对YG10超细硬质合金组织和性能的影响

陈慧

重庆文理学院,重庆市高校微纳米材料工程与技术重点实验室,重庆402160
重庆文理学院

基金项目: 重庆市自然科学基金项目(CSTC2012JJYS0003)%重庆市教委项目(KJ131216)重庆文理学院校级项目(Y2012CJ61,R2012CJ17)

计量
- 文章访问数: 174
- HTML全文浏览量: 27
- PDF下载量: 11
- 被引次数: 0
出版历程

Effects of Y2O3 Addition on Microstructure and Properties of Ultra-fine YG10 Cemented Carbides

摘要: 采用高能球磨、真空烧结工艺制备YG10超细硬质合金.研究了Y2O3含量对YG10硬质合金组织结构、磁学性能和机械性能的影响.研究发现:Y2O3的加入可提高合金致密度、硬度和抗弯强度,随着含量的增加,合金的矫顽磁力增加,磁饱和强度略有降低.加入质量分数为0.4％,球磨时间为120 h的Y2O3,YG10超细硬质合金的综合性能最佳,平均粒度为0.3 μm,硬度达到92.4 HRA,抗弯强度达到1 950 MPa.
- 超细硬质合金 /
- 组织和性能 /
- Y2O3

参考文献(0)

资源附件(0)

WeChat

点击查看大图

计量

文章访问数: 174
HTML全文浏览量: 27
PDF下载量: 11
被引次数: 0

/

下载: 全尺寸图片幻灯片

分享

用微信扫码二维码

分享至好友和朋友圈

返回

网站版权《粉末冶金技术》编辑部京ICP备13030111号

本系统由北京仁和汇智信息技术有限公司开发