Effect of Cr on the properties and microstructure of nickel aluminum metal bond
-
摘要: 为改善镍铝基金属结合剂力学性能的不足,采用真空热压烧结法将Cr粉添加到镍铝基金属结合剂中,探究Cr粉含量和烧结温度对镍铝基金属结合剂的力学性能和显微结构的影响。结果表明:Cr起到固溶强化的作用,可以改善镍铝基金属结合剂的力学性能。当烧结温度为800℃时,随Cr添加量的增多,结合剂的抗折强度呈先增大后减小的趋势,而洛氏硬度呈现整体增大的趋势。当Cr含量为12mol%时,其综合性能最佳,抗折强度为178MPa,洛氏硬度为104.2HRB,分别较纯镍铝基金属结合剂提高了36.9%和6.8%。
-
关键词:
Abstract: Vacuum hot pressing sintering was used to add Cr powder to the nickel aluminum metal bond in order to improve the mechanical properties of nickel aluminum metal bond. The effects of Cr powder content and sintering temperature on the mechanical properties and microstructure of the nickel aluminum metal bond were studied. The results show that Cr can solution strengthening and the mechanical properties of nickel aluminum metal bond were improved. As the Cr content increases, the flexural strength of the bond increases first and then decreases with the increase of Cr content, while Rockwell hardness shows an overall increase tendency at 800℃.When Cr content is 12 mol%, the optimal flexural strength and Rockwell hardness are 178 MPa and 104.2 HRB, respectively, which are increased by 36.9% and 6.8%.-
Key words:
- metal bond /
- Cr doping /
- microstructure /
- mechanical property /
- phase composition
点击查看大图
计量
- 文章访问数: 62
- HTML全文浏览量: 17
- PDF下载量: 7
- 被引次数: 0