Guo Shiju, Yang Xia, Chen Bangfeng, Hu Xuesheng, Wei Yanping. High density compaction of stainless steel 316L powders through warm compaction and die wall lubrication[J]. Powder Metallurgy Technology, 2005, 23(6): 403-408. doi: 10.3321/j.issn:1001-3784.2005.06.001
Citation: Guo Shiju, Yang Xia, Chen Bangfeng, Hu Xuesheng, Wei Yanping. High density compaction of stainless steel 316L powders through warm compaction and die wall lubrication[J]. Powder Metallurgy Technology, 2005, 23(6): 403-408. doi: 10.3321/j.issn:1001-3784.2005.06.001
shu

316L不锈钢粉末温压与模壁润滑的高密度成形

doi: 10.3321/j.issn:1001-3784.2005.06.001

  • 北京科技大学粉末冶金研究所,北京,100083

  • 北京科技大学

基金项目: 国家科技攻关项目(2001AA337010)
详细信息

  • 中图分类号: TF1

High density compaction of stainless steel 316L powders through warm compaction and die wall lubrication

    摘要
  • 摘要: 通常在室温下,用内润滑方式难以将316L不锈钢粉末压制成高密度生坯.本工作研究了316L不锈钢粉末的温压、模壁润滑和同时使用温压与模壁润滑的压制过程.研究发现:(1)模壁润滑和温压的同时使用可大幅度提高316L粉末的模压生坯密度.(2)复合润滑剂比单质EBS蜡更适用于有模壁润滑的温压过程,在工业常用的压制压力下,粒度＜74μm的316L粉末的生坯密度超过7.4g/cm3.(3)316L粉末的高密度成形使得粉末颗粒强烈塑性变形,出现了晶粒内的亚晶结构.(4)同时使用模壁润滑和温压得到的高密度生坯在烧结过程不会发生体积膨胀,烧结密度超过7.56 g/cm3.
    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  238
  • HTML全文浏览量:  60
  • PDF下载量:  5
  • 被引次数: 0
出版历程

目录

    /

    返回文章
    返回

    网站版权 《粉末冶金技术》编辑部京ICP备13030111号

    本系统由 北京仁和汇智信息技术有限公司开发    百度统计