高温稀土永磁Sm(Co0.72Fe0.15Cu0.10Zr0.03)7.5的制备和性能

彭龙,  徐光亮,  张明,  王敬东

downloadPDF
文章导航 > 粉末冶金技术  > 2006 >  24(6): 437-440
彭龙, 徐光亮, 张明, 王敬东. 高温稀土永磁Sm(Co0.72Fe0.15Cu0.10Zr0.03)7.5的制备和性能[J]. 粉末冶金技术, 2006, 24(6): 437-440. doi: 10.3321/j.issn:1001-3784.2006.06.009
引用本文: 彭龙, 徐光亮, 张明, 王敬东. 高温稀土永磁Sm(Co0.72Fe0.15Cu0.10Zr0.03)7.5的制备和性能[J]. 粉末冶金技术, 2006, 24(6): 437-440. doi: 10.3321/j.issn:1001-3784.2006.06.009
shu
Peng Long, Xu Guangliang, Zhang Ming, Wang Jingdong. Preparation and properties of high temperature rare earth permanent magnet Sm(Co0.72Fe0.15Cu0.10Zr0.03)7.5[J]. Powder Metallurgy Technology, 2006, 24(6): 437-440. doi: 10.3321/j.issn:1001-3784.2006.06.009
Citation: Peng Long, Xu Guangliang, Zhang Ming, Wang Jingdong. Preparation and properties of high temperature rare earth permanent magnet Sm(Co0.72Fe0.15Cu0.10Zr0.03)7.5[J]. Powder Metallurgy Technology, 2006, 24(6): 437-440. doi: 10.3321/j.issn:1001-3784.2006.06.009
shu

高温稀土永磁Sm(Co0.72Fe0.15Cu0.10Zr0.03)7.5的制备和性能

doi: 10.3321/j.issn:1001-3784.2006.06.009

  • 西南科技大学材料科学与工程学院,四川绵阳,621010

  • 西南应用磁学研究所,四川绵阳,621000

  • 西南科技大学

  • 西南应用磁学研究所

基金项目: 四川省青年基金(02ZQ026-047)%四川省重点项目(02GG009-011)%四川省应用基础研究计划(05JY029-072)
详细信息

  • 中图分类号: TG1

Preparation and properties of high temperature rare earth permanent magnet Sm(Co0.72Fe0.15Cu0.10Zr0.03)7.5

    摘要
  • 摘要: 采用粉末冶金法制备稀土永磁Sm(Co0.72Fe0.15Cu0.10Zr0.03)7.5.结果表明:磁体的密度和各项磁性能都随预烧温度的提高而增加,在1 200℃时获得最大值;提高烧结温度有利于提高磁体的密度,但各项磁性能都在1 215℃获得最大值;提高固溶温度对磁体的密度和Br的影响不大,但Hcb、Hci和(BH)max都在1 185℃时获得最大值.最佳工艺制备的磁体的室温磁性能为:Br=0.94T,Hcb=708.4kA·m,Hci=2276.6kA·m-1,(BH)max=171.9kJ·m-3;500℃时的磁性能为:Br=0.67T,Hcb=429.8kA·m-1,Hci=509.4kA·m-1,(BH)max=81.2kJ·m-3;磁体的温度稳定性良好,内禀矫顽力温度系数β(25～500 ℃)为-0.16%/℃,工作温度达到533℃.
    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  172
  • HTML全文浏览量:  40
  • PDF下载量:  3
  • 被引次数: 0
出版历程

目录

    /

    返回文章
    返回

    网站版权 《粉末冶金技术》编辑部京ICP备13030111号

    本系统由 北京仁和汇智信息技术有限公司开发    百度统计