粘结化铁基粉末的高速压制成形与烧结行为研究

章林,  吕元之,  邵健,  张应波,  刘志伟,  曲选辉

downloadPDF
文章导航 > 粉末冶金技术  > 2012 >  30(1): 57-62
章林, 吕元之, 邵健, 张应波, 刘志伟, 曲选辉. 粘结化铁基粉末的高速压制成形与烧结行为研究[J]. 粉末冶金技术, 2012, 30(1): 57-62. doi: 10.3969/j.issn.1001-3784.2012.01.011
引用本文: 章林, 吕元之, 邵健, 张应波, 刘志伟, 曲选辉. 粘结化铁基粉末的高速压制成形与烧结行为研究[J]. 粉末冶金技术, 2012, 30(1): 57-62. doi: 10.3969/j.issn.1001-3784.2012.01.011
shu
Zhang Lin, Lü Yuanzhi, Shao Jian, Zhang Yingbo, Liu Zhiwei, Qu Xuanhuí. Study on high velocity compaction and sintering behaviour of bonding treated ferrous powder[J]. Powder Metallurgy Technology, 2012, 30(1): 57-62. doi: 10.3969/j.issn.1001-3784.2012.01.011
Citation: Zhang Lin, Lü Yuanzhi, Shao Jian, Zhang Yingbo, Liu Zhiwei, Qu Xuanhuí. Study on high velocity compaction and sintering behaviour of bonding treated ferrous powder[J]. Powder Metallurgy Technology, 2012, 30(1): 57-62. doi: 10.3969/j.issn.1001-3784.2012.01.011
shu

粘结化铁基粉末的高速压制成形与烧结行为研究

doi: 10.3969/j.issn.1001-3784.2012.01.011

  • 北京科技大学新材料技术研究院;新金属材料国家重点实验室,北京100083

  • 莱芜市新艺粉末冶金制品有限公司,山东莱芜,271103

  • 上海汽车粉末冶金有限公司,上海,200072

  • 北京科技大学

  • 莱芜市新艺粉末冶金制品有限公司

  • 上海汽车粉末冶金有限公司

基金项目: 国家973计划资助项目(2011CB606306)%国家高技术发展计划资助项目(2009AA033201)%国家科技支撑计划资助项目(2009BAE74B04)
详细信息

  • 中图分类号: TF124

Study on high velocity compaction and sintering behaviour of bonding treated ferrous powder

    摘要
  • 摘要: 研究了采用粉末改性处理和高速压制相结合的技术制备高密度铁基粉末冶金材料的工艺.所用的粘结化铁基粉末的名义成分(质量分数)为Fe - 1.5Ni -0.5Cu -0.5C；重点研究了压制能量和粉末塑化改性对压坯密度的影响,以及高密度压坯的烧结致密化行为.结果表明:粘结化铁基粉末具有较高的流动性(25.1s/50g)和松装密度(3.2 ～ 3.4g/cm3).未经塑化改性处理的粉末随着压制速度的增加,压坯密度提高缓慢,在8.7m/s高压制速度下,压坯密度为7.37g/cm3.塑化改性处理粉末具有优异的塑性变形能力,压坯密度随着冲击能量的增加而迅速增大,在6.2 ～ 8.7m/s的压制速度范围内,压坯密度为7.07～7.62g/cm3.经过8.7m/s高速压制和1 150℃烧结后,烧结体密度达到7.51 g/cm3,相对密度为96.5％.
    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  186
  • HTML全文浏览量:  28
  • PDF下载量:  8
  • 被引次数: 0
出版历程

目录

    /

    返回文章
    返回

    网站版权 《粉末冶金技术》编辑部京ICP备13030111号

    本系统由 北京仁和汇智信息技术有限公司开发    百度统计