张大勇, 石增敏. 原始成分组成对Ti(C,N)基金属陶瓷烧结性能的影响[J]. 粉末冶金技术, 2012, 30(2): 83-88,97. DOI: 10.3969/j.issn.1001-3784.2012.02.001
引用本文: 张大勇, 石增敏. 原始成分组成对Ti(C,N)基金属陶瓷烧结性能的影响[J]. 粉末冶金技术, 2012, 30(2): 83-88,97. DOI: 10.3969/j.issn.1001-3784.2012.02.001
shu
Zhang Dayong, Shi Zengmin. Effect of chemical composition on the sinterability and mechanical properties of Ti ( C, N) -based cermets[J]. Powder Metallurgy Technology, 2012, 30(2): 83-88,97. DOI: 10.3969/j.issn.1001-3784.2012.02.001
Citation: Zhang Dayong, Shi Zengmin. Effect of chemical composition on the sinterability and mechanical properties of Ti ( C, N) -based cermets[J]. Powder Metallurgy Technology, 2012, 30(2): 83-88,97. DOI: 10.3969/j.issn.1001-3784.2012.02.001
shu

原始成分组成对Ti(C,N)基金属陶瓷烧结性能的影响

Effect of chemical composition on the sinterability and mechanical properties of Ti ( C, N) -based cermets

    摘要
  • 摘要: 采用真空烧结工艺制备了Ti(C,N)基金属陶瓷,研究了原始成分组成对材料烧结特性和力学性能的影响规律.结果表明:保持Mo/(Mo+Ni)为定值,随着硬质相成分的增加,烧结体抗弯强度降低,硬度增加；硬质相成分TiN含量超过一定阈值时,烧结体疏松导致硬度和抗弯强度同时大幅下降；TiN含量保持定值,硬质相成分含量增加,烧结体硬度增加,抗弯强度下降；粘结相成分用Co部分替代Ni,随Co含量的增加,烧结体硬度略有升高的基础上抗弯强度升高.

     