烧结温度对Al-Cu系含油轴承压溃强度、含油率和微观形貌的影响

安旭光,  查五生,  雷宇,  贾永灿,  胡绍磊

downloadPDF
文章导航 > 粉末冶金技术  > 2012 >  30(2): 108-111
安旭光, 查五生, 雷宇, 贾永灿, 胡绍磊. 烧结温度对Al-Cu系含油轴承压溃强度、含油率和微观形貌的影响[J]. 粉末冶金技术, 2012, 30(2): 108-111. doi: 10.3969/j.issn.1001-3784.2012.02.005
引用本文: 安旭光, 查五生, 雷宇, 贾永灿, 胡绍磊. 烧结温度对Al-Cu系含油轴承压溃强度、含油率和微观形貌的影响[J]. 粉末冶金技术, 2012, 30(2): 108-111. doi: 10.3969/j.issn.1001-3784.2012.02.005
shu
An Xuguang, Zha Wusheng, Lei Yu, Jia Yongcan, Hu Shaolei. Effect of sintering temperature on crushing strength, oil content and microstructure of Al-Cu oil bearing[J]. Powder Metallurgy Technology, 2012, 30(2): 108-111. doi: 10.3969/j.issn.1001-3784.2012.02.005
Citation: An Xuguang, Zha Wusheng, Lei Yu, Jia Yongcan, Hu Shaolei. Effect of sintering temperature on crushing strength, oil content and microstructure of Al-Cu oil bearing[J]. Powder Metallurgy Technology, 2012, 30(2): 108-111. doi: 10.3969/j.issn.1001-3784.2012.02.005
shu

烧结温度对Al-Cu系含油轴承压溃强度、含油率和微观形貌的影响

doi: 10.3969/j.issn.1001-3784.2012.02.005

  • 西华大学材料科学与工程学院,成都,610039

  • 西华大学

基金项目: 西华大学创新基金%四川省教育厅重点项目(12ZA158)
详细信息

  • 中图分类号: TF124.5

Effect of sintering temperature on crushing strength, oil content and microstructure of Al-Cu oil bearing

    摘要
  • 摘要: 采用粉末冶金法制备了Al-Cu系含油轴承,研究了烧结温度对Al-Cu系含油轴承的压溃强度、含油率和微观形貌的影响规律及机理.结果表明:烧结温度显著影响Al-Cu系含油轴承的压溃强度、含油率和微观形貌；以540℃、550℃、560℃和570℃真空烧结,烧结坯分别呈现出欠烧结、最佳烧结、过烧结及熔融等不同状态；540℃烧结时,粉末颗粒之间未发生明显的冶金结合,压溃强度较低；高于560℃烧结时,烧结坯发生过烧结及熔融,收缩较大,含油率较低；550℃为最佳烧结温度,在此温度下,烧结坯发生局部熔化,粉末颗粒之间产生良好的冶金结合,微观形貌良好,压溃强度和含油率达到最佳,分别为198MPa和22％.
    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  195
  • HTML全文浏览量:  56
  • PDF下载量:  13
  • 被引次数: 0
出版历程

目录

    /

    返回文章
    返回

    网站版权 《粉末冶金技术》编辑部京ICP备13030111号

    本系统由 北京仁和汇智信息技术有限公司开发    百度统计