高级检索

碳纳米管对低Ni含量Ti(C,N)基金属陶瓷组织与性能的影响

王赛玉,  熊惟皓,  蔺绍江

downloadPDF
文章导航 > 粉末冶金技术  > 2013 >  31(3): 185-190
王赛玉, 熊惟皓, 蔺绍江. 碳纳米管对低Ni含量Ti(C,N)基金属陶瓷组织与性能的影响[J]. 粉末冶金技术, 2013, 31(3): 185-190. doi: 10.3969/j.issn.1001-3784.2013.03.005
引用本文: 王赛玉, 熊惟皓, 蔺绍江. 碳纳米管对低Ni含量Ti(C,N)基金属陶瓷组织与性能的影响[J]. 粉末冶金技术, 2013, 31(3): 185-190. doi: 10.3969/j.issn.1001-3784.2013.03.005
shu
Wang Saiyu, Xiong Weihao, Lin Shaojiang. Effect of carbon nano-tubes on microstructure and properties of Ti(C, N)-based cermets with low Ni content[J]. Powder Metallurgy Technology, 2013, 31(3): 185-190. doi: 10.3969/j.issn.1001-3784.2013.03.005
Citation: Wang Saiyu, Xiong Weihao, Lin Shaojiang. Effect of carbon nano-tubes on microstructure and properties of Ti(C, N)-based cermets with low Ni content[J]. Powder Metallurgy Technology, 2013, 31(3): 185-190. doi: 10.3969/j.issn.1001-3784.2013.03.005
shu

碳纳米管对低Ni含量Ti(C,N)基金属陶瓷组织与性能的影响

doi: 10.3969/j.issn.1001-3784.2013.03.005

  • 湖北理工学院,湖北黄石,435003

  • 华中科技大学材料成形与模具技术国家重点实验室,武汉,430074

  • 湖北理工学院

  • 华中科技大学

基金项目: 湖北省教育厅科学技术研究重点项目(D20093003)

Effect of carbon nano-tubes on microstructure and properties of Ti(C, N)-based cermets with low Ni content

    摘要
  • 摘要: 为了探讨碳纳米管对Ti(C,N)基金属陶瓷性能的影响,添加不同质量分数的碳纳米管作为增强相,采用粉末冶金法制备Ti(C,N)基金属陶瓷材料.通过对材料的显微组织分析,抗弯、硬度等力学性能的测试,研究了碳纳米管含量对Ti(C,N)基金属陶瓷的组织和性能的影响.结果表明:添加碳纳米管后,低Ni含量的金属陶瓷材料的组织结构为典型的芯-壳结构,由黑色芯部、具有明显包覆层的组织,白色芯部、包覆层不明显的组织,粘结相组成；相同烧结温度下,添加≤1％(质量分数)的CNTs时,随碳纳米管含量增多,材料抗弯强度下降；添加Ni包覆的碳纳米管的金属陶瓷材料的性能比添加未做过表面处理的碳纳米管的材料性能好.
    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  177
  • HTML全文浏览量:  40
  • PDF下载量:  7
  • 被引次数: 0
出版历程

目录

    /

    返回文章
    返回

    网站版权 《粉末冶金技术》编辑部京ICP备13030111号

    本系统由 北京仁和汇智信息技术有限公司开发    百度统计