粉末热挤压法制备Mg2B2O5w/6061Al复合材料的组织和力学性能研究

喇培清,  刘国龙,  马国俊,  魏玉鹏,  卢学峰

downloadPDF
文章导航 > 粉末冶金技术  > 2013 >  31(4): 283-290
喇培清, 刘国龙, 马国俊, 魏玉鹏, 卢学峰. 粉末热挤压法制备Mg2B2O5w/6061Al复合材料的组织和力学性能研究[J]. 粉末冶金技术, 2013, 31(4): 283-290. doi: 10.3969/j.issn.1001-3784.2013.04.009
引用本文: 喇培清, 刘国龙, 马国俊, 魏玉鹏, 卢学峰. 粉末热挤压法制备Mg2B2O5w/6061Al复合材料的组织和力学性能研究[J]. 粉末冶金技术, 2013, 31(4): 283-290. doi: 10.3969/j.issn.1001-3784.2013.04.009
shu
La Peiqing, Liu Guolong, Ma Guojun, Wei Yupeng, Lu Xuefeng. Microstructure and mechanical properties of Mg2B2O5w/6061 aluminum alloy matrix composites prepared by hot extrusion[J]. Powder Metallurgy Technology, 2013, 31(4): 283-290. doi: 10.3969/j.issn.1001-3784.2013.04.009
Citation: La Peiqing, Liu Guolong, Ma Guojun, Wei Yupeng, Lu Xuefeng. Microstructure and mechanical properties of Mg2B2O5w/6061 aluminum alloy matrix composites prepared by hot extrusion[J]. Powder Metallurgy Technology, 2013, 31(4): 283-290. doi: 10.3969/j.issn.1001-3784.2013.04.009
shu

粉末热挤压法制备Mg2B2O5w/6061Al复合材料的组织和力学性能研究

doi: 10.3969/j.issn.1001-3784.2013.04.009

  • 兰州理工大学有色金属新材料国家重点实验室,兰州,730050

  • 兰州理工大学有色金属新材料国家重点实验室,兰州730050;青海大学机械工程学院,青海西宁810016

  • 兰州理工大学

基金项目: 国家自然科学基金资助项目(51164022)%青海省科技厅项目(2010H803)

Microstructure and mechanical properties of Mg2B2O5w/6061 aluminum alloy matrix composites prepared by hot extrusion

    摘要
  • 摘要: 采用粉末冶金法制备了含量分别为5％、10％、15％、20％(体积分数,下同)的硼酸镁(Mg2B2O5)晶须增强6061铝基复合材料,利用SEM和EPMA研究了复合材料的微观组织,并测定了其力学性能.结果表明:在复合材料制备过程中Mg2B2O5晶须发生了破碎和折断,Mg2B2O5多以晶须团聚体的形式存在,出现尺寸为10 ～ 25μm的颗粒状增强体；Mg2B2 O5晶须沿挤压方向定向排列,并且定向排列性随晶须含量的增加而减弱；复合材料的抗拉强度随着晶须含量的增加先升高后降低,并在晶须含量为15％时达到最大值191MPa,较基体合金增加16.5％；复合材料的伸长率随晶须含量的增加逐渐下降,当晶须含量为20％时降至最低值6.3％.
    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  149
  • HTML全文浏览量:  34
  • PDF下载量:  6
  • 被引次数: 0
出版历程

目录

    /

    返回文章
    返回

    网站版权 《粉末冶金技术》编辑部京ICP备13030111号

    本系统由 北京仁和汇智信息技术有限公司开发    百度统计