高级检索

Ti(C,N)含量对硬质合金脱β层的形成及其CVD涂层刀具切削性能的影响

邹伶俐

downloadPDF
文章导航 > 粉末冶金技术  > 2015 >  33(2): 116-120
邹伶俐. Ti(C,N)含量对硬质合金脱β层的形成及其CVD涂层刀具切削性能的影响[J]. 粉末冶金技术, 2015, 33(2): 116-120. doi: 10.3969/j.issn.1001-3784.2015.02.007
引用本文: 邹伶俐. Ti(C,N)含量对硬质合金脱β层的形成及其CVD涂层刀具切削性能的影响[J]. 粉末冶金技术, 2015, 33(2): 116-120. doi: 10.3969/j.issn.1001-3784.2015.02.007
shu
Effect of Ti(C, N) content on the formation of gradient cemented carbide and its cutting performance of CVD-coated tools[J]. Powder Metallurgy Technology, 2015, 33(2): 116-120. doi: 10.3969/j.issn.1001-3784.2015.02.007
Citation: Effect of Ti(C, N) content on the formation of gradient cemented carbide and its cutting performance of CVD-coated tools[J]. Powder Metallurgy Technology, 2015, 33(2): 116-120. doi: 10.3969/j.issn.1001-3784.2015.02.007
shu

Ti(C,N)含量对硬质合金脱β层的形成及其CVD涂层刀具切削性能的影响

doi: 10.3969/j.issn.1001-3784.2015.02.007

  • 厦门金鹭特种合金有限公司,厦门,361006

  • 厦门金鹭特种合金有限公司

基金项目: 国家科技重大专项(2014ZX04012012)

Effect of Ti(C, N) content on the formation of gradient cemented carbide and its cutting performance of CVD-coated tools

    摘要
  • 摘要: 本文通过改变原料中Ti(C,N)的含量(0.5％和1.5％)(质量分数,下同),采用一步烧结法制备了WC-Ti(C,N)-NbC-Co脱β层硬质合金,并通过化学气相沉积(CVD)技术制备TiN/MT-TiCN/Al2O3涂层硬质合金,研究的目的是比较Ti(C,N)含量的微量变化对其脱β层硬质合金的微观组织和物理力学性能,以及其涂层刀具车削45#钢的使用寿命的影响.研究结果表明:在两种合金的表层均形成了脱β层,随着Ti(C,N)含量从0.5％增加至1.5％,脱β层厚度从11 μm增加至35 μm,另外,WC平均晶粒度从1.97 μm减少至1.60μm;矫顽磁力HC和维氏硬度HV30提高,合金密度D和断裂韧性KIC降低.涂层刀片的切削试验结果表明:高Ti(C,N)含量制备的涂层刀片的耐磨性略微降低,而抗冲击性能明显提高.
    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  150
  • HTML全文浏览量:  27
  • PDF下载量:  10
  • 被引次数: 0
出版历程

目录

    /

    返回文章
    返回

    网站版权 《粉末冶金技术》编辑部京ICP备13030111号

    本系统由 北京仁和汇智信息技术有限公司开发    百度统计