高级检索

改性SiO2气凝胶微球凝胶注模法制备块体材料

陶艳平,  何方,  张德印,  程娟,  吴菊英,  黄瑜鸿,  邢涛

downloadPDF
文章导航 > 粉末冶金技术  > 2015 >  33(4): 264-269
陶艳平, 何方, 张德印, 程娟, 吴菊英, 黄瑜鸿, 邢涛. 改性SiO2气凝胶微球凝胶注模法制备块体材料[J]. 粉末冶金技术, 2015, 33(4): 264-269. doi: 10.3969/j.issn.1001-3784.2015.04.005
引用本文: 陶艳平, 何方, 张德印, 程娟, 吴菊英, 黄瑜鸿, 邢涛. 改性SiO2气凝胶微球凝胶注模法制备块体材料[J]. 粉末冶金技术, 2015, 33(4): 264-269. doi: 10.3969/j.issn.1001-3784.2015.04.005
shu
Tao Yanping, He Fang, Zhang Deyin, Cheng Juan, Wu Juying, Huang Yuhong, Xing Tao. Preparation of Bulk Material by Gel-casting Method with Modified Silica Aerogel Microspheres[J]. Powder Metallurgy Technology, 2015, 33(4): 264-269. doi: 10.3969/j.issn.1001-3784.2015.04.005
Citation: Tao Yanping, He Fang, Zhang Deyin, Cheng Juan, Wu Juying, Huang Yuhong, Xing Tao. Preparation of Bulk Material by Gel-casting Method with Modified Silica Aerogel Microspheres[J]. Powder Metallurgy Technology, 2015, 33(4): 264-269. doi: 10.3969/j.issn.1001-3784.2015.04.005
shu

改性SiO2气凝胶微球凝胶注模法制备块体材料

doi: 10.3969/j.issn.1001-3784.2015.04.005

  • 河南工业大学,材料科学与工程学院,河南郑州450001

  • 中国工程物理研究院总体工程研究所,四川绵阳,621900

  • 河南工业大学

  • 中国工程物理研究院

基金项目: 国家自然科学基金委员会和中国工程物理研究院联合基金资助项目(NSAF) (11076010)河南工业大学自然科学基础研究重点培育计划(2012JCYJ10)

Preparation of Bulk Material by Gel-casting Method with Modified Silica Aerogel Microspheres

    摘要
  • 摘要: 以改性SiO2气凝胶微球为原料,玻璃粉为烧结剂,采用凝胶注模法制备形状可控的块体材料,考察了改性SiO2气凝胶微球、玻璃粉含量和烧结制度对块体材料的性能、微观形貌及孔结构的影响.结果表明:固相量一定时,低熔点玻璃粉含量越高,块体越致密,强度越高,孔隙率越低;当块体中聚合物含量增多时,加热后块体孔隙相对增加,同时聚合物碳化分解的产物很难排除;降低升温速率,延长保温时间可防止块体开裂,有利于有机物排除.经检测,固相量为70％(质量分数),气凝胶微球与低熔点玻璃粉质量比为1∶1.5时,凝胶注模法制备的块体材料性能最佳:气孔率约为60％,比表面积为169.36 m2/g左右,孔径分布主要在40nm以下,具有明显介孔特征.
    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  235
  • HTML全文浏览量:  57
  • PDF下载量:  8
  • 被引次数: 0
出版历程

目录

    /

    返回文章
    返回

    网站版权 《粉末冶金技术》编辑部京ICP备13030111号

    本系统由 北京仁和汇智信息技术有限公司开发    百度统计