高级检索

MgO和烧结温度对Al2O3陶瓷致密化过程的影响

程诚,  纪箴,  贾成厂,  王召利,  黄小泓,  王聪瑜

downloadPDF
文章导航 > 粉末冶金技术  > 2015 >  33(4): 275-280,284
程诚, 纪箴, 贾成厂, 王召利, 黄小泓, 王聪瑜. MgO和烧结温度对Al2O3陶瓷致密化过程的影响[J]. 粉末冶金技术, 2015, 33(4): 275-280,284. doi: 10.3969/j.issn.1001-3784.2015.04.007
引用本文: 程诚, 纪箴, 贾成厂, 王召利, 黄小泓, 王聪瑜. MgO和烧结温度对Al2O3陶瓷致密化过程的影响[J]. 粉末冶金技术, 2015, 33(4): 275-280,284. doi: 10.3969/j.issn.1001-3784.2015.04.007
shu
Cheng Cheng, Ji Zhen, Jia Chengchang, Wang Zhaoli, Huang Xiaohong, Wang Congyu. Effect of MgO Addition and Sintering Temperatures on Densification Process of Al2O3 Ceramics[J]. Powder Metallurgy Technology, 2015, 33(4): 275-280,284. doi: 10.3969/j.issn.1001-3784.2015.04.007
Citation: Cheng Cheng, Ji Zhen, Jia Chengchang, Wang Zhaoli, Huang Xiaohong, Wang Congyu. Effect of MgO Addition and Sintering Temperatures on Densification Process of Al2O3 Ceramics[J]. Powder Metallurgy Technology, 2015, 33(4): 275-280,284. doi: 10.3969/j.issn.1001-3784.2015.04.007
shu

MgO和烧结温度对Al2O3陶瓷致密化过程的影响

doi: 10.3969/j.issn.1001-3784.2015.04.007

  • 北京科技大学新材料技术研究院,北京,100083

  • 北京科技大学

基金项目: 国际合作项目(2014DFR50570)

Effect of MgO Addition and Sintering Temperatures on Densification Process of Al2O3 Ceramics

    摘要
  • 摘要: 以高纯α-Al2O3粉体为原料,MgO为烧结助剂,采用放电等离子烧结技术(SPS)制备氧化铝陶瓷.研究了MgO添加量和烧结温度对氧化铝陶瓷致密化过程及显微结构的影响,并分析了烧结过程中气孔的扩散与演变.结果表明:添加适量MgO可以降低氧化铝陶瓷的烧结温度,抑制晶粒长大,提高致密度,0.25％(质量分数)是MgO的最佳添加量;随着烧结温度的升高,晶粒逐渐长大,气孔率降低,1 550℃为最佳烧结温度;在此条件下获得的微米晶氧化铝陶瓷,其相对密度达到99.96％,平均晶粒尺寸约为3 μm,且晶粒大小均匀,几乎无异常长大现象.
    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  416
  • HTML全文浏览量:  55
  • PDF下载量:  28
  • 被引次数: 0
出版历程

目录

    /

    返回文章
    返回

    网站版权 《粉末冶金技术》编辑部京ICP备13030111号

    本系统由 北京仁和汇智信息技术有限公司开发    百度统计