高级检索

温压与冷压法制备三元碳化物Cr2AlC坯体的致密化机理

董洪峰,  郭从盛

downloadPDF
文章导航 > 粉末冶金技术  > 2015 >  33(4): 290-295
董洪峰, 郭从盛. 温压与冷压法制备三元碳化物Cr2AlC坯体的致密化机理[J]. 粉末冶金技术, 2015, 33(4): 290-295. doi: 10.3969/j.issn.1001-3784.2015.04.010
引用本文: 董洪峰, 郭从盛. 温压与冷压法制备三元碳化物Cr2AlC坯体的致密化机理[J]. 粉末冶金技术, 2015, 33(4): 290-295. doi: 10.3969/j.issn.1001-3784.2015.04.010
shu
Dong Hongfeng, Guo Congsheng. Densification mechanism of ternary carbidesCr2AlC compact during warm and cold pressing[J]. Powder Metallurgy Technology, 2015, 33(4): 290-295. doi: 10.3969/j.issn.1001-3784.2015.04.010
Citation: Dong Hongfeng, Guo Congsheng. Densification mechanism of ternary carbidesCr2AlC compact during warm and cold pressing[J]. Powder Metallurgy Technology, 2015, 33(4): 290-295. doi: 10.3969/j.issn.1001-3784.2015.04.010
shu

温压与冷压法制备三元碳化物Cr2AlC坯体的致密化机理

doi: 10.3969/j.issn.1001-3784.2015.04.010

  • 陕西理工学院 材料科学与工程学院 汉中723003

  • 陕西理工学院

基金项目: 陕西理工学院校级人才启动项目(SLGQD13(2)-17)%陕西省教育厅专项科研计划项目(14JK1146)

Densification mechanism of ternary carbidesCr2AlC compact during warm and cold pressing

    摘要
  • 摘要: 以球磨Cr、Al、C.(石墨粉)单质粉末制成的混合粉末为原料,分别采用温压和冷压法,在不同压力下制备三元碳化物Cr2Al坯体;利用Kawakita模型建立温压、冷压坯体相对密度和压力间关系,用松装密度测定仪、显微硬度计、OM、SEM、EDS和阿基米德原理表征粉末松装密度、粉末及坯体显微硬度、组织、形貌、分布和坯体密度.结果表明:Kawakita模型拟合方程的精确度高,由于单质粉末经球磨后产生“核壳”结构,改变整体粉末性能,使得球磨粉初始屈服强度值在Cr粉和Al粉之间,且在冷压条件下与模型拟合值相似,而温压Al粉的高温蠕变使得球磨粉初始强度拟合值小于试验值;Al粉在温压和冷压条件下不同的变形性和加工硬化造成的温、冷坯体组织差异均导致了Kawakita模型拟合误差.
    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  121
  • HTML全文浏览量:  26
  • PDF下载量:  7
  • 被引次数: 0
出版历程

目录

    /

    返回文章
    返回

    网站版权 《粉末冶金技术》编辑部京ICP备13030111号

    本系统由 北京仁和汇智信息技术有限公司开发    百度统计