高级检索

冷压烧结法制备Cu-15% Cr2 AlC复合材料工艺研究

孙林,  郭阳,  刘锦云,  金应荣,  鲁云,  庞刚

downloadPDF
文章导航 > 粉末冶金技术  > 2015 >  33(5): 359-364
孙林, 郭阳, 刘锦云, 金应荣, 鲁云, 庞刚. 冷压烧结法制备Cu-15% Cr2 AlC复合材料工艺研究[J]. 粉末冶金技术, 2015, 33(5): 359-364. doi: 10.3969/j.issn.1001-3784.2015.05.009
引用本文: 孙林, 郭阳, 刘锦云, 金应荣, 鲁云, 庞刚. 冷压烧结法制备Cu-15% Cr2 AlC复合材料工艺研究[J]. 粉末冶金技术, 2015, 33(5): 359-364. doi: 10.3969/j.issn.1001-3784.2015.05.009
shu
Sun Lin, Guo Yang, Liu Jinyun, Jin Yingrong, Lu Yun, Pang Gang. The technology research of the Cu-15% Cr2AlC composite prepared by cold-pressing sintering method[J]. Powder Metallurgy Technology, 2015, 33(5): 359-364. doi: 10.3969/j.issn.1001-3784.2015.05.009
Citation: Sun Lin, Guo Yang, Liu Jinyun, Jin Yingrong, Lu Yun, Pang Gang. The technology research of the Cu-15% Cr2AlC composite prepared by cold-pressing sintering method[J]. Powder Metallurgy Technology, 2015, 33(5): 359-364. doi: 10.3969/j.issn.1001-3784.2015.05.009
shu

冷压烧结法制备Cu-15% Cr2 AlC复合材料工艺研究

doi: 10.3969/j.issn.1001-3784.2015.05.009

  • 西华大学材料科学与工程学院,成都,610039

  • 日本千葉大学工学部,日本千葉263-8522

  • 西华大学

  • 日本千葉大学

基金项目: 教育部春晖计划资助项目(Z2010096)%西华大学创新基金项目资助(ycjj201259)

The technology research of the Cu-15% Cr2AlC composite prepared by cold-pressing sintering method

    摘要
  • 摘要: 以自制的高纯Cr2AlC陶瓷粉体和工业纯铜为原料,采用冷压真空烧结技术制备了Cu-15％ Cr2AlC(体积分数)复合材料.通过正交优化试验探讨了压制压力、烧结时间及烧结温度对复合材料相对密度、显微硬度的影响,并对复合材料组织进行扫面电镜分析.结果表明:压制压力对复合材料性能的影响大于烧结时间和烧结温度;随着压制压力的增加,复合材料的相对密度和显微硬度逐渐升高;Cr2AlC颗粒弥散分布于Cu基体中;压制压力为500发MPa,烧结时间为1h,烧结温度为1 000℃,密度为6.91 g/cm3,相对密度达到97.26％,显微硬度为158.93 HV,压溃强度为280 MPa.
    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  246
  • HTML全文浏览量:  58
  • PDF下载量:  9
  • 被引次数: 0
出版历程

目录

    /

    返回文章
    返回

    网站版权 《粉末冶金技术》编辑部京ICP备13030111号

    本系统由 北京仁和汇智信息技术有限公司开发    百度统计