超音速火焰喷涂技术制备的双峰WC-CoCr涂层磨粒磨损特性

王大锋,  张波萍,  贾成厂,  高峰,  于月光,  赵晓琳,  白智辉

downloadPDF
文章导航 > 粉末冶金技术  > 2017 >  35(2): 118-127
王大锋, 张波萍, 贾成厂, 高峰, 于月光, 赵晓琳, 白智辉. 超音速火焰喷涂技术制备的双峰WC-CoCr涂层磨粒磨损特性[J]. 粉末冶金技术, 2017, 35(2): 118-127. doi: 10.3969/j.issn.1001-3784.2017.02.008
引用本文: 王大锋, 张波萍, 贾成厂, 高峰, 于月光, 赵晓琳, 白智辉. 超音速火焰喷涂技术制备的双峰WC-CoCr涂层磨粒磨损特性[J]. 粉末冶金技术, 2017, 35(2): 118-127. doi: 10.3969/j.issn.1001-3784.2017.02.008
shu
WANG Da-feng, ZHANG Bo-ping, JIA Cheng-chang, GAO Feng, YU Yue-guang, ZHAO Xiao-lin, BAI Zhi-hui. Abrasive wear behavior of bimodal WC-CoCr coatings sprayed by high velocity oxy-fuel[J]. Powder Metallurgy Technology, 2017, 35(2): 118-127. doi: 10.3969/j.issn.1001-3784.2017.02.008
Citation: WANG Da-feng, ZHANG Bo-ping, JIA Cheng-chang, GAO Feng, YU Yue-guang, ZHAO Xiao-lin, BAI Zhi-hui. Abrasive wear behavior of bimodal WC-CoCr coatings sprayed by high velocity oxy-fuel[J]. Powder Metallurgy Technology, 2017, 35(2): 118-127. doi: 10.3969/j.issn.1001-3784.2017.02.008
shu

超音速火焰喷涂技术制备的双峰WC-CoCr涂层磨粒磨损特性

doi: 10.3969/j.issn.1001-3784.2017.02.008

  • 北京科技大学材料科学与工程学院,北京,100083

  • 北京矿冶研究总院北矿新材科技有限公司,北京,100160

  • 北京科技大学

基金项目: 国家自然科学基金资助项目(51001117)%北京矿冶研究总院产品开发基金资助项目(YJZ201404)
详细信息

  • 中图分类号: TG174.442

Abrasive wear behavior of bimodal WC-CoCr coatings sprayed by high velocity oxy-fuel

    摘要
  • 摘要: 采用超音速火焰喷涂(high velocity oxy-fuel,HVOF)工艺分别制备了双峰结构和常规结构的WC-CoCr复合涂层.比较了不同结构WC-CoCr涂层的组织结构、显微硬度和断裂韧性;在涂层磨粒磨损实验的基础上,探讨了双峰结构WC-CoCr涂层的磨损机理.结果表明:与常规结构的WC-CoCr复合涂层相比,在由含质量分数30％超细WC粉末制备的双峰结构涂层中,WC在黏结相中溶解最多,断裂韧性最低;由含质量分数50％超细WC粉末制备的双峰结构涂层最致密,显微硬度与断裂韧性最高,耐磨粒磨损性能最优良.
    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  218
  • HTML全文浏览量:  97
  • PDF下载量:  11
  • 被引次数: 0
出版历程

目录

    /

    返回文章
    返回

    网站版权 《粉末冶金技术》编辑部京ICP备13030111号

    本系统由 北京仁和汇智信息技术有限公司开发    百度统计