摘要: 金属粉末注射成形技术可以大批量、低成本地制造高性能异形精密零部件，是当前先进制造技术领域研究的热点之一。本文概述了金属粉末注射成形的工艺，包括粉末制备、粘结剂选取、混料、注射以及后续的脱脂、烧结，介绍了金属粉末注射成形的发展过程、现状及新工艺，深入分析了金属粉末注射成形数值模拟，在此基础上展望了金属粉末注射成形的发展趋势。Abstract: Metal powder injection molding (MIM) can be used to manufacture the high performance precision parts with the special shape in large quantities and low cost, which is regarded as one of the research hotspots in the field of the advanced manufacturing technology. The MIM technology was summarized in this paper, including the powder preparation, the binder selection, the mixing, the injection, and the subsequent debinding and sintering. The development, status, and new technology of MIM were introduced, the numerical simulation of MIM was deeply analyzed, and the development trend of MIM was prospected.
-
Keywords:
- metal powder injection molding /
- powder metallurgy /
- numerical simulation /
- binder
-
硬质合金是以难熔金属碳化物（WC、TiC、TaC等）为硬质相，以过渡金属元素（Co、Ni、Fe等）为粘结相，采用粉末冶金方法制备的复合材料[1‒2]。硬质合金具有高强度、高硬度、高弹性模量、高耐磨损、高耐腐蚀、低热膨胀系数以及高化学稳定性等优点，被广泛地应用于拉丝模具、机械加工、耐磨耐腐蚀零件以及结构部件等领域，被誉为“工业的牙齿”[3‒6]。
自1923年发展至今，硬质合金的材料体系、WC晶粒尺寸、微观结构类型不断得到丰富与发展[7‒9]。均匀结构硬质合金是指内部微观结构均匀一致，具有相同成分、组织及性能的硬质合金[10]。根据WC晶粒大小，均匀结构硬质合金可分为纳米及超细晶硬质合金、超粗晶硬质合金和双晶硬质合金等[11‒18]。均匀结构硬质合金由陶瓷硬质相和金属粘结相组成，陶瓷硬质相的比例提高有助于硬度和耐磨性的改善，但会造成韧性的降低；反之，当金属粘结相的比例提高时，会出现相反的力学性能变化规律。均匀结构硬质合金存在无法同时提高耐磨性和断裂韧性的局限性。表面改性在硬质合金表层空间尺度上实现微观组织的变化，进而对表面力学性能进行优化调控，最终提高硬质合金工具的使用寿命，满足工业应用不断发展的现状。目前主要通过化学表面改性和物理表面改性获得具有实际工程应用价值的非均匀结构硬质合金。近年来，通过渗碳、脱碳、渗氮或脱氮处理等化学表面改性制备梯度硬质合金或通过物理气相沉积和化学气相沉积等物理表面改性制备涂层硬质合金已成为非均匀结构硬质合金的研究热点。基于物理气相沉积或化学气相沉积涂层方法的多层复合涂层硬质合金已实现大规模商业化应用。
本文针对目前传统均匀结构硬质合金耐磨性和断裂韧性难以同时提升的问题提出改进措施，介绍了不同表面改性处理得到非均匀结构硬质合金的制备机理与研究现状，并对今后的研究方向提出了展望。
1. 化学表面改性
随着硬质合金制备技术的发展，非均匀结构硬质合金的制备方法不断丰富，其中表面改性是制备非均匀结构硬质合金的主要方法。化学表面改性是通过原子扩散、液体流动、化学反应等方法实现硬质合金表面物相及微观组织的改变，进而完成合金表面力学性能的定向改善[19‒20]。目前通过化学表面改性制备的常见梯度硬质合金如表1所示。
表 1 基于化学表面改性的常见梯度硬质合金Table 1. Graded cemented carbides based on the chemical surface modification化学表面
改性方法材料体系特点 梯度结构特征 渗碳处理 缺碳 表层贫Co，芯部含η相 正常碳的质量分数 表层贫Co，芯部不含η相 脱碳处理 碳的质量分数偏高 表层富Co 渗氮处理 含Ti、Ta、Nb等元素 表层富含立方相 脱氮处理 含N元素 表层富Co，无立方相 渗碳或脱碳处理实现梯度结构是基于碳的扩散及碳的质量分数对硬质合金微观组织的影响。如WC–Co合金中只出现WC与Co两相，正常碳的质量分数应分布在富碳上限和缺碳下限之间[21]，其中富碳上限为（6.13+0.058×Co质量分数）%，缺碳下限为（6.13‒0.079×Co质量分数）%。当合金中的碳质量分数高于富碳上限时，就会出现游离C，也就是石墨相；当合金中的碳质量分数低于缺碳下限时，就会出现η相[21‒22]。渗氮或脱氮是基于氮的扩散和氮、钛及碳之间的化学反应。氮的扩散实现硬质合金表面物相和微观组织的变化，进而促进梯度结构的形成[19,23]。
1.1 渗碳处理——表层贫Co且芯部含η相梯度结构
表层贫Co且芯部含η相梯度结构的形成机理分析如下[24–27]：通过预烧结制备含η相硬质合金，然后进行渗碳液相烧结，渗入合金表面的C原子与表面η相发生反应，生成WC与Co。随着C原子由表及里的迁移，C原子由外向内与η相反应，这种反应导致η相降低甚至消失，Co相增加。C原子浓度在液相Co中呈现出外高内低的梯度，C原子浓度梯度驱动分解出来的W原子往外表层迁移，并且会与液相Co中的C原子反应生成WC。由W原子往外迁移而引起的体积缺陷也会驱动外表层中的液相Co由表及里迁移，因而导致过渡层的Co含量（质量分数）偏高，进而引起过渡层WC晶粒粗化。
表层贫Co且芯部含η相梯度结构示意图如图1所示[27]，可分为贫Co表层、富Co过渡层和含η相芯部。该梯度硬质合金的Co含量（质量分数）与维氏硬度分布如图2所示[27]。由图可知，表层Co质量分数低于名义Co质量分数，因而表层硬度高；过渡层的Co质量分数高于名义Co质量分数，因而硬度低，韧性高；芯部含有η相，其Co质量分数是合金的名义Co质量分数。
![]()
![]()
1.2 渗碳处理——表层贫Co且芯部不含η相梯度结构
图3所示为WC–10Co硬质合金的W–Co–C相图[28]。关于表层贫Co且芯部不含η相梯度结构形成机理分析如下[28‒29]：当温度在1275～1325 ℃区间时，WC、固相Co和液相Co三相共存，在此温度范围内，当C质量分数在5.34%～5.65%范围内增加时，固相Co含量（质量分数）明显减少，而液相Co含量显著增加。因此，当低C含量且不含η相硬质合金在此温度下进行渗碳处理时，C原子逐渐渗入合金的表层，较高的C含量使合金表层首先出现液相Co，进而液相Co从合金表层向合金内部渗入，当保温一定时间，再冷却降温后，所有Co都会以固相Co的形式存在，最终出现表层贫Co的梯度硬质合金。该梯度结构特征如图4所示[28]，由贫Co的表层和无η相的芯部组成。
![]()
1.3 脱碳处理——富Co表层梯度硬质合金
富Co表层梯度结构形成机理分析[30‒32]如下：从图3可以看出，液相Co含量（质量分数）会随着温度和C含量（质量分数）的变化而改变。脱碳处理即在低碳势的气氛下进行烧结，在1300 ℃以下进行脱碳，硬质合金表层的C含量将会率先降低，表层的Co优先从液相到固相发生转变，当液相Co开始凝固时，表层中溶解在液相Co中的C和W溶解度会下降，进而表层中的C和W向合金的内部迁移，最终形成表层富Co层，类似于一层Co覆盖在硬质合金的表层。脱碳处理得到的富Co表层梯度硬质合金如图5所示[28]。通过脱碳处理制备表层覆盖Co层的梯度硬质合金，对原始合金的C含量（质量分数）要求偏高，否则将会造成合金内部缺C。
![]()
1.4 渗氮处理——表层富含立方相梯度结构
表层富含立方相梯度结构形成机理如图6所示[19,33‒34]：渗氮促使烧结气氛中的N原子扩散到合金表面，N原子与合金表面的C、Ti原子反应生成Ti(C,N)。该反应促使合金内部区域的Ti原子从里往外迁移。合金次表层的Ti原子向外迁移留下空位，此空位需要其他原子予以填充。金属Co原子在硬质合金材料体系中的扩散系数高，尤其是液相烧结，部分Co相为液相，流动性最好，所以Co原子会定向迁移填充由Ti原子迁移所造成的原子空位。此时，合金的次表层Co含量增加，次表层Co的富集促进次表层WC晶粒通过溶解–析出机制长大粗化，所以次表层富Co且WC晶粒粗大。最终形成表层富立方相、次表层富Co且WC晶粒粗大的梯度结构硬质合金。
![]()
1.5 脱氮处理——表层富Co且无立方相梯度结构
表层富Co且无立方相梯度结构形成机理如图7所示[35‒36]：在无氮或贫氮的烧结气氛下，含氮硬质合金在液相烧结过程中合金表面的氮化物发生分解，即合金表面N原子向烧结气氛中扩散，进而造成合金表层的N原子含量降低。此时，合金内部N原子的浓度大于合金表面N原子的浓度，合金内部的N原子向合金表面扩散。由于N与Ti原子之间存在强烈的亲和力，当合金内部的N原子通过粘结相向合金表面扩散时，合金表面的Ti原子也会通过粘结相向内部扩散，同时液相Co会从合金内部流向表层去填补由TiN分解出现的空位，进而导致合金表层的Co含量增加。直至合金表层TiN几乎全部发生分解，进而形成表层富Co且无立方相梯度结构硬质合金。
![]()
目前，部分基于化学表面改性方法的结构功能一体化梯度硬质合金材料已实现商业化且制备机理已基本清晰。但在化学表面改性实现梯度结构过程中，关于化学扩散与热扩散原理还缺乏深入研究，需要深入分析原子的迁移驱动力、动力学方程，建立原子在化学势和温度梯度作用下的迁移模型。
2. 物理表面改性
物理表面改性是通过涂覆的方法在硬质合金表面制备单层或者多层复合涂层，从而赋予硬质合金特定的表面性能[37]。目前，涂层硬质合金主要通过物理气相沉积和化学气相沉积方法在材料表面涂覆高耐磨的难熔金属或非金属化合物[38]。
2.1 涂层方法分析
国内外研究人员对物理气相沉积和化学气相沉积涂层方法进行了广泛且深入的研究，结果表明两种方法分别具有不同优势[38‒41]。对于物理气相沉积，沉积温度低，涂层的沉积温度约200～500 ℃，一般对基体影响不大；对于化学气相沉积，由于沉积温度较高（850～1050 ℃），基体通常参与了薄膜成膜初期的化学反应。物理气相沉积涂层表面光滑，内部产生压应力，有助于抗裂纹扩展。对于化学气相沉积，涂层反应源的制备相对比较容易，涂层与基体结合强度高，涂层附着力强、均匀性好，适合用来给复杂形貌工件镀层。化学气相沉积涂层工业化成本低于物理气相沉积涂层。
2.2 涂层结构设计
由于单一涂层难以满足当前机加工对涂层硬质合金刀具的力学性能要求，涂层成分趋于多元化，涂层结构趋于复合化，涂层微观组织趋于纳米化[38,42]。从目前应用需求分析，机加工对涂层结构的功能性要求越来越高[42]，复合功能涂层结构已取得广泛应用。
瑞典、美国等国家的著名刀具公司都开发有多层结构的涂层硬质合金刀具。如瑞典Sandvik Coromant公司的GC2015牌号刀具具有TiCN–TiN/Al2O3–TiN的三层结构复合涂层，TiCN底层与基体的结合强度高，TiN/Al2O3中间层既耐磨又能抑制裂纹的扩展，TiN表层具有较好的化学稳定性且易于观察刀具的磨损[43]。美国Kennametal Hertel公司的KC9315型刀片上共有三层涂层，底层是Al2O3，中间层是TiCN，表面层是TiN。这种多层复合涂层的性能较单层的TiC、TiN涂层及TiC/TiN双层涂层具有明显性能优势。多层复合涂层的功能分析如图8所示[42]。
物理表面改性方法解决了硬质合金刀具硬度与强度之间的矛盾，已经在数控车床刀具领域取得广泛应用。涂层的性能取决于材料的微观组织结构与化学成分，除了研究涂层材料、涂层制备技术、涂层工艺之外，还需要重点研究涂层材料与硬质合金材料之间化学成分和热膨胀系数的匹配关系。
3. 总结与展望
硬质合金的主要研究方向已经从均匀结构向非均匀结构转变。对于化学表面改性梯度硬质合金，在研究当前梯度硬质合金微观结构及形成机理的基础上，需要完善其热力学、动力学数据，从微观机制上完整解释梯度结构的形成过程，实现准确调控梯度结构形成的重要参数，为功能梯度硬质合金的制备提供更充分的基础理论指导。对于物理表面改性涂层硬质合金，当前研究主要是在均匀结构硬质合金基体上进行涂层结构复合化设计，对硬质合金基体的梯度结构设计在改善涂层与基体结合强度方面具有潜在技术优势，因此，需要对硬质合金基体的非均匀结构设计开展深入研究。
-
![]()
![]()
![]()
表 1 金属粉末注射成形常用材料系列
Table 1 Common material series in MIM
材料系列 合金成分 低合金钢 Fe–2Ni，Fe–8Ni 不锈钢 304L，314L，316L，440A，440C，17-4PH 硬质合金 WC–6Co 重合金 W–Ni–Fe，W–Ni–Cu，W–Cu 工具钢 42CrMo4，M2 钛合金 TiAl，Ti–6Al–4V，TiMo 陶瓷 ZrO2，Si3N4，AlN，Al2O3，SiO2 新型合金 Fe–Al–Si，无Ni奥氏体不锈钢 
下载: 导出CSV
表 2 金属粉末注射成形常用粘结剂体系及其优缺点
Table 2 Common binder systems and the characteristics of MIM
粘结剂体系 优点 缺点 热塑性体系 石蜡基粘结剂熔点低，流动性好，可填充复杂模腔；聚合物基粘结剂强度高，保形性好。 石蜡冷却时体积收缩大，注射时薄壁与厚壁的交界处应力较大；聚合物基粘结剂黏度高，混料难度大 热固性体系 脱脂时间短，可制备较大尺寸零件 注射坯强度低，脱脂不完全，注射料不能重复利用 凝胶水基体系 脱模简单，注射坯强度高，脱脂简单快速，
可生产大尺寸零件粘结剂中的水受热挥发影响注射料黏度，并且水对金属粉末有一定的氧化作用，凝胶化时间长，脱模困难 水溶性体系 绿色环保，不污染环境 注射坯易变形，不适合生产烧结密度高的产品
下载: 导出CSV
-
[1] 高建祥, 卓海宇, 高泽平, 等. 金属粉末注射成形过程计算机模拟技术的现状及发展. 硬质合金, 2006, 23(1): 47 DOI: 10.3969/j.issn.1003-7292.2006.01.012 Gao J X, Zhuo H Y, Gao Z P, et al. Situation and development tendency of MIM computer simulation technology. Cement Carb, 2006, 23(1): 47 DOI: 10.3969/j.issn.1003-7292.2006.01.012
[2] Wiech R E. Manufacture of Parts from Particulate Materials: US Patent, 5613183. 1997-3-18
[3] Wiech R E. Method and Means for Removing Binder from a Green Body: EP Patent, 0032404. 1981-7-22
[4] Rivers R D. Method of Injection Molding Powder Metal Parts: US Patent, 4113480. 1978-9-12
[5] 李云平, 曲选辉, 郑洲顺, 等. 注射成形W–Cu研究现状及产业化发展趋势. 粉末冶金技术, 2003, 21(2): 108 DOI: 10.3321/j.issn:1001-3784.2003.02.008 Li Y P, Qu X H, Zheng Z S, et al. The present state in research and development trend in industrialization of PIM W–Cu composites. Powder Metall Technol, 2003, 21(2): 108 DOI: 10.3321/j.issn:1001-3784.2003.02.008
[6] Hu G X, Zhang L X, Fan Y L, et al. Fabrication of high porous NiTi shape memory alloy by metal injection molding. J Mater Process Technol, 2008, 206(1-3): 395 DOI: 10.1016/j.jmatprotec.2007.12.044
[7] Bose A, German R M. Potential of powder injection molding and hot isostatic pressing of nickel aluminide matrix composites. Ind Heat, 1988, 55(5): 38
[8] Kamal M R, Kenig S. The injection molding of thermoplastics part I: Theoretical model. Polym Eng Sci, 1972, 12(4): 294 DOI: 10.1002/pen.760120408
[9] Kamal M R, Kenig S. The injection molding of thermoplastics part II: Experimental test of the model. Polym Eng Sci, 1972, 12(4): 302 DOI: 10.1002/pen.760120409
[10] Hieber C A, Shen S F. Flow analysis of the non-isothermal two-dimensional filling process in injection molding. Isr J Technol, 1978, 16: 248
[11] Hieber C A, Shen S F. A finite-element/finite-difference simulation of the injection molding process. J Non-Newtonian Fluid Mech, 1980, 7: 1 DOI: 10.1016/0377-0257(80)85012-9
[12] Lacey P M C. Development in the theory of particle mixing. J Appl Chem, 1954, 4(5): 257
[13] 梁叔全, 黄伯云. 粉末注射成形流变学. 长沙: 中南大学出版社, 2000 Liang S Q, Huang B Y. Rheology of Powder Injection Molding. Changsha: Central South University Press, 2000
[14] 尉念伦, 孙世清. 金属注射成形用钴铬钼粉末的制备. 河北工业科技, 2021, 38(1): 1 Yu N L, Sun S Q. Preparation of cobalt-chromium-molybdenum powders for metal injection molding. Hebei J Ind Sci Technol, 2021, 38(1): 1
[15] 贺毅强, 陈志华, 陈志刚, 等. 金属粉末注射成形的原理与发展趋势. 材料科学与工程学报, 2013, 31(2): 317 He Y Q, Chen Z H, Chen Z G, et al. Metal injection molding: principle and development. J Mater Sci Eng, 2013, 31(2): 317
[16] 郝向阳, 盖国胜, 邹欣, 等. 氢化脱氢钛粉末颗粒的整形及其机理研究. 稀有金属材料与工程, 2009, 38(增刊3): 264 Hao X Y, Gai G S, Zou X, et al. Shape modification of HDH Ti powder and its mechanism analysis. Rare Met Mater Eng, 2009, 38(Suppl 3): 264
[17] Mahmud N N, Azam F A A, Ramli M I, et al. Rheological properties of irregular-shaped titanium-hydroxyapatite bimodal powder composite moulded by powder injection moulding. J Mater Res Technol, 2021, 11: 2255 DOI: 10.1016/j.jmrt.2021.02.016
[18] 郭世柏, 曲选辉. 金属注射成形粘结剂的研究进展. 粉末冶金技术, 2004, 22(3): 178 DOI: 10.3321/j.issn:1001-3784.2004.03.012 Guo S B, Qu X H. Research progress in binders used for metal injection molding. Powder Metall Technol, 2004, 22(3): 178 DOI: 10.3321/j.issn:1001-3784.2004.03.012
[19] Muller E, Horowitz D, Egozy A. Polyhydroxyalkanoate Molding Compositions: US Patent, 6071998. 2000-6-6
[20] Hens K F, Kupp D M, Alexander R A, et al. Method and Binder for Use in Powder Molding: US Patent, 5332537. 1994-7-26
[21] Hens S, Van Landuyt J, Bender H, et al. Chemical and structural analysis of etching residue layers in semiconductor devices with energy filtering transmission electron microscopy. Mater Sci Semicond Process, 2001, 4(1-3): 109 DOI: 10.1016/S1369-8001(00)00147-5
[22] 赵小娟, 党新安. 金属粉末注射成形技术及模具的研究现状. 模具技术, 2008(5): 11 DOI: 10.3969/j.issn.1001-4934.2008.05.004 Zhao X J, Dang X A. Research status of metal powder injection molding technology and the mold. Mould Technol, 2008(5): 11 DOI: 10.3969/j.issn.1001-4934.2008.05.004
[23] Kwon T H, Hwang C J, Rhee R E. Numerical simulation of powder injection molding filling process for 3D complicated cavity geometries. Adv Powder Metall Part Mater, 1996, 5: 19
[24] 肖平安, 胡业奇, 刘吉梓, 等. 一种粉末注射成形用梯度负压热脱脂技术: 中国专利, 1974080A. 2007-6-6 Xiao P A, Hu Y Q, Liu J Z, et al. A Gradient Negative Pressure Thermal Degreasing Technology for Powder Injection Molding: China Patent, 1974080A. 2007-6-6
[25] Camargo A, Rodrigues D, Tschiptschin A P. Debinding kinetics of injection molding samples — The effects of the binder melt index flow. Key Eng Mater, 2001, 189-191: 604 DOI: 10.4028/www.scientific.net/KEM.189-191.604
[26] Yang X M, Petcavich R J. Powder and Binder Systems for Use in Metal and Ceramic Powder Injection Molding: US Patent, 6008281. 1999-12-28
[27] 范景莲, 黄伯云, 曲选辉, 等. 液相烧结高比重合金早期固相烧结阶段的致密化机理. 中国有色金属学报, 1998, 8(增刊1): 36 Fan J L, Huang B Y, Qu X H, et al. Densification mechanism of liquid phase sintered tungsten heavy alloy during initial solid state sintering stage. Chin J Nonferrous Met, 1998, 8(Suppl 1): 36
[28] 戴煜, 王利民. 分压控制式真空脱脂烧结一体炉: 中国专利, 2718480Y. 2005-8-17 Dai Y, Wang L M. Partial Pressure Controlled Vacuum Degreasing and Sintering Integrated Furnace: China Patent, 2718480Y. 2005-8-17
[29] 易健宏, 史文芳. 金属粉末注射成形技术及其发展动态. 矿冶工程, 2001, 21(2): 7 Yi J H, Shi W F. The technology of metal powder injection molding and its development. Miner Metall Eng, 2001, 21(2): 7
[30] Chen L J, Li T, Li Y M, et al. Porous titanium implants fabricated by metal injection molding. Trans Nonferrous Met Soc China, 2009, 19(5): 1174 DOI: 10.1016/S1003-6326(08)60424-0
[31] German R M. Powder Injection Molding. Princeton: Powder Industries Federation, 1997
[32] Zauner R. Micro powder injection moulding. Microelectron Eng, 2006, 83: 1442 DOI: 10.1016/j.mee.2006.01.170
[33] Rota A C. New features in material issues for metallic micro components by MIM // World Conference on Powder Metallurgy & Particulate Materials. Orlando, 2002: 49
[34] Zeep B, Norajitra P, Piotter V. Net shaping of tungsten components by micro powder injection moulding. Fusion Eng Des, 2007, 82: 2660 DOI: 10.1016/j.fusengdes.2007.07.013
[35] Piotter V, Zeep B, Norajitra P, et al. Development of a powder metallurgy process for tungsten components. Fusion Eng Des, 2008, 83: 1517 DOI: 10.1016/j.fusengdes.2008.06.022
[36] Nishiyabu K. Micro metal powder injection molding [J/OL]. InTech (2012-03-15)[2020-12-07]. http://www.intechopen.com/books/some-critical-issues-for-injection-molding/micro-metal-powder-injection-molding
[37] Ammosova L, Mnkknen K, Suvanto M. Precise fabrication of microtextured stainless steel surfaces using metal injection moulding. Precis Eng, 2020, 62: 89 DOI: 10.1016/j.precisioneng.2019.11.012
[38] Piotter V, Gietzelt T, Merz L. Micro powder-injection moulding of metals and ceramics. Sadhana, 2003, 28: 299 DOI: 10.1007/BF02717139
[39] 尹海清, 贾成厂, 曲选辉. 粉末微注射成形技术现状. 粉末冶金技术, 2007, 25(5): 382 Yin H Q, Jia C C, Qu X H. Status of micro powder injection molding. Powder Metall Technol, 2007, 25(5): 382
[40] Powder Injection Moulding International Group. WORLDPM2018 Congress: Global MIM markets show healthy growth. Powder Inject Mould Int, 2018, 12(4): 67
[41] 杨廷志. 现代粉末冶金材料与技术进展. 中国金属通报, 2019(12): 10 DOI: 10.3969/j.issn.1672-1667.2019.12.007 Yang T Z. Progress of modern powder metallurgy materials and technology. China Met Bull, 2019(12): 10 DOI: 10.3969/j.issn.1672-1667.2019.12.007
[42] Najima L A. Simulation of mold filling for powder injection molding processes. Adv Powder Metall, 1990, 3: 299
[43] 卓海宇, 高建祥, 曲选辉. 金属粉末注射成形充模过程数学模型研究. 新技术新工艺, 2007(6): 87 DOI: 10.3969/j.issn.1003-5311.2007.06.034 Zhuo H Y, Gao J X, Qu X H. Research on mathematical mold of filling process of metal powder injection molding. New Technol New Process, 2007(6): 87 DOI: 10.3969/j.issn.1003-5311.2007.06.034
[44] Samanta S K, Chattopadhyay H, Pustal B, et al. A numerical study of solidification in powder injection molding process. Int J Heat Mass Transfer, 2008, 51(3-4): 672 DOI: 10.1016/j.ijheatmasstransfer.2007.04.033
[45] 王玉会, 曲选辉, 何新波, 等. 粉末注射成形充模过程特有边界层效应的数值模拟. 机械工程材料, 2008, 32(2): 77 DOI: 10.3969/j.issn.1000-3738.2008.02.023 Wang Y H, Qu X H, He X B, et al. Numerical simulation of unique boundary layer effect during powder injection molding filling flow process. Mater Mech Eng, 2008, 32(2): 77 DOI: 10.3969/j.issn.1000-3738.2008.02.023
[46] 王玉会, 曲选辉, 何新波, 等. 粉末注射成型过程的双流体数学模型. 机械工程材料, 2008, 32(5): 74 DOI: 10.3969/j.issn.1000-3738.2008.05.022 Wang Y H, Qu X H, He X B, et al. Two-fluid model during powder injection molding process. Mater Mech Eng, 2008, 32(5): 74 DOI: 10.3969/j.issn.1000-3738.2008.05.022
[47] 王玉会, 曲选辉, 张勇, 等. PIM充模过程的边界层效应及机理分析. 粉末冶金技术, 2008, 26(4): 254 Wang Y H, Qu X H, Zhang Y, et al. Boundary layer effect of powder injection molding filling flow process and mechanics analysis. Powder Metall Technol, 2008, 26(4): 254
[48] Aizawa T, Iwai T, Kihara J. Granular modeling of steel powder flow and compaction in injection molding // Proc Powder Injection Molding Symp92. New Jersey , 1992: 419
[49] Iwai T, Aizawa T, Kihara J. Numerical modeling for powder-binder compound flow in metal injection molding. Adv Powder Metall Part Mater, 1995, 49(3): 103
[50] 郑洲顺, 曲选辉, 徐勤武, 等. 粉末注射成形两相流动三维数值模拟及粉末与粘结剂的分离. 中国有色金属学报, 2014, 24(1): 122 Zheng Z S, Qu X H, Xu Q W, et al. Three-dimensional numerical simulation of two phase flow for powder injection molding and separation of powder and binder. Chin J Nonferrous Met, 2014, 24(1): 122
[51] 刘煜, 李益民, 肖燕芳, 等. 粉末注射成型中颗粒接触模型的研究. 长沙大学学报, 2010, 24(5): 30 DOI: 10.3969/j.issn.1008-4681.2010.05.012 Liu Y, Li Y M, Xiao Y F, et al. Research on particle contact model in powder injection molding. J Changsha Univ, 2010, 24(5): 30 DOI: 10.3969/j.issn.1008-4681.2010.05.012
[52] 李大鹏. 基于颗粒模型的粉末注射成形充模流动过程研究[学位论文]. 长沙: 中南大学, 2013 Li D P. Investigation on the Mold Filling Process in Powder Injection Molding Based on Granular Model [Dissertation]. Changsha: Central South University, 2013
[53] 郑洲顺, 曲选辉, 韩旭里, 等. 粉末注射成形充模流动过程模壁凝固层增长的计算与模拟. 中国有色金属学报, 2008, 18(3): 511 DOI: 10.3321/j.issn:1004-0609.2008.03.022 Zheng Z S, Qu X H, Han X L, et al. Computation and simulation of solidification on wall of cavity in powder injection molding filling process. Chin J Nonferrous Met, 2008, 18(3): 511 DOI: 10.3321/j.issn:1004-0609.2008.03.022
[54] 吴苑标, 郑振兴. 基于数值模拟的粉末注射成形模具结构优化设计. 机械设计与制造, 2009(12): 236 DOI: 10.3969/j.issn.1001-3997.2009.12.097 Wu Y B, Zheng Z X. The optimal design of mold structure in powder injection molding based on the numerical simulation. Mach Des Manuf, 2009(12): 236 DOI: 10.3969/j.issn.1001-3997.2009.12.097
[55] 刘飞, 李文明. 数值模拟研究浇口方式对粉末注射成形铣刀粉体分布的影响. 粉末冶金材料科学与工程, 2018, 23(3): 292 DOI: 10.3969/j.issn.1673-0224.2018.03.009 Liu F, Li W M. Numerical simulation research on the effect of gate patterns on powder volume fraction variation of MIM milling cutter. Mater Sci Eng Powder Metall, 2018, 23(3): 292 DOI: 10.3969/j.issn.1673-0224.2018.03.009
[56] 郑振兴, 夏伟, 周照耀. 基于数值模拟的粉末注射成形工艺参数优化. 华南理工大学学报(自然科学版), 2009, 37(2): 49 Zheng Z X, Xia W, Zhou Z Y. Optimization of process parameters of powder injection molding based on numerical simulation. J South China Univ Technol Nat Sci, 2009, 37(2): 49
-
期刊类型引用(2)
1. 唐彦渊，羊求民，徐国钻，王红云，钟志强. 微量Y_2O_3对WC-6Co非均匀结构硬质合金微观结构及性能的影响. 粉末冶金技术. 2024(02): 184-191 . 
本站查看
2. 周晓刚，纪飞飞. 激光喷丸作用下TC4双相钛合金HCP结构位错组态及性能研究. 应用激光. 2022(10): 99-105 . 百度学术
其他类型引用(0)
计量
- 文章访问数: 1040
- HTML全文浏览量: 729
- PDF下载量: 126
- 被引次数: 2