退磁工艺对各向异性粘结NdFeCoB退磁效果的影响

退磁工艺对各向异性粘结NdFeCoB退磁效果的影响

张涛, 孙爱芝, 姚修楠

文章导航 > 粉末冶金技术 > 2008 > 26(1): 37-40

张涛, 孙爱芝, 姚修楠. 退磁工艺对各向异性粘结NdFeCoB退磁效果的影响[J]. 粉末冶金技术, 2008, 26(1): 37-40.

引用本文:

张涛, 孙爱芝, 姚修楠. 退磁工艺对各向异性粘结NdFeCoB退磁效果的影响[J]. 粉末冶金技术, 2008, 26(1): 37-40.

Zhang Tao, Sun Aizhi, Yao Xiunan. Influence of demagnetization process on the effect of demagnetization of anisotropic bonded NdFeCoB magnets[J]. Powder Metallurgy Technology, 2008, 26(1): 37-40.

Citation:

Zhang Tao, Sun Aizhi, Yao Xiunan. Influence of demagnetization process on the effect of demagnetization of anisotropic bonded NdFeCoB magnets[J]. Powder Metallurgy Technology, 2008, 26(1): 37-40.

张涛, 孙爱芝, 姚修楠. 退磁工艺对各向异性粘结NdFeCoB退磁效果的影响[J]. 粉末冶金技术, 2008, 26(1): 37-40.

引用本文:

张涛, 孙爱芝, 姚修楠. 退磁工艺对各向异性粘结NdFeCoB退磁效果的影响[J]. 粉末冶金技术, 2008, 26(1): 37-40.

Zhang Tao, Sun Aizhi, Yao Xiunan. Influence of demagnetization process on the effect of demagnetization of anisotropic bonded NdFeCoB magnets[J]. Powder Metallurgy Technology, 2008, 26(1): 37-40.

Citation:

Zhang Tao, Sun Aizhi, Yao Xiunan. Influence of demagnetization process on the effect of demagnetization of anisotropic bonded NdFeCoB magnets[J]. Powder Metallurgy Technology, 2008, 26(1): 37-40.

退磁工艺对各向异性粘结NdFeCoB退磁效果的影响

北京科技大学材料科学与工程学院,北京,100083
北京科技大学

基金项目: 国家高技术研究发展计划(863计划)(2001AA324016)

中图分类号: TF12
计量
- 文章访问数: 141
- HTML全文浏览量: 16
- PDF下载量: 6
- 被引次数: 0
出版历程

Influence of demagnetization process on the effect of demagnetization of anisotropic bonded NdFeCoB magnets

摘要: 分别研究了以聚四氟乙烯(PTFE)和环氧树脂(Epoxy resin)为粘结剂的各向异性粘结NdFeCoB取向成形后经不同次数的交流脉冲退磁后的表面剩磁Br,以及上述磁体再经过热退磁后的表面剩磁Br.发现两种磁体即使经过多次交流退磁也并不能将其完全退磁,因此必须对其进行热退磁.研究了热退磁对两种磁体的表面剩磁的影响,同时重点研究了热退磁温度和保温时间对以PTFE为粘结剂的各向异性粘结NdFeCoB的表面剩磁和矫顽力的影响.结果表明,在370℃保温10min,既可以保证退磁效果,又不至于引起磁体更多的热磁损失.
- 热退磁 /
- 交流脉冲退磁 /
- 表面剩磁 /
- 矫顽力 /
- 各向异性粘结NdFeCoB

参考文献(0)

资源附件(0)

WeChat

点击查看大图

计量

文章访问数: 141
HTML全文浏览量: 16
PDF下载量: 6
被引次数: 0

/

下载: 全尺寸图片幻灯片

分享

用微信扫码二维码

分享至好友和朋友圈

返回

网站版权《粉末冶金技术》编辑部京ICP备13030111号

本系统由北京仁和汇智信息技术有限公司开发