高级检索

Fe-V-C系奥氏体中VC析出动力学计算

李小明,  钟海林,  王学兵,  吴立志,  况春江

downloadPDF
文章导航 > 粉末冶金技术  > 2012 >  30(3): 167-170,199
李小明, 钟海林, 王学兵, 吴立志, 况春江. Fe-V-C系奥氏体中VC析出动力学计算[J]. 粉末冶金技术, 2012, 30(3): 167-170,199. doi: 10.3969/j.issn.1001-3784.2012.03.002
引用本文: 李小明, 钟海林, 王学兵, 吴立志, 况春江. Fe-V-C系奥氏体中VC析出动力学计算[J]. 粉末冶金技术, 2012, 30(3): 167-170,199. doi: 10.3969/j.issn.1001-3784.2012.03.002
shu
Li Xiaoming, Zhong Hailin, Wang Xuebing, Wu Lizhi, Kuang Chunjiang. Thermodynamic computation of vanadium carbide precipitation in austenite of Fe-V-C[J]. Powder Metallurgy Technology, 2012, 30(3): 167-170,199. doi: 10.3969/j.issn.1001-3784.2012.03.002
Citation: Li Xiaoming, Zhong Hailin, Wang Xuebing, Wu Lizhi, Kuang Chunjiang. Thermodynamic computation of vanadium carbide precipitation in austenite of Fe-V-C[J]. Powder Metallurgy Technology, 2012, 30(3): 167-170,199. doi: 10.3969/j.issn.1001-3784.2012.03.002
shu

Fe-V-C系奥氏体中VC析出动力学计算

doi: 10.3969/j.issn.1001-3784.2012.03.002

  • 安泰科技股份有限公司,北京,100081

  • 河冶科技股份有限公司,石家庄,050031

  • 安泰科技股份有限公司

  • 河冶科技股份有限公司

基金项目: 国家“十一五"科技支撑计划资助项目(2007BAE51B05)%国家高科技发展计划资助项目(202AA03A509)
详细信息

  • 中图分类号: TG142.1

Thermodynamic computation of vanadium carbide precipitation in austenite of Fe-V-C

    摘要
  • 摘要: 以材料热力学及动力学为基础,以Fe-V-C三元系为研究对象,研究了l 130℃恒温条件下碳化物VC在奥氏体中从形核、长大到熟化的连续过程.各元素在碳化物-基体界面处达到局部平衡,根据基体成分以及每个碳化物颗粒的大小分别计算出生长速度.当碳化物生长进入熟化阶段,在Gibbs-Thomson效应作用下,小颗粒开始回溶,大颗粒继续长大,表现为总颗粒数量减少,平均半径变大;当保温时间达到l x 104s时,析出量接近平衡状态,VC体积分数为1.51％、平均半径为0.72μm.
    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  172
  • HTML全文浏览量:  38
  • PDF下载量:  12
  • 被引次数: 0
出版历程

目录

    /

    返回文章
    返回

    网站版权 《粉末冶金技术》编辑部京ICP备13030111号

    本系统由 北京仁和汇智信息技术有限公司开发    百度统计