包覆分解法制备多层陶瓷电容器用超细Ni粉性能表征

李军义,  王东新,  孙本双,  何季麟,  郭顺,  杨国启

downloadPDF
文章导航 > 粉末冶金技术  > 2013 >  31(5): 360-364
李军义, 王东新, 孙本双, 何季麟, 郭顺, 杨国启. 包覆分解法制备多层陶瓷电容器用超细Ni粉性能表征[J]. 粉末冶金技术, 2013, 31(5): 360-364. doi: 10.3969/j.issn.1001-3784.2013.05.008
引用本文: 李军义, 王东新, 孙本双, 何季麟, 郭顺, 杨国启. 包覆分解法制备多层陶瓷电容器用超细Ni粉性能表征[J]. 粉末冶金技术, 2013, 31(5): 360-364. doi: 10.3969/j.issn.1001-3784.2013.05.008
shu
Li Junyi, Wang Dongxin, Sun Benshuang, He Jilin, Guo Shun, Yang Guoqi. Characterization of ultrafine nickel powder for MLCC fabricated by coated precursor thermal decomposition method[J]. Powder Metallurgy Technology, 2013, 31(5): 360-364. doi: 10.3969/j.issn.1001-3784.2013.05.008
Citation: Li Junyi, Wang Dongxin, Sun Benshuang, He Jilin, Guo Shun, Yang Guoqi. Characterization of ultrafine nickel powder for MLCC fabricated by coated precursor thermal decomposition method[J]. Powder Metallurgy Technology, 2013, 31(5): 360-364. doi: 10.3969/j.issn.1001-3784.2013.05.008
shu

包覆分解法制备多层陶瓷电容器用超细Ni粉性能表征

doi: 10.3969/j.issn.1001-3784.2013.05.008

  • 国家钽铌特种金属材料工程技术研究中心,宁夏石嘴山753000;宁夏东方钽业股份有限公司,宁夏石嘴山753000

  • 国家钽铌特种金属材料工程技术研究中心,宁夏石嘴山,753000

  • 国家钽铌特种金属材料工程技术研究中心

基金项目: 宁夏回族自治区自然科学基金资助项目(NZ13257)

Characterization of ultrafine nickel powder for MLCC fabricated by coated precursor thermal decomposition method

    摘要
  • 摘要: 采用包覆草酸镍前驱体热分解法制备出了各项性能满足MLCC用超细Ni粉.讨论了正压条件下草酸盐热分解原理,分析了工艺参数对Ni粉粒度的影响,采用XRD、SEM、TEM、BET、化学分析等分析手段对Ni粉进行了表征.结果表明:反应溶液的pH值为5时制备的草酸镍分散性好、有利于包覆,Ni粉颗粒大小可以通过调节草酸镍制备过程中的反应温度和Ni离子浓度调节,采用包覆草酸盐热分解法可以制备出结晶度好、纯度高、呈类球形、粒度均匀可控、分散性好的Ni粉.
    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  174
  • HTML全文浏览量:  48
  • PDF下载量:  6
  • 被引次数: 0
出版历程

目录

    /

    返回文章
    返回

    网站版权 《粉末冶金技术》编辑部京ICP备13030111号

    本系统由 北京仁和汇智信息技术有限公司开发    百度统计